A kind of liquid polyisoprene rubber and preparation method thereof

A technology of polyisoprene and isoprene, which is applied in the field of liquid polyisoprene rubber and its preparation, can solve the problems of poor molecular chain linearity, fast anionic polymerization rate, and reduced reaction rate, and achieve economical Desolvent removal link, good industrial application value, and the effect of improving production efficiency

Active Publication Date: 2020-06-09
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, free radical polymerization is mainly used in China to produce liquid rubber. Its advantage is low cost, and its disadvantages are poor linearity of molecular chains, easy branching, wide molecular weight distribution, and difficulty in microstructure adjustment.
[0004] The molecular weight distribution of liquid polyisoprene rubber obtained by anionic polymerization is narrow, the microstructure and molecular weight distribution can be adjusted freely, and the quality is uniform, but there are also significant disadvantages: the anionic polymerization rate is extremely fast, the polymerization heat is difficult to withdraw in time, low molecular weight and At high monomer concentration, the conversion of the monomer is completed in a short time, the temperature of the polymerization system is as high as 300-400°C, the side reaction is very serious, and the product performance deteriorates
Due to the use of retarded anionic polymerization technology, the concentration of polymerized monomers has been greatly increased and the production efficiency has been improved, but there are disadvantages that the viscosity of the system increases sharply in the later stage and the reaction rate decreases sharply.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] The invention provides a kind of preparation method of liquid polyisoprene rubber, the method comprises:

[0017] (1) In the presence of an organolithium compound and a non-polar solvent, the isoprene is subjected to an initiation reaction, and the initiation reaction time is 1-8 minutes;

[0018] (2) In the presence of a retarder, the product of the initiating reaction is subjected to the first polymerization reaction to a conversion rate of isoprene of 70% by weight or more; wherein, the retarder is selected from one of the metal alkyl compounds one or more kinds;

[0019] (3) In the presence of an accelerator, the product of the first polymerization reaction is subjected to a second polymerization reaction; wherein, the accelerator is one or more of saturated ether compounds.

[0020] According to the present invention, in step (1), the isoprene is made to obtain a small molecular weight isoprene polymer active chain with an active end under the trigger of the organ...

Embodiment 1

[0055] This example is used to illustrate the liquid polyisoprene rubber of the present invention and its preparation method.

[0056] Under nitrogen protection, 1650 g of n-heptane and 720 g of isoprene were added to the reaction vessel, and 130 mL of a hexane solution of n-butyllithium (1mol.L -1 , the same below) to react for 2min; then add 110mL triisobutylaluminum hexane solution (1mol.L -1 , the same below), heated to 90°C for 80 minutes of polymerization (the conversion rate of isoprene was 83% by weight, and the highest temperature of the polymerization system was 122°C); then 165mL THF (about 2mol) was added, and the reaction was carried out at 90°C for 1.5h ; Continuously feed carbon dioxide gas into the reaction system at 80° C., the pressure is 0.5 MPa, and the time is 20 min; stop feeding carbon dioxide gas, and add 1520 antioxidant (purchased from Ciba, Switzerland) with a weight ratio of 1:1 after 10 min. Chemical (China) Co., Ltd., hereinafter the same) and 10...

Embodiment 2

[0058] This example is used to illustrate the liquid polyisoprene rubber of the present invention and its preparation method.

[0059] Under nitrogen protection, 1200g of isooctane and 1200g of isoprene were added to the reaction vessel, and 120mL of a hexane solution of sec-butyllithium (1mol.L -1 , the same below) to react for 4 minutes; then add 102 mL of a hexane solution of triisobutylaluminum and heat to 80° C. to carry out a polymerization reaction for 100 minutes (the conversion rate of isoprene is 86% by weight, and the maximum temperature of the polymerization system is 124° C.); then Add 50mL THF (about 0.6mol), and react at 80°C for 1.4h; continuously feed carbon dioxide gas into the reaction system at 70°C, the pressure is 0.6MPa, and the time is 15min; stop feeding carbon dioxide gas, and add after 10min After 2.4g of the mixture of 1520 antioxidant and 1076 antioxidant with a weight ratio of 1:1 and stirred for 10min, a liquid polyisoprene rubber IR-2 was obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the field of liquid polyisoprene rubbers, and discloses a liquid polyisoprene rubber preparation method, which comprises: (1) in the presence of an organic lithium compound and a non-polar solvent, carrying out an initiation reaction on isoprene for 1-8 min; (2) in the presence of a blocking agent, carrying out a first polymerization reaction on the product of theinitiation reaction until the conversion rate of the isoprene is more than 70 wt%; and (3) in the presence of an accelerating agent, carrying out a second polymerization reaction on the product of thefirst polymerization reaction. The invention further provides the liquid polyisoprene rubber prepared through the preparation method. According to the present invention, with the preparation method,the performing of the polymerization reaction can be well controlled, such that the liquid polyisoprene rubber with characteristics of narrow molecular weight distribution and highly-controlled molecular weight can be prepared through the high monomer conversion rate; and especially the method can be performed in the high monomer concentration, and has the good industrial application value.

Description

technical field [0001] The invention relates to liquid polyisoprene rubber, in particular to a liquid polyisoprene rubber and a preparation method thereof. Background technique [0002] Liquid rubber is generally a viscous flowable rubber with an index average molecular weight of 500-60,000. It has the advantages of simple processing equipment and easy operation. It can be used to prepare various rubber products such as tapes, hoses, and shockproof pads. Liquid rubber is also an excellent processing aid and is widely used in the plastics industry and the electronics industry. According to different polymerized monomers, common liquid rubbers include polybutadiene rubber, polyisoprene rubber, styrene-butadiene copolymer, nitrile rubber and neoprene rubber. [0003] Liquid rubber polymerization methods mainly include free radical polymerization and anionic polymerization. At present, free radical polymerization is mainly used in China to produce liquid rubber, which has the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F136/08C08F2/40C08F4/48
Inventor 李建成刘天鹤毕海鹏赵姜维
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com