Ecological ceramic water filter brick and manufacturing method thereof

A technology of ecological ceramics and manufacturing methods, applied in the direction of ceramic products, ceramic material production, clay products, etc., can solve the problems of strong weathering resistance, weakened or disappeared functions, weathering, etc., and achieve the effect of protecting the environment and reducing resource consumption

Inactive Publication Date: 2018-05-08
福建省绿城生态科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are many styles of traditional permeable bricks and permeable bricks, but they all have a fatal weakness, which cannot meet the requirements of high strength, high water permeability and strong weather resistance
Moreover, such materials are laid on the urban ground, and it will not take long for them to break, weather, and weaken or disappear.
Cause waste of repairing and resurfacing of urban ground and secondary pollution of the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] S1 Material preparation: The ceramic waste is pulverized by a large pulverizer, ground into ceramic particles, and separated into ceramic particles of three particle sizes through a screening machine and stacked separately for use. The particle size of the large ceramic particles is 4-12 mesh, and the medium ceramic particles are The particle size of the particles is 12-16 mesh, and the particle size of the small ceramic particles is 16-30 mesh.

[0026] The surface layer blank is configured according to the following parts by weight: 90 parts of ceramic particles, 7 parts of high-temperature binder, and 3 parts of low-temperature solvent. Among them, the ceramic particles are composed of 50% large ceramic particles, 40% medium ceramic particles and 10% small ceramic particles; the high-temperature binder is composed of 5% dolomite, 25% feldspar, 5% quartz, 55% bentonite and 10% Composition of kaolin. Potassium feldspar is used as low temperature solvent.

[0027] The...

Embodiment 2

[0034] S1 Material preparation: The ceramic waste is pulverized by a large pulverizer, ground into ceramic particles, and separated into ceramic particles of three particle sizes through a screening machine and stacked separately for use. The particle size of the large ceramic particles is 4-12 mesh, and the medium ceramic particles are The particle size of the particles is 12-16 mesh, and the particle size of the small ceramic particles is 16-30 mesh.

[0035] The surface layer blank is configured according to the following parts by weight: 84 parts of ceramic particles, 13 parts of high-temperature binder, and 3 parts of low-temperature solvent. Among them, the ceramic particles are composed of 55% large ceramic particles, 40% medium ceramic particles and 5% small ceramic particles; the high-temperature binder is composed of 10% dolomite, 20% feldspar, 10% quartz, 50% bentonite and 10% Composition of kaolin. Albite is used as a low-temperature solvent.

[0036] The base ma...

Embodiment 3

[0043] S1 Material preparation: The ceramic waste is pulverized by a large pulverizer, ground into ceramic particles, and separated into ceramic particles of three particle sizes through a screening machine and stacked separately for use. The particle size of the large ceramic particles is 4-12 mesh, and the medium ceramic particles are The particle size of the particles is 12-16 mesh, and the particle size of the small ceramic particles is 16-30 mesh.

[0044]The surface layer blank is configured according to the following parts by weight: 92 parts of ceramic particles, 5 parts of high-temperature binder, and 3 parts of low-temperature solvent. Among them, the ceramic particles are composed of 50% large ceramic particles, 40% medium ceramic particles and 10% small ceramic particles; the high-temperature binder is composed of 7% dolomite, 30% feldspar, 9% quartz, 45% bentonite and 9% Composition of kaolin. Albite is used as a low-temperature solvent.

[0045] The base materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a building material and particularly relates to an ecological ceramic water filter brick. The water filter brick comprises a surface layer and a bottom layer. The surface layer blank comprises ceramic particles, a high temperature binder and a low temperature solvent. The bottom layer blank comprises ceramic particles and a high temperature binder. The whole blank mainly comprises high-strength waste ceramic particles. Through mixing of the surface layer blank and bottom layer blank ceramic particles in different levels and at different ratios and combination of the ceramic particles, an inorganic high-temperature binder and an inorganic low-temperature flux, the bricks form natural gaps. Through sintering in a high-temperature kiln, the waste brick particles are closely bonded through clever processes to form an integral body as the high strength, high water permeability and high abrasion resistance ceramic water filter brick. The invention also discloses a method for manufacturing the ecological ceramic water filter brick.

Description

technical field [0001] The invention relates to building materials, in particular to an ecological ceramic water filter brick and a manufacturing method thereof. Background technique [0002] With the development of the economy and the acceleration of urban construction, the surface of modern cities is gradually hardened and covered by buildings and water-blocking materials such as concrete, stone, and imitation stone floor tiles, forming an ecological "artificial desert". When the rainfall is concentrated in a short period of time, the rainwater can only be discharged into the river through the urban drainage facilities. During the heavy rain, it is easy to cause serious water accumulation in the urban area, which not only increases the burden on the urban drainage facilities, but also makes the precious water resources flow away in vain. [0003] While convenient transportation facilities and paved roads bring great convenience to people's travel, the hardening of these ro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B33/132C04B33/13E01C5/04E01C11/22
CPCC04B33/13C04B33/1324C04B38/0041C04B2235/321C04B2235/3418C04B2235/3454C04B2235/3463C04B2235/3472C04B2235/349C04B2235/656C04B2235/96E01C5/04E01C11/225Y02P40/60
Inventor 蒋玉勇
Owner 福建省绿城生态科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com