Wear-resistant wood-restructuring integrated wooden material

A technology for integrating wood and wood, applied in wood treatment, wood impregnation, wood impregnation, etc., to achieve the effects of significant economic benefits, reduced adhesive dosage, and environmental protection of products

Inactive Publication Date: 2017-12-15
龙门县品汐竹木制品有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Our country is rich in fast-growing wood resources and has a large stock volume. At present, there are still a large number of fast-growing and rich-yielding forest resources that need to be developed and utilized reasonably and efficiently.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant wood-restructuring integrated wooden material
  • Wear-resistant wood-restructuring integrated wooden material
  • Wear-resistant wood-restructuring integrated wooden material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A wear-resistant wood recombined integrated wood material, comprising at least one plate structure unit body, characterized in that: the plate structure unit body is composed of wood edge strips arranged alternately in sequence; the wood edge strips include a first wood Edge Strip, Second Timber Edge Strip, Third Timber Edge Strip.

[0043] Further, the first wood edge strip is a beech wood edge strip, and its average density is 0.55g / cm 3 .

[0044] Further, the second wood edge strip is a camphorwood wood edge strip, and its average density is 0.6g / cm 3 .

[0045] Further, the third wood edge strip is a red sandalwood wood edge strip, and its average density is 0.65g / cm 3 .

[0046] Further, the average density of the plate structural unit is 1.35g / cm 3 .

[0047] Further, the surface layer of the board structure unit body is paved in parallel with the third wood edge strips.

[0048] Further, the wood side strips of the built-in layer of the board structure un...

Embodiment 2

[0064] A wear-resistant wood recombined integrated wood material, comprising at least one plate structure unit body, characterized in that: the plate structure unit body is composed of wood edge strips arranged alternately in sequence; the wood edge strips include a first wood Edge Strip, Second Timber Edge Strip, Third Timber Edge Strip.

[0065] Further, the first wood edge strip is a beech wood edge strip, and its average density is 0.8g / cm 3 .

[0066] Further, the second wood edge strip is a camphorwood wood edge strip, and its average density is 0.8g / cm 3 .

[0067] Further, the third wood edge strip is a red sandalwood wood edge strip, and its average density is 0.85g / cm 3 .

[0068] Further, the average density of the plate structural unit is 1.85g / cm 3 .

[0069] Further, the surface layer of the board structure unit body is paved in parallel with the third wood edge strips.

[0070] Further, the wood side strips of the built-in layer of the board structure uni...

Embodiment 3

[0083] A wear-resistant wood recombined integrated wood material, comprising at least one plate structure unit body, characterized in that: the plate structure unit body is composed of wood edge strips arranged alternately in sequence; the wood edge strips include a first wood Edge Strip, Second Timber Edge Strip, Third Timber Edge Strip.

[0084] Further, the first wood edge strip is a beech wood edge strip, and its average density is 0.7g / cm 3 .

[0085] Further, the second wood edge strip is a camphorwood wood edge strip, and its average density is 0.7g / cm 3 .

[0086] Further, the third wood edge strip is a red sandalwood wood edge strip, and its average density is 0.75g / cm 3 .

[0087] Further, the average density of the structural unit body of the plate is 1.55g / cm 3 .

[0088] Further, the surface layer of the board structure unit body is paved in parallel with the third wood edge strips.

[0089] Further, the wood side strips of the built-in layer of the board s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average densityaaaaaaaaaa
Average densityaaaaaaaaaa
Average densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a wear-resistant wood-restructuring integrated wooden material. The wear-resistant wood-restructuring integrated wooden material at least comprises a board structural unit body. The wear-resistant wood-restructuring integrated wooden material is characterized in that the board structural unit body is composed of wooden edgings which are sequentially arranged in an alternating stack-up mode, and the wooden edgings comprise the first wooden edging, the second wooden edging and the third wooden edging. The woodiness feeling of a wear-resistant wood-restructuring integrated wooden material product is high, the density and the strength are high, and the decorating property is good.

Description

technical field [0001] The invention belongs to the technical field of wood processing, and in particular relates to a recombined and integrated wood material of wear-resistant wood. Background technique [0002] At present, my country's economy is developing rapidly, but the output of logs has been decreasing year by year, resulting in a growing gap between timber supply and demand. Therefore, it is imperative to find a new product to alleviate the contradiction between supply and demand. Our country is rich in fast-growing wood resources and has a large stock volume. At present, there are still a large number of fast-growing and high-yielding forest resources that need to be developed and utilized reasonably and efficiently. The recombined wood is made of low-quality fast-growing small-diameter wood and thinning wood. After grinding, it is separated into curtain-like wood bundles that are not broken in the horizontal direction, loose in the vertical direction, and inter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27D1/08B27D1/10B27K3/02B27K3/08B27K3/50B27K5/00
CPCB27D1/10B27D1/08B27K3/0214B27K3/08B27K3/50B27K5/0075
Inventor 王历文
Owner 龙门县品汐竹木制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com