Environment-friendly plastic and forming method thereof

A plastic and environmentally friendly technology, applied in the field of plastics, can solve the problems of failing to meet environmental protection requirements, poor degradability, toxic and odorous, etc., and achieve the effects of low cost, good plasticity, and improved environmental protection.

Inactive Publication Date: 2018-02-06
德阳市米雅乐食品厂
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most plastic materials are poisonous and smelly, have poor degradation ability, and are easy to cause pollution to the environment, so they cannot meet the requirements of environmental protection and are restricted by the state. The environmentally friendly plastic and its forming method proposed by the present invention can effectively solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of environmental protection plastic that the present invention proposes, comprises the raw material of following parts by weight: 12 parts of natural latex, 20 parts of polyethylene resin, 12 parts of polypropylene resin, 18 parts of calcium carbonate, 14 parts of starch, 9 parts of talcum powder, biodegradation agent 15 parts, 10 parts of zinc laurate soap, 8 parts of dioctyl phthalate, 9 parts of chlorinated paraffin, 6 parts of castor oil.

[0020] Its formation method comprises the following steps:

[0021] S1. Add calcium carbonate to the pulverizer according to the specific gravity, and pulverize for 15 minutes to obtain calcium carbonate powder;

[0022] S2. Heat polyethylene resin, natural rubber latex, and chlorinated paraffin to 94°C according to the specific gravity, stir while adding, and wait until they are fully melted to obtain mixture A;

[0023] S3. Add polypropylene resin, calcium carbonate powder, di-sec-octyl phthalate, and talc powder to mix...

Embodiment 2

[0027] A kind of environment-friendly plastic that the present invention proposes comprises the raw material of following parts by weight: 15 parts of natural latex, 25 parts of polyethylene resin, 15 parts of polypropylene resin, 20 parts of calcium carbonate, 12 parts of starch, 10 parts of talcum powder, biodegradation agent 15 parts, zinc laurate soap 12 parts, dio-octyl phthalate 9 parts, chlorinated paraffin 8 parts, castor oil 10 parts.

[0028] Its formation method comprises the following steps:

[0029] S1, add calcium carbonate in the pulverizer according to the specific gravity, and pulverize for 20 minutes to obtain calcium carbonate powder;

[0030] S2. Heat polyethylene resin, natural rubber latex, and chlorinated paraffin to 95°C according to the specific gravity, stir while adding, and wait until they are fully melted to obtain mixture A;

[0031] S3. Add polypropylene resin, calcium carbonate powder, di-sec-octyl phthalate, and talc powder to mixture A accord...

Embodiment 3

[0035] A kind of environment-friendly plastic that the present invention proposes comprises the raw material of following parts by weight: 18 parts of natural latex, 35 parts of polyethylene resin, 18 parts of polypropylene resin, 20 parts of calcium carbonate, 15 parts of starch, 12 parts of talcum powder, biodegradation agent 14 parts, zinc laurate soap 12 parts, di-sec-octyl phthalate 13 parts, chlorinated paraffin 14 parts, castor oil 10 parts.

[0036] Its formation method comprises the following steps:

[0037] S1, add calcium carbonate in the pulverizer according to the specific gravity, and pulverize for 18 minutes to obtain calcium carbonate powder;

[0038] S2. Heat polyethylene resin, natural rubber latex, and chlorinated paraffin to 98°C according to the specific gravity, stir while adding, and wait until they are fully melted to obtain mixture A;

[0039] S3. Add polypropylene resin, calcium carbonate powder, dioctyl phthalate, and talc powder to mixture A accord...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmentally friendly plastic, which comprises the following raw materials in parts by weight: 10-20 parts of natural latex, 10-40 parts of polyethylene resin, 10-20 parts of polypropylene resin, 15-25 parts of calcium carbonate, and 10-18 parts of starch 5-15 parts of talcum powder, 12-18 parts of biodegradation agent, 8-15 parts of zinc laurate soap, 5-15 parts of di-sec-octyl phthalate, 5-15 parts of chlorinated paraffin, 4 parts of lubricant ‑12 servings. The environmentally friendly plastic proposed by the invention is non-toxic and odorless, will not cause air and environmental pollution, has good plasticity, can produce various plastic products suitable for production or daily life, has strong practicability, and the added biodegradant improves The degradability of the plastic improves its environmental protection. The production process of the invention is simple, the raw materials are easy to obtain, and the cost is low.

Description

technical field [0001] The invention relates to the field of plastics, in particular to an environmentally friendly plastic and a forming method thereof. Background technique [0002] The environment is the basic premise of human survival and development. With the development of social economy, environmental issues have become an unavoidable important issue. As a common product in production and daily life, plastic has a huge production volume. At present, most plastic materials are poisonous and odorous, have poor degradation ability, and are easy to pollute the environment, so they cannot meet the environmental protection requirements and are restricted by the state. The environmentally friendly plastic and its forming method proposed by the present invention can effectively solve the above problems. Contents of the invention [0003] The object of the present invention is to solve the shortcomings in the prior art, and propose an environment-friendly plastic and its fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L7/02C08L23/12C08L3/02C08L91/06C08L91/00C08K13/02C08K3/26C08K3/34C08K5/098C08K5/12
CPCC08L23/06C08L2201/06C08L2205/02C08L2205/035C08L7/02C08L23/12C08L3/02C08L91/06C08L91/00C08K13/02C08K2003/265C08K3/34C08K5/098C08K5/12
Inventor 易光容
Owner 德阳市米雅乐食品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com