High-performance concrete

A high-performance concrete and modified material technology, applied in the field of high-performance concrete, can solve problems such as poor corrosion resistance and easy cracking

Inactive Publication Date: 2018-03-23
广西丰达三维科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to the good toughness index, the high toughness concrete has only a limited improvement in penetration resistance and tensile strength, and is prone to cracks and poor corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance concrete
  • High-performance concrete

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The preparation method of described high-performance concrete comprises the following steps:

[0018] S1, ingredients: firstly mix cement, sand, stone, water, paper rebar, rice straw, hemp knife, and polypropylene fiber according to the weight ratio to obtain a mixed homogeneous material;

[0019] S2. Modified material: polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-( Mix hydroxymethyl)-1,3-propanediol ether, SJ-101 resin, polyphenol novolac, and zinc trimerized acrylate according to the weight ratio, stir for 4-6min, then raise the temperature to 85-92°C rapidly, and the stirring modification time For 15-30min, the modified material is obtained;

[0020] S3. Stirring: add the mixed homogeneous material prepared in step S1 into water by weight, stir for 8-10 minutes, then add the modified material prepared in step S2, and stir for another 10-15 minutes to prepare high-performance concrete.

Embodiment 1

[0023] A high-performance concrete, in parts by weight, comprising the following raw materials: 122 parts of cement, 25 parts of sand, 20 parts of stone, 250 parts of water, 16 parts of paper tendon, 18 parts of rice straw, 12 parts of hemp knife, 8 parts of polypropylene fiber Parts, 4 parts of polyphenol novolac, 12 parts of polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-(hydroxymethyl)-1, 6 parts of 3-propylene glycol ether, 8 parts of SJ-101 resin, 3 parts of zinc trimerized acrylate;

[0024] The preparation method of described high-performance concrete comprises the following steps:

[0025] S1, ingredients: firstly mix cement, sand, stone, water, paper rebar, rice straw, hemp knife, and polypropylene fiber according to the weight ratio to obtain a mixed homogeneous material;

[0026] S2. Modified material: Polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-(hydroxymethyl base)-1,3-propanediol ether, SJ-101 resin, polyphenol novola...

Embodiment 2

[0029] A high-performance concrete, in parts by weight, comprising the following raw materials: 140 parts of cement, 28 parts of sand, 25 parts of stone, 350 parts of water, 18 parts of paper tendon, 22 parts of rice straw, 15 parts of hemp knife, 12 parts of polypropylene fiber Parts, 6 parts of polyphenol novolac, 18 parts of polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-(hydroxymethyl)-1, 8 parts of 3-propylene glycol ether, 10 parts of SJ-101 resin, 5 parts of zinc trimerized acrylate;

[0030] The preparation method of described high-performance concrete comprises the following steps:

[0031] S1, ingredients: firstly mix cement, sand, stone, water, paper rebar, rice straw, hemp knife, and polypropylene fiber according to the weight ratio to obtain a mixed homogeneous material;

[0032] S2. Modified material: Polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-(hydroxymethyl base)-1,3-propanediol ether, SJ-101 resin, polyphenol alde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance concrete, which belongs to the technical field of concrete preparation. The high-performance concrete includes the following raw materials: cement, sand, stone, water, paper tendon, rice straw, hemp knife, polypropylene fiber, polystyrene Phenolic, polysulfone resin, poly[(2-oxiranyl)-1,2-cyclohexanediol] 2-ethyl-2-(hydroxymethyl)-1,3-propylene glycol ether, SJ-101 Resin, zinc trimer acrylate. The high-performance concrete prepared by the invention has high tensile strength and compressive strength, and excellent toughness and corrosion resistance.

Description

【Technical field】 [0001] The invention belongs to the technical field of concrete preparation, and in particular relates to a high-performance concrete. 【Background technique】 [0002] Concrete is a general term for engineering composite materials in which aggregates are cemented into a whole by cementitious materials. The term concrete usually refers to the cement concrete obtained by using cement as the cementitious material, gravel and fine sand as the aggregate, mixed with water in a certain proportion, and admixtures and admixtures can also be added. Called ordinary concrete, it is widely used in civil engineering. [0003] Most of the existing concrete is made of simple cement, gravel, and fine sand mixed with water. The surface of the concrete produced in this way is prone to cracks, low in tensile strength, poor in corrosion resistance, and poor in toughness. For example, the Chinese patent application document "High Toughness Concrete Formula" (publication number:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2201/50C04B14/06C04B14/00C04B18/241C04B18/248C04B16/02C04B16/0633C04B24/302C04B24/22C04B24/32C04B24/04C04B24/2641
Inventor 陈汝森
Owner 广西丰达三维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products