Pretreatment method of cunninghamia lanceolata floor board material

A pretreatment and flooring technology, applied in wood treatment, wood treatment details, impregnated wood, etc., can solve problems such as unfavorable sustainable development of Chinese fir plantations, low fir prices, poor anti-deformation ability of fir, etc., and achieve scientific and reasonable process design. , good performance, the effect of improving stability

Inactive Publication Date: 2018-01-30
RONGSHUI DINGFENG BAMBOO & WOOD PROD CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ability of Chinese fir to resist deformation is poor, resulting in a long-term slump in the price of Chinese fir, which is not conducive to the sustainable development of Chinese fir plantations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pretreatment method of cunninghamia lanceolata floor board material
  • Pretreatment method of cunninghamia lanceolata floor board material
  • Pretreatment method of cunninghamia lanceolata floor board material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] like Figure 1-2 Shown, a kind of pretreatment method of Chinese fir floor material, comprises the following steps:

[0031] S1: Treat the fir floor material with oil, soak the fir floor material in vegetable oil, heat the vegetable oil to 50°C, and soak for 2 hours;

[0032] S2: Take out the soaked fir floor material, and dry it at 60°C for 1 hour;

[0033] S3: The fir floor material dried in S2 is subjected to a second oil treatment, and the fir floor material treated in S2 is immersed in vegetable oil again, and the vegetable oil is heated to 60° C. for 1 hour;

[0034] S4: leave the fir floor material after S3 processing under vacuum condition, and the standing time is 2h;

[0035] S5: Place the bamboo slices obtained in S4 in ethanol, soak for 20 minutes, and take them out;

[0036] S6: Place the fir flooring material at 40°C and a pressure of 1.2MPa for 5 hours;

[0037] S7: drying the fir floor material treated in S6 to ensure a moisture content of 2%.

Embodiment 2

[0039] like Figure 3-4 Shown, a kind of pretreatment method of Chinese fir floor material, comprises the following steps:

[0040] S1: Treat the fir floor material with oil, soak the fir floor material in vegetable oil, heat the vegetable oil to 50°C, and soak for 2 hours;

[0041] S2: Take out the soaked fir floor material, and dry it at 60°C for 1 hour;

[0042] S3: The fir floor material dried in S2 is subjected to a second oil treatment, and the fir floor material treated in S2 is immersed in vegetable oil again, and the vegetable oil is heated to 60° C. for 1 hour;

[0043] S4: leave the fir floor material after S3 processing under vacuum condition, and the standing time is 2h;

[0044] S5: Place the bamboo slices obtained in S4 in ethanol, soak for 20 minutes, and take them out;

[0045] S6: Place fir flooring materials at 50°C and a pressure of 1.5MPa for 10 hours;

[0046] S7: drying the fir floor material treated in S6 to ensure a moisture content of 3%.

Embodiment 3

[0048] A kind of pretreatment method of Chinese fir floor material, comprises the following steps:

[0049] S1: Treat the fir floor material with oil, soak the fir floor material in vegetable oil, heat the vegetable oil to 50°C, and soak for 4 hours;

[0050] S2: Take out the soaked fir floor material, and dry it at 60°C for 2 hours;

[0051] S3: The fir floor material dried in S2 is subjected to a second oil treatment, and the fir floor material treated in S2 is immersed in vegetable oil again, and the vegetable oil is heated to 60° C. for 2 hours;

[0052] S4: leave the fir floor material after S3 processing under vacuum condition, and the standing time is 2h;

[0053] S5: Place the bamboo slices obtained in S4 in ethanol, soak for 40 minutes, and take them out;

[0054] S6: Place the fir floor material at 40°C and a pressure of 1.5MPa for 5 hours;

[0055] S7: drying the fir floor material treated in S6 to ensure a moisture content of 3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pretreatment method of a cunninghamia lanceolata floor board material. The method comprises the following steps of S1, performing oil treatment on the cunninghamia lanceolatafloor board material; soaking the cunninghamia lanceolata floor board material into plant oil; S2, taking out the soaked cunninghamia lanceolata floor board material; performing drying treatment; S3,performing secondary oil treatment on the cunninghamia lanceolata floor board material dried in the step S2; soaking the cunninghamia lanceolata floor board material treated in the step S2 into the plant oil again; S4, performing still standing on the cunninghamia lanceolata floor board material treated in the step S3 under the vacuum condition; S5, putting bamboo sheets obtained in the step S4 into ethanol; S6, putting the cunninghamia lanceolata floor board material for 5 to 10h in the environment being 40 to 50 DEG C at the pressure being 1.2 to 1.5MPa; S7, drying the cunninghamia lanceolata floor board material treated in the step S6; ensuring the moisture content being 2 to 3 percent. The pretreatment method of the cunninghamia lanceolata floor board material disclosed by the invention has the advantages that the process design is scientific and reasonable; according to the self performance characteristics of the cunninghamia lanceolata, the scientific method is used for modifying the cunninghamia lanceolata floor board material; the cunninghamia lanceolata is enabled to have good performance; cracking and deformation cannot occur; the stability of the cunninghamia lanceolatafloor board material is greatly improved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a pretreatment method for fir flooring materials. Background technique [0002] Chinese fir (Cunninghamia Lanceolata) is a unique fast-growing commercial timber tree species in my country. It grows fast and has good materials. It is artificially cultivated in large quantities at the Dafeng fir base. The wood texture is straight, the structure is uniform, not warped or cracked, the bulk density of the wood is 0.39, the average number of annual rings per centimeter is 3.0, the rate of late wood is 22.0%, the drying shrinkage coefficient (volume) is 0.386, and the ultimate compressive strength along the grain is 358 kg / cm2 , the static bending limit strength is 661 kg / cm2, and the end face strength is 285 kg / cm2. The material is light and tough, with moderate strength and high quality coefficient. It has a fragrance, and the wood contains "Shannao", which can resist ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/04B27K5/00B27K3/34
Inventor 廖岁顽
Owner RONGSHUI DINGFENG BAMBOO & WOOD PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap