Degradable highly-elastic sponge and preparation technology thereof

A sponge and high-elastic technology, applied in the sponge field, can solve the problems of poor mechanical properties of low-density sponges that cannot meet the standards of seat cushion sponges, high production costs of high-density sponges, and difficulty in degrading artificial polymers, and achieves high environmental protection value. Strong foaming ability and the effect of improving physical properties

Inactive Publication Date: 2018-02-02
德清舒华泡沫座椅有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the high production cost of the above-mentioned high-density sponge, the poor mechanical properties of the low-density sponge cannot meet the standard of seat cushion sponge, and the pollution generated in the preparation process of the sponge is relatively large, the artificial high polymer is difficult to degrade, and the foaming agent is In order to solve the problems of harming people and polluting the environment during the soaking process, it provides a product containing healthy green natural ingredients, the production process is environmentally friendly, has no pollution to the environment, has no harm to the human body, can avoid resource waste and environmental pollution, and has resilience and permanent compression. Degradable high-elastic sponge with mechanical properties such as deformation values ​​in line with international standards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Preparation of pineapple superfine powder suspension:

[0034] a) Put pineapple in an ultrafine pulverizer for ultrafine pulverization, and the pulverization time is 15 minutes to obtain pineapple superfine powder;

[0035] b) Add 10% casein solution to the pineapple superfine powder obtained in step a), the weight of the added 10% casein solution is 75% of the weight of pineapple, to obtain a mixture;

[0036] c) Add an appropriate amount of water to the mixture obtained in step b) to prepare a pineapple superfine powder suspension with a total solid content of 9%.

[0037] Preparation of environmentally friendly and degradable low-density sponge:

[0038] 1) Add formaldehyde to the natural latex, stir it, the stirring speed is 100r / min, and the stirring time is 10min, to obtain formaldehyde latex;

[0039] 2) Mix and grind sulfur, zinc dibenzyldithioaminomethanol and 2-mercaptobenzothiazole, stir and disperse fully, add to the formaldehyde latex obtained in step 1),...

Embodiment 2

[0046] Preparation of pineapple superfine powder suspension:

[0047] a) Put pineapple in an ultrafine pulverizer for ultrafine pulverization, and the pulverization time is 60 minutes to obtain pineapple superfine powder;

[0048] b) Add 10% casein solution to the pineapple superfine powder obtained in step a), the weight of the added 10% casein solution is 80% of the weight of pineapple, to obtain a mixture;

[0049] c) Add an appropriate amount of water to the mixture obtained in step b) to prepare a pineapple superfine powder suspension with a total solid content of 11%

[0050] Preparation of environmentally friendly and degradable low-density sponge:

[0051] 1) Add formaldehyde to the natural latex, stir it, the stirring speed is 80r / min, and the stirring time is 15min, to obtain formaldehyde latex;

[0052] 2) Mix and grind sulfur, zinc dibenzyldithioaminomethanol and 2-mercaptobenzothiazole, stir and disperse fully, add to the formaldehyde latex obtained in step 1), ...

Embodiment 3

[0059] Preparation of pineapple superfine powder suspension:

[0060] a) Put pineapple in an ultrafine pulverizer for ultrafine pulverization, and the pulverization time is 30 minutes to obtain pineapple superfine powder;

[0061] b) Add 10% casein solution to the pineapple superfine powder obtained in step a), the weight of the added 10% casein solution is 78% of the weight of pineapple, to obtain a mixture;

[0062] c) Add an appropriate amount of water to the mixture obtained in step b) to prepare a pineapple superfine powder suspension with a total solid content of 10%

[0063] Preparation of environmentally friendly and degradable low-density sponge:

[0064] 1) Add formaldehyde to the natural latex and stir it at a stirring speed of 90r / min for a stirring time of 12min to obtain formaldehyde latex;

[0065] 2) Mix and grind sulfur, zinc dibenzyldithioaminomethanol and 2-mercaptobenzothiazole, stir and disperse fully, add to the formaldehyde latex obtained in step 1), a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to degradable highly-elastic sponge and a preparation technology thereof. The degradable highly-elastic sponge and the preparation technology thereof have the advantages that thedegradable highly-elastic sponge is made of green, natural and healthy materials according to the environment-friendly preparation technology, harmless to human bodies and capable of avoiding resource waste and environment pollution, and its mechanical properties including rebound resilience and compression set value are in compliance with the international standards; through adoption of recyclable pineapple fibers, resource waste is reduced and physical properties of low-density sponge with natural latex matrixes are improved to comply with the international standards; sodium alcohol ether sulphate and sodium lauryl sulfate which serve as foaming agents substitute for traditional pollutional ones to further avoid pollution; the high-performance low-density sponge with the excellent mechanical properties can be produced at a low preparation cost; the preparation technology is safe, simple and environment friendly.

Description

technical field [0001] The invention relates to the field of a sponge, in particular to a sponge containing healthy green natural ingredients, the production process is environmentally friendly, has no pollution to the environment, has no harm to the human body, can avoid waste of resources and environmental pollution, and has mechanical properties such as resilience and compression permanent deformation values ​​in line with International standard degradable high-elastic sponge and its preparation process. Background technique [0002] Sponge is a very common porous material with good water absorption, some of which have good elasticity, deformation recovery and other properties, and can be used to clean items or to produce some comfortable and soft seat cushions. [0003] Commonly used sponges are made from wood cellulose fibers or expanded plastic polymers. Alternatively, there are natural sponges made from spongy animals, and most natural sponges are used for body clean...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/02C08L97/02C08L89/00C08K13/02C08K3/34C08K3/22C08K3/06C08K5/47C08J9/28C08J9/04
CPCC08J9/28C08J9/0033C08J9/0052C08J9/0061C08J9/0066C08J9/0085C08J9/04C08J2201/0484C08J2203/18C08J2307/02C08J2489/00C08J2497/02
Inventor 卢伟
Owner 德清舒华泡沫座椅有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products