Alumina hydrate composition containing ZSM-48 type molecular sieve, catalyst, preparation method and hydroisomerization method

A technology of ZSM-48 and hydrated alumina, applied in the direction of molecular sieve catalysts, chemical instruments and methods, physical/chemical process catalysts, etc., can solve problems such as transfer difficulties, secondary dust pollution, and increase in the amount of unqualified products, and achieve simplification Process flow, the effect of reducing operating energy consumption

Active Publication Date: 2020-08-18
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] (1) Pseudo-boehmite that has not been completely dried has strong viscosity, is difficult to transfer, and easily causes secondary dust pollution;
[0016] (2) Drying starts from the surface. The drying of the wet solid product separated from the mixture obtained from the gelling reaction is incomplete drying, so there is a sandwich biscuit phenomenon, that is, the surface of part of the pseudo-boehmite is dried (that is, the dried surface is substantially free of free water), while the interior is still wet (that is, for the non-dried interior, the content of free water is basically maintained at the level before drying), since the surface is dried, Therefore, hard particles are formed. When peptizing agent and / or binder are added to this incompletely dried pseudo-boehmite and kneaded, the hard particles formed during the drying process are in the process of extrusion. It is easy to cause blockage and affect production efficiency;
[0017] (3) It is difficult to stably control the dry base of pseudo-boehmite. The instability of the dry base will cause great interference to the molding process, making the molding process very unstable, resulting in an increase in the amount of unqualified products and low production efficiency;
[0018] (4) CN103769118A adopts a conventional molding process when molding, yet because the dry basis (35%-50%) of the pseudo-boehmite it adopts is far lower than the conventional dry basis content (about 70%), that is The water content is high, and there is basically no extrusion pressure during the extrusion molding process. Therefore, the carrier obtained after the extrudate is dried and roasted has basically no mechanical strength. As long as a little external force is applied, it will be pulverized and has no possibility of industrial application. sex, which is the biggest problem facing the technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alumina hydrate composition containing ZSM-48 type molecular sieve, catalyst, preparation method and hydroisomerization method
  • Alumina hydrate composition containing ZSM-48 type molecular sieve, catalyst, preparation method and hydroisomerization method
  • Alumina hydrate composition containing ZSM-48 type molecular sieve, catalyst, preparation method and hydroisomerization method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0106] According to the preparation method of the hydrated alumina composition of the present invention, the raw material mixture contains hydrated alumina wet gel, ZSM-48 molecular sieve and a compound having at least two proton acceptor sites. The compound having at least two proton acceptor sites and its type, as well as the ZSM-48 molecular sieve and its type have been described in detail above, and will not be repeated here.

[0107] The hydrated alumina wet gel can be synthesized by conventional methods, such as one or more of precipitation method (including acid method and alkali method), hydrolysis method, seed separation method and rapid dehydration method. Generally, it is obtained by optionally aging the hydrated alumina gel solution, followed by washing and solid-liquid separation.

[0108] The precipitation method includes acid method and alkali method. The acid method is to carry out precipitation reaction of aluminum salt with basic compound. The alkali method...

Embodiment 1

[0238] The alumina hydrate wet gel used in this example is a quasi-alumina hydrogel solution prepared by the acid method (sodium metaaluminate-aluminum sulfate method, obtained from Sinopec Changling Branch) after washing and filtering. The wet filter cake of boehmite (the wet filter cake is coded as SLB-1), after measurement, the i value of the wet filter cake is 80.2%.

[0239] (1) Add 5.48kg H-ZSM-48 molecular sieve (product of Sinopec Catalyst Branch Jianchang Branch Company, the ratio of silicon to aluminum is 50, dry basis is 0.98) to 50kg wet filter cake SLB-1, then add 10kg water to mix Beat the pulp for 5 minutes, then filter the slurry with a belt filter to obtain 15.2kg of wet filter cake SLBZ-1. The i value of the wet filter cake SLBZ-1 was determined to be 80.2%. After the wet filter cake SLBZ-1 was roasted at 600°C for 3 hours, it was determined that the weight ratio of alumina to ZSM-48 molecular sieve was 58:42.

[0240] (2) Put 200g of wet filter cake numbere...

Embodiment 2

[0251] (1) Mix 5 kg of wet filter cake numbered SLBZ-1 with 500 g of deionized water for beating for 1 minute, then send the resulting slurry into a plate and frame filter press, adjust the pressure of the plate and frame to 0.7 MPa and maintain After 15 minutes, a wet filter cake (coded as LBZ-1) was obtained. It has been determined that the i value of the wet filter cake numbered LBZ-1 is 63%.

[0252] (2) 300g of wet filter cake numbered LBZ-1 was placed in a beaker, and 4.3g of hydroxyethyl methylcellulose (purchased from Shanghai Huiguang Fine Chemical Co., Ltd., the same below) and 1.7g of scallop powder ( The content of galactomannan is 85% by weight (purchased from Beijing Chemical Reagent Company). After stirring for 10 minutes with a mechanical stirrer, the hydrated alumina composition of the present invention is obtained, and its properties are listed in Table 1.

[0253] (3) Extrude the hydrated alumina composition prepared in step (2) on an F-26 twin-screw extrud...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrated alumina composition containing a ZSM-48 type molecular sieve, and a preparation method thereof, and a molding body, a preparation method and applications thereof. The hydrated alumina composition contains hydrated alumina, a ZSM-48 type molecular sieve and a compound having at least two proton acceptor sites, wherein the [phi] value is less than 5. The present invention further discloses a hydroisomerization catalyst using a molding body formed from the hydrated alumina composition as a carrier, and a preparation method thereof, and a hydroisomerization method. According to the present invention, the high-strength molding body is prepared by using the hydrated alumina wet gel as the starting raw material, such that the hydrated alumina wet gel drying stepis eliminated, the total process is simplified, the total operation energy consumption is reduced, the dust pollution caused by the application of the pseudoboehmite dry glue powder as the raw material is avoided, and the working environment is greatly improved; and the obtained catalyst has high catalytic activity in the hydroisomerization reaction.

Description

technical field [0001] The present invention relates to the technical field of alumina forming, specifically, the present invention relates to a hydrated alumina composition containing ZSM-48 molecular sieve and its preparation method, and the present invention also relates to the hydrated alumina formed from the hydrated alumina composition. Aluminum molded body and alumina molded body, the present invention further relates to a hydroisomerization catalyst using the molded body formed from the hydrated alumina composition as a carrier, a preparation method thereof, and a hydroisomerization process using the catalyst method. Background technique [0002] ZSM-48 molecular sieve is a kind of high silica zeolite, which belongs to the orthorhombic crystal structure. It has non-through interlaced linear channels with 10-membered openings. The channels are connected by 5-membered rings, and the diameter of the pores is about 0.6nm. ZSM-48 molecular sieve is widely used in the iso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J32/00B01J29/70B01J29/72B01J35/10C07C9/16C07C5/27B01J20/18B01J20/30
CPCB01J20/08B01J20/186B01J29/703B01J29/7261B01J35/1019B01J35/1042B01J2229/186B01J2229/20B01J2229/40C07C5/2708C07C9/16
Inventor 毕云飞夏国富杨清河李明丰辛靖李洪宝郭庆洲
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com