Wear-resistant corrosion-resistant metallic furniture coating and preparation method thereof

A furniture coating and corrosion-resistant technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of poor wear resistance and corrosion resistance, and achieve the performance of wear resistance and corrosion resistance Excellent, not easy to fall off, the effect of meeting the market demand

Inactive Publication Date: 2018-04-20
GUANGDONG DEXIN TECH INCUBATOR CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of metal furniture, metal furniture coatings are more and more valued by the market, and the existing metal furniture coatings gradually show the defects of poor wear resistance and poor corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A wear-resistant and corrosion-resistant coating for metal furniture, consisting of the following raw materials in parts by weight: 110 parts of styrene-acrylic emulsion, 24 parts of acrylonitrile-butadiene-styrene resin, 18 parts of polyvinylpyrrolidone, epoxidized polybutylene 30 parts of diene resin, 2 parts of ricinoleic acid, 13 parts of sodium carboxymethylcellulose, 4 parts of propylene glycol phenyl ether, 2 parts of polyoxypropylene glyceryl ether, 0.5 parts of ammonium octamolybdate, 1 part of ethylene bis stearamide 1 part, 1 part of hydroquinone, 2 parts of propylene carbonate, 25 parts of diatomaceous earth.

[0023] The invention also discloses a preparation method of the wear-resistant and corrosion-resistant metal furniture coating, the steps are as follows:

[0024] 1) Weigh diatomite, put it into a calciner, and calcinate at 580° C. for 1 hour. After cooling in the furnace, discharge, pulverize, and sieve to obtain calcined diatomite, wherein the sievi...

Embodiment 2

[0032] A wear-resistant and corrosion-resistant coating for metal furniture, consisting of the following raw materials in parts by weight: 113 parts of styrene-acrylic emulsion, 25 parts of acrylonitrile-butadiene-styrene resin, 19 parts of polyvinylpyrrolidone, epoxidized polybutylene 34 parts of diene resin, 2.8 parts of ricinoleic acid, 16 parts of sodium carboxymethyl cellulose, 5 parts of propylene glycol phenyl ether, 3 parts of polyoxypropylene glyceryl ether, 0.9 parts of ammonium octamolybdate, 1.8 parts of ethylene bis stearamide parts, 1.3 parts of hydroquinone, 3 parts of propylene carbonate, and 29 parts of diatomaceous earth.

[0033] The invention also discloses a preparation method of the wear-resistant and corrosion-resistant metal furniture coating, the steps are as follows:

[0034] 1) Weigh diatomite, put it into a calciner, and calcinate at 590° C. for 1 hour. After cooling in the furnace, discharge, pulverize, and sieve to obtain calcined diatomite, where...

Embodiment 3

[0042] A wear-resistant and corrosion-resistant coating for metal furniture, consisting of the following raw materials in parts by weight: 115 parts of styrene-acrylic emulsion, 27 parts of acrylonitrile-butadiene-styrene resin, 20 parts of polyvinylpyrrolidone, epoxidized polybutylene 32 parts of diene resin, 2.4 parts of ricinoleic acid, 15 parts of sodium carboxymethylcellulose, 6 parts of propylene glycol phenyl ether, 3.5 parts of polyoxypropylene glyceryl ether, 0.8 parts of ammonium octamolybdate, 1.5 parts of ethylene bis stearamide parts, 1.7 parts of hydroquinone, 4 parts of propylene carbonate, and 28 parts of diatomaceous earth.

[0043] The invention also discloses a preparation method of the wear-resistant and corrosion-resistant metal furniture coating, the steps are as follows:

[0044] 1) Weigh diatomite, put it into a calciner, and calcinate at 590° C. for 1.5 hours. After cooling in the furnace, discharge, pulverize, and sieve to obtain calcined diatomite, w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant corrosion-resistant metallic furniture coating which is composed of the following raw materials in parts by weight: 110-120 parts of styrene-acrylic emulsion,24-29 parts of acrylonitrile-butadiene-styrene resin, 18-22 parts of polyvinylpyrrolidone, 30-35 parts of polybutadiene epoxy resin, 2-3 parts of ricinoleic acid, 13-17 parts of sodium carboxymethylcellulose, 4-8 parts of phenoxy-1-propanol, 2-5 parts of polyoxypropylene glycerol ether, 0.5-1.0 part of ammonium octamolybdate, 1-2 parts of ethylene bis-stearamide, 1-2 parts of hydroquinone, 2-5 parts of propylene carbonate and 25-30 parts of diatomite. The invention further discloses a preparation method of the wear-resistant corrosion-resistant metallic furniture coating. The metallic furniture coating disclosed by the invention is excellent in wear resistance and corrosion resistance and long in service life and has wide market prospects.

Description

technical field [0001] The invention relates to the technical field of furniture coatings, in particular to a wear-resistant and corrosion-resistant metal furniture coating and a preparation method thereof. Background technique [0002] With the development and extension of the concept of modern furniture, the current metal furniture has gradually become a popular choice among many furniture choices due to its unique expressive force. The metal materials used in metal furniture are easy to realize automatic processing and a high degree of mechanization. Improve labor efficiency and reduce product cost, which is unmatched by wooden furniture. Thin-walled pipes and sheets used in metal furniture can be bent arbitrarily or formed at one time. Create different shapes such as square, round, pointed, flat, etc. Metal furniture with different shapes can be obtained through stamping, forging, casting, molding, welding and other processing of metal materials. It not only has the fu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D155/02C09D139/06C09D163/00C09D101/28C09D5/08C09D7/61C09D7/63
CPCC09D125/14C08L2205/035C09D5/08C08L55/02C08L39/06C08L63/00C08L1/286C08K13/06C08K3/24C08K5/20C08K5/109C08K3/34
Inventor 冯奋吴龙梅吴道祥
Owner GUANGDONG DEXIN TECH INCUBATOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap