Jun porcelain celeste blue glaze and preparation method thereof

A technology of porcelain celadon glaze and celadon glaze, which is applied in the field of Jun porcelain celadon glaze and its preparation, can solve the problems of poor corrosion resistance and mechanical resistance of the glaze surface, low yield rate, high production cost and high production difficulty, etc. Achieve the effects of promoting economic development, increasing opacity, and promoting the improvement of common technologies

Inactive Publication Date: 2018-01-12
禹州市锦丰源瓷业有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention provides a kind of jun porcelain celadon glaze with scientific raw materials and proportioning and its preparation method to solve the problem that the existing jun ware celadon glaze has few formulas and preparation methods, and the glaze surface has poor corrosion resistance and mechanical resistance. Low yield, high production cost and difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jun porcelain celeste blue glaze and preparation method thereof
  • Jun porcelain celeste blue glaze and preparation method thereof
  • Jun porcelain celeste blue glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A celadon glaze for Jun porcelain, prepared from the following raw materials in parts by weight: 32-40 parts of feldspar, 14-18 parts of quartz, 10-14 parts of calcite, 10-14 parts of this medicine, and 4-6 parts of spodumene , talc 3-5 parts, iron oxide 0.5-1.5 parts, copper ore 4-6 parts, tin oxide 0.5-1.5 parts, wood ash 6-10 parts.

[0026] The preparation method of above-mentioned Jun porcelain sky green glaze comprises the following steps:

[0027] (1) Crush the above raw materials and put them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 56-58%, wet mill for 6-8 hours, and pass the wet milled slurry through a 200-300 mesh sieve to obtain the glaze slurry ;

[0028] (2) The green body is dipped in glaze 1-2 times;

[0029] (3) Firing, the firing temperature is 1260-1290°C.

[0030] The firing process in step (3) specifically includes the following steps:

[0031] ①The body after glazing is put into the kiln and...

Embodiment 2

[0036] A celadon glaze for Jun porcelain, prepared from the following raw materials in parts by weight: 36 parts of feldspar, 16 parts of quartz, 12 parts of calcite, 12 parts of this medicine, 5 parts of spodumene, 4 parts of talc, 1 part of iron oxide, 5 parts of copper ore, 1 part of tin oxide, and 8 parts of wood ash.

[0037] The preparation method of above-mentioned Jun porcelain sky green glaze, comprises the following steps:

[0038] (1) Crush the above raw materials and put them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 56-58%, wet mill for 6-8 hours, and pass the wet milled slurry through a 200-300 mesh sieve to obtain the glaze slurry ;

[0039] (2) The green body is dipped in glaze twice;

[0040] (3) Firing, specifically including the following steps:

[0041] ①The body after glazing is put into the kiln and fired in an oxidizing atmosphere, so that the temperature rises evenly to 1020°C in 5 hours;

[0042]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a jun porcelain celeste blue glaze which is prepared from the following raw materials in parts by weight: 32-40 parts of melilite, 14-18 parts of quartz, 10-14 parts of calcite, 10-14 parts of herb drug, 4-6 parts of spodumene, 3-5 parts of talc, 0.5-1.5 parts of ferric oxide, 4-6 parts of copper ore, 0.5-1.5 parts of tin oxide and 6-10 parts of wood ash. A preparation method for the jun porcelain celeste blue glaze comprises the following steps: (1) crushing the raw materials, mixing and putting into a ball mill for milling, adding water till the mass concentration ofthe glaze reaches up to 56-58%, wetly milling for 6-8 hours and using a 200-300 mesh sieve for sieving the wetly milled slurry, thereby acquiring glaze slip; (2) soaking the blank into the glaze slipfor 1-2 times; (3) sintering under the sintering temperature of 1260-1290 DEG C.

Description

technical field [0001] The invention relates to the technical field of Jun porcelain manufacturing, in particular to a Jun porcelain sky blue glaze and a preparation method thereof. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family with a lot of money is not as good as a piece of Jun porcelain". [0003] Jun Porcelain is a unique national treasure porcelain in Shenhou Town, Yuzhou City, Xuchang City, Henan Province. With its simple shape, exquisite craftsmanship, complex glaze matching, and the magical kiln transformation of "one color in the kiln, thousands of colors in the kiln", the scenery of lakes and mountains, clouds and clouds Fog, human, animal, flower, bird, insect, fish, etc. are known as the first of the "Five Famous Porcelains" i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/86
Inventor 崔松伟温红超崔世豪崔鹏豪
Owner 禹州市锦丰源瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap