Glaze for Jun porcelain plate and preparation method of glaze

A technology for glazes and porcelain plates, applied in the field of preparation of glazes for porcelain, to achieve uniform glaze particles and good glaze coating effect

Inactive Publication Date: 2018-01-16
YUZHOU ZHENGYUJUN KILN CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The above-mentioned process steps were obtained by the groping of Jun porcelain masters in the past dynasties, and they are also textbook-like classics well known to those skilled in the art. However, the applicant believes that Jun porcelain plates have certain particularities, as the body is thin and the glazed area is large. , considering that the inner surface and the outer peripheral surface of the disc parison have different ornamental values, and the inner surface of the disc parison is mainly used as the main ornamental surface, and the rest of the outer peripheral surfaces are used as auxiliary. Therefore, according to the conventional operation steps, only the A layer of glaze slurry with a suitable thickness is attached to the outer surface of the plain tire, which does not bring good results. Therefore, the applicant believes that since the inner surface is the main ornamental part, the glaze used by the two should be different. Therefore, the applicant has worked out a brand-new glazing formula and its preparation method applied to the disc parison through several years of exploration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A method for preparing a glaze for a Jun porcelain plate, characterized in that it includes a surface glaze preparation step and a bottom glaze preparation step;

[0034] Described surface glaze preparation step, concrete operation method is as follows:

[0035] Step 1. Take the above-mentioned parts of copper oxide, tin dioxide and zinc oxide and add them to the ball mill, grind for 10-12 hours, and collect the ground raw materials through 100 mesh for later use;

[0036] Step 2: Take the talc, potassium feldspar, feldspar and kaolinite in the above number and add them to a ball mill, grind for 10-12 hours, and collect the ground raw materials through 100 mesh for later use;

[0037] Step 3, put the powder obtained in step 1, the powder obtained in step 2 and the above-mentioned number of glass powders into the mixer and mix for 1-2 hours, then take out the mixture and set aside;

[0038] Step 4: Put the mixture prepared in step 3 into the ball mill, grind again for 1...

Embodiment 1

[0044] Embodiment one, a kind of glaze material that Jun porcelain plate is used, described glaze material is made up of bottom glaze and surface glaze, and described bottom glaze is made of copper oxide 4.5 parts, potassium feldspar 13 parts, kaolinite 9 parts, 1.5 parts of tin dioxide, 10 parts of talc, 13 parts of feldspar and 15 parts of glass powder; the surface glaze is composed of 4.5 parts of copper oxide, 13 parts of talc, 4.5 parts of tin dioxide, 4 parts of zinc oxide, and 10 parts of potassium feldspar. 8 parts of feldspar stone, 13 parts of kaolinite and 15 parts of glass powder.

[0045] A method for preparing a glaze for Jun porcelain dishes, comprising a top glaze preparation step and a bottom glaze preparation step;

[0046]The preparation steps of the surface glaze, the specific operation method is as follows: take the above-mentioned parts of copper oxide, tin dioxide and zinc oxide and add them to the ball mill, grind for 10 hours, and collect the ground ma...

Embodiment 2

[0051] Embodiment two, a kind of glaze that Jun porcelain plate is used, described glaze is made up of bottom glaze and surface glaze, and described bottom glaze is made of copper oxide 4.5 parts, potassium feldspar 13 parts, kaolinite 9 parts, 1.5 parts of tin dioxide, 10 parts of talc, 13 parts of feldspar, and 15 parts of glass powder; the surface glaze is composed of 4.5 parts of copper oxide, 13 parts of talc, 1.5 parts of tin dioxide, 4 parts of zinc oxide, and potassium feldspar 10 parts, 8 parts of feldspar stone, 13 parts of kaolinite and 15 parts of glass powder.

[0052] A method for preparing a glaze for Jun porcelain dishes, comprising a top glaze preparation step and a bottom glaze preparation step;

[0053] The preparation steps of the surface glaze, the specific operation method is as follows: take the above-mentioned parts of copper oxide, tin dioxide and zinc oxide and add them to the ball mill, grind for 12 hours, and collect the ground materials through 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses glaze for a Jun porcelain plate and a preparation method of the glaze. The glaze is prepared from ground glaze and cover glaze, wherein the ground glaze is prepared from 4-5 parts of copper oxide, 10-16 parts of potash feldspar, 8-12 parts of kaolinite, 1-2 parts of tin dioxide, 8-12 parts of talc, 10-16 parts of Changbai stone and 10-20 parts of glass powder; the cover glaze is prepared from 4-5 parts of copper oxide, 10-16 parts of talc, 4-5 parts of tin dioxide, 2-6 parts of zinc oxide, 8-12 parts of potash feldspar, 5-10 parts of Changbai stone, 10-16 parts of kaolinite and 10-20 parts of glass powder. Uniform particles of the glaze are guaranteed by optimizing the formula of the cover glaze and the ground glaze for the Jun porcelain plate and performing fine adjustment on the preparation process of the cover glaze and the ground glaze, and the glazing effect is better.

Description

technical field [0001] The invention relates to a method for preparing a glaze for porcelain, in particular to a glaze for Jun porcelain plates and a preparation method thereof. Background technique [0002] At present, there are mainly three kinds of porcelain handicrafts: Jun porcelain, Ru porcelain and peony porcelain. The advantage of peony porcelain is that it takes the natural shape of peony as the main theme and makes the three-dimensional shape of peony flower on top of porcelain. The creative achievement of the organic integration of peony culture has a very high value of cultural research, craft research, artistic aesthetics and collection gifts. Ru porcelain and Jun porcelain also have their own advantages, and Jun porcelain has its own advantages. [0003] With the unique artistic effect of natural kiln transformation, it is unique and outstanding in the porcelain forest. The artistic effect of the glaze color kiln change of Jun porcelain is not artificial, but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00
Inventor 王现锋
Owner YUZHOU ZHENGYUJUN KILN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap