A process method for combined firing of painted pottery and black pottery

A process method and technology of black pottery, applied in the field of combined firing of painted pottery and black pottery, to achieve good appearance and artistic effect, very market competitiveness and economic benefits, compatible and uniform effect

Active Publication Date: 2020-09-29
界首市十三窑工艺美术有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the production of painted pottery and black pottery is mostly carried out separately, and the combined firing process of the two is rarely seen on the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for combined firing of painted pottery and black pottery, comprising the steps of:

[0031] (1) Green body preparation:

[0032] a. Put the yellow glue mud in the sun for exposure treatment, then crush the yellow glue mud after the sun exposure treatment, put it into clear water, stir and wash it continuously, and finally filter it to obtain the yellow glue mud for later use;

[0033] b. Add the mixed soil of 15% of its total mass to the yellow glue slurry obtained after the operation a treatment, put it into the mixer and mix it uniformly to get the green clay for subsequent use; the mixed soil is made up of the following parts by weight: 50 parts Kaolin, 10 parts of quartz, 8 parts of muscovite, 3 parts of iron oxide, 1 part of manganese oxide, 2 parts of calcium oxide;

[0034] c. After the clay obtained in operation b is molded, dried in the shade, and repaired, the green body is prepared for subsequent use;

[0035] (2) Biscuit treatment:

[0036] Put t...

Embodiment 2

[0052] A method for combined firing of painted pottery and black pottery, comprising the steps of:

[0053] (1) Green body preparation:

[0054] a. Put the yellow glue mud in the sun for exposure treatment, then crush the yellow glue mud after the sun exposure treatment, put it into clear water, stir and wash it continuously, and finally filter it to obtain the yellow glue mud for later use;

[0055]b. Add the mixed soil of 20% of its total mass to the yellow glue slurry obtained after the operation a treatment, put it into the mixer and mix it uniformly to get the green clay for subsequent use; the mixed soil is made up of the following parts by weight: 55 parts Kaolin, 15 parts of quartz, 12 parts of muscovite, 5 parts of iron oxide, 3 parts of manganese oxide, 4 parts of calcium oxide;

[0056] c. After the clay obtained in operation b is molded, dried in the shade, and repaired, the green body is prepared for subsequent use;

[0057] (2) Biscuit treatment:

[0058] Put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a painted pottery and black pottery combined sintering process. The method comprises the following steps: 1) preparing a blank body; 2) performing briscuit firing; 3) performing glaze firing; 4) performing surface treatment; and 5) performing carburizing firing. The painted pottery and black pottery combined sintering process makes improved treatment on a pottery sinteringtechnology, a finally prepared pottery is a finished product by combing a painted pottery and a black pottery, and can present strong color contrast and visual impact, the color compatibility is uniform, the product has good appearance condition and artistic effect, and has market competitiveness and economic benefit.

Description

technical field [0001] The invention belongs to the technical field of pottery firing, and in particular relates to a process method for combined firing of painted pottery and black pottery. Background technique [0002] The invention of pottery is a symbol of human civilization and a stage in the development of farming culture. Pottery is not a unique invention in China. Its origins are diverse. It is the product of the development of farming culture to a certain stage and an important part of the splendid ancient culture. During archaeological excavations, series of red pottery, gray pottery, white pottery, painted pottery, black pottery and glazed pottery were found. Black pottery is exquisite black pottery. Black pottery is characterized by simple decoration, dignified and graceful shape, fine and moist texture, calm and elegant luster. It is a bright pearl bred in the long history of Chinese culture and is known as "The art of earth and fire, the crystallization of po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/32C04B33/16C04B41/89
CPCC04B33/16C04B33/32C04B41/009C04B41/52C04B41/89C04B2235/3208C04B2235/3262C04B2235/3272C04B2235/3472C04B41/5022C04B41/4572C04B41/5001C04B41/5031C04B41/0072
Inventor 张玲
Owner 界首市十三窑工艺美术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com