Anti-slipping artificial stone

An artificial stone and anti-slip technology, which is applied in the field of building materials, can solve the problems of uneven density of the patterned plate on the surface of the plate, difficult dispersion of materials in the mold, harmful waste gas, waste water, etc., to achieve controllable and uniform pattern, and increase the hardness and thickness requirements , Cloth easy effect

Inactive Publication Date: 2018-02-13
JIANGSU MINJIANG MINING CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing resin-type artificial stone slab technology is to stir and mix the resin and quartz sand powder before forming the upper mold. After the resin is opened, it will chemically react with the air, and the solvent will start to volatilize. Therefore, it will be affected by time when the mold is placed. Restricted, and because the viscosity of the resin adhesive has been expressed, the material in the mold is difficult to disperse, and the distribution is uneven, resulting in the pattern on the surface of the plate and uneven density of each part of the plate. Different densities will cause different stress and easy deformation
[0003] At present, all traditional artificial stone plates use unsaturated resin as adhesive, so accelerator, coupling agent and curing agent are needed as chemical auxiliary materials. Specific disadvantages: 1. There are harmful waste gas and waste water in the process of processing
2. The board has harmful substances precipitated during use and should not be in direct contact with food
3. The surface hardness is low, generally around 6 Mohs, and the finish is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The anti-slip artificial stone of the present invention is made of the following components in proportion by weight fraction:

[0017] Proportion by weight fraction is made from the following components:

[0018] 18 parts of low-melting glass powder, 40 parts of resin, 44 parts of quartz sand, 30 parts of inorganic pellets, 16 parts of quartz powder, 20 parts of coarse stone powder, 2 parts of accelerator, 5 parts of low-melting glass powder, 41 parts of water, emulsion glue 3 parts, 6 parts of water reducer, 23 parts of hollow glass microspheres, 3 parts of pigment, 2 parts of dye.

[0019] In the above formula, the particle size of quartz sand is 10-20 mesh, 30%, 30-60 mesh, 25%, 60-80 mesh, 30%, 80-100 mesh, 10%, and 100-120 mesh. Accounting for 5%, the particle size of glass powder is 400-500 mesh accounting for 26%, the particle size of quartz powder is 150-250 mesh accounting for 28%, 250-300 mesh accounting for 30%, and 300-400 mesh accounting for 16%. Glass po...

Embodiment 2

[0021] The anti-slip artificial stone of the present invention is made of the following components in proportion by weight fraction:

[0022] Proportion by weight fraction is made from the following components:

[0023] 21 parts of low-melting glass powder, 40 parts of resin, 57 parts of quartz sand, 30 parts of inorganic pellets, 21 parts of quartz powder, 20 parts of coarse stone powder, 6 parts of accelerator, 5 parts of low-melting glass powder, 53 parts of water, emulsion glue 4 parts, 9 parts of water reducer, 43 parts of hollow glass microspheres, 5 parts of pigment, 3 parts of dye.

[0024] In the above formula, the particle size of quartz sand is 10-20 mesh, 30%, 30-60 mesh, 25%, 60-80 mesh, 30%, 80-100 mesh, 10%, and 100-120 mesh. Accounting for 5%, the particle size of glass powder is 400-500 mesh accounting for 26%, the particle size of quartz powder is 150-250 mesh accounting for 28%, 250-300 mesh accounting for 30%, and 300-400 mesh accounting for 16%. Glass po...

Embodiment 3

[0026] The anti-slip artificial stone of the present invention is made of the following components in proportion by weight fraction:

[0027] Proportion by weight fraction is made from the following components:

[0028] 20 parts of low-melting glass powder, 40 parts of resin, 50 parts of quartz sand, 30 parts of inorganic pellets, 18 parts of quartz powder, 20 parts of coarse stone powder, 4 parts of accelerator, 5 parts of low-melting glass powder, 47 parts of water, emulsion glue 3 parts, 7 parts of water reducer, 33 parts of hollow glass microspheres, 4 parts of pigment, 2 parts of dye.

[0029] In the above formula, the particle size of quartz sand is 10-20 mesh, 30%, 30-60 mesh, 25%, 60-80 mesh, 30%, 80-100 mesh, 10%, and 100-120 mesh. Accounting for 5%, the particle size of glass powder is 400-500 mesh accounting for 26%, the particle size of quartz powder is 150-250 mesh accounting for 28%, 250-300 mesh accounting for 30%, and 300-400 mesh accounting for 16%. Glass po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an anti-slipping artificial stone. The anti-slipping artificial stone is prepared from the following components in parts by weight: 18 to 21 parts of low-melting glass powder,40 parts of resin, 44 to 57 parts of quartz sand, 30 parts of inorganic matter aggregates, 16 to 21 parts of quartz powder, 20 parts of middling flour, 2 to 6 parts of an accelerant, 5 parts of low-melting glass powder, 41 to 53 parts of water, 3 to 4 parts of an emulsion adhesive, 6 to 9 parts of a water reducing agent, 23 to 43 parts of hollow glass microspheres, 3 to 5 parts of a pigment and 2to 3 parts of a dyestuff. The anti-slipping artificial stone provided by the invention has the advantages that various materials are prepared to form an artificial quartz stone with an extremely goodline effect.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an anti-slip artificial stone. Background technique [0002] The existing resin-type artificial stone slab technology is to stir and mix the resin and quartz sand powder before forming the upper mold. After the resin is opened, it will chemically react with the air, and the solvent will start to volatilize. Therefore, it will be affected by time when the mold is placed. Due to the viscosity of the resin adhesive, it is difficult to disperse the material in the mold, and the distribution is uneven, resulting in uneven density on the surface of the plate and various parts of the plate. Different densities will cause different stress and easy deformation. [0003] At present, all traditional artificial stone panels use unsaturated resin as adhesive, so accelerator, coupling agent and curing agent are needed as chemical auxiliary materials. Specific disadvantages: 1. There are harmf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/00
CPCC04B30/00C04B2111/00362C04B14/22C04B14/06C04B14/02C04B2103/0068C04B24/24C04B2103/302C04B14/24C04B2103/54
Inventor 施路明
Owner JIANGSU MINJIANG MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com