Self-adhesive polymer modified asphalt waterproof coiled material and preparation method therefor

A technology of modified asphalt and waterproof coiled material, applied in the field of chemical materials for construction, can solve the problems of difficulty in opening the isolation film, affecting the construction efficiency, melting and softening of the coiled material, etc., and achieves excellent adhesion and good full adhesion effect. , the effect of excellent weather resistance

Inactive Publication Date: 2018-05-08
GUILIN HEXIN WATERPROOF DECORATION MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But as far as the current self-adhesive polymer modified bitumen waterproofing membrane is concerned, its heat resistance is not high, and many problems have appeared in summer construction. Soft, with a tendency to flow; and the isolation film is difficult to uncover, which affects construction efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) The penetration of petroleum asphalt is 80, the softening point is 48°C, and the content of asphaltene is 15%. The softening point of natural lake asphalt is 95°C, it contains 33% porous minerals, and the content of asphaltene in natural lake asphalt is 38%. Compound petroleum asphalt and natural lake asphalt, and natural lake asphalt accounts for 50% of the total asphalt;

[0021] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 50 parts of the above compounded asphalt, 8 parts of SBS synthetic rubber, 15 parts of waste rubber powder, and 1.5 parts of polypropylene resin.

[0022] 3) First raise the temperature of the above compound asphalt to 200°C, add waste engine oil and stir to cool down to 180°C, then add SBS synthetic rubber, heat up to 240°C, add waste rubber powder, keep stirring for 2 hours, then add polypropylene resin and continue stirring After 0.5h, the modified asphalt compound is obtained.

[0023]...

Embodiment 2

[0025] 1) The softening point of natural lake asphalt is 110°C, it contains 38% porous minerals, and the content of asphaltene in natural lake asphalt is 43%.

[0026] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 62 parts of natural lake asphalt, 10 parts of SBS synthetic rubber, 25 parts of waste rubber powder, and 2.5 parts of polypropylene resin.

[0027] 3) First raise the temperature of natural lake asphalt to 220°C, add waste engine oil and stir evenly to cool down to 190°C, then add SBS synthetic rubber, heat up to 250°C, add waste rubber powder, keep stirring for 3 hours, then add polypropylene resin and continue stirring for 1 hour , that is, the modified asphalt compound.

[0028] 4) Glass fiber felt or polyester felt is used as the reinforcement body, and the modified asphalt layer is coated on the top of the reinforcement body. mm, mineral particle layer 2.0mm, thermoplastic polyolefin layer 1.5mm, modified as...

Embodiment 3

[0030] 1) The penetration of petroleum asphalt is 70, the softening point is 50°C, and the content of asphaltene is 16%. The softening point of natural lake asphalt is 105°C, it contains 35% porous minerals, and the content of asphaltene in natural lake asphalt is 40%. Compound petroleum asphalt and natural lake asphalt, and natural lake asphalt accounts for 80% of the total asphalt;

[0031] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 58 parts of the above-mentioned compound asphalt, 9 parts of SBS synthetic rubber, 20 parts of waste rubber powder, and 2 parts of polypropylene resin.

[0032] 3) First raise the temperature of the above compound asphalt to 210°C, add waste engine oil and stir to cool down to 185°C, then add SBS synthetic rubber, heat up to 245°C, add waste rubber powder, keep stirring for 2.5 hours, then add polypropylene resin to continue Stir for 0.8h to obtain the modified asphalt compound.

[0033] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a self-adhesive polymer modified asphalt waterproof coiled material. According to the self-adhesive polymer modified asphalt waterproof coiled material, glass fiber felt or polyester felt serves as a reinforcer, the upper face of the reinforcer is coated with a modification asphalt layer, the upper surface of the modification asphalt layer is coated with a mineral particlelayer, and the lower face of the reinforcer is coated with a thermoplastic polyolefin layer; a modified asphalt mastic layer is arranged between an upper cover layer and an middle body layer; and themodified asphalt mastic layer is prepared from the following raw materials in parts by weight: 50-62 parts of asphalt, 8-10 parts of SBS synthetic rubber, 15-25 parts of waste rubber powder and 1.5-2.5 parts of polypropylene resin. The waterproof coiled material disclosed by invention is long in service life and good in waterproof performance and aging resistance.

Description

technical field [0001] The invention belongs to the field of chemical materials for construction, and in particular relates to a self-adhesive polymer modified asphalt waterproof coiled material and a preparation method thereof. Background technique [0002] Self-adhesive waterproof membrane is a new type of waterproof material with great development prospects. The self-adhesive roll material has the characteristics of good water impermeability, strong adaptability to low temperature, good deformation resistance and self-healing property, good waterproof effect, and no need for hot melt, cold construction, direct laying and sticking, which not only improves the construction efficiency, It also eliminates fire hazards and has been highly praised by construction, design and construction units. [0003] But as far as the current self-adhesive polymer modified bitumen waterproofing membrane is concerned, its heat resistance is not high, and many problems have appeared in summer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B11/12B32B11/10B32B17/02B32B27/02B32B27/36B32B33/00B32B37/06B32B37/10
CPCB32B11/12B32B11/10B32B33/00B32B37/06B32B37/10B32B2255/02B32B2255/20B32B2255/26B32B2262/0276B32B2262/101B32B2307/3065B32B2307/712B32B2307/7265B32B2307/762
Inventor 黄志强钟圣福王继发
Owner GUILIN HEXIN WATERPROOF DECORATION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap