Heat sink zinc-based microalloy

A micro-alloy, zinc-based technology, applied in stacked capacitors, parts of fixed capacitors, electrodes of fixed capacitors, etc., can solve the problems of inconvenient storage, transportation and production management, low density, splashing, etc.

Inactive Publication Date: 2017-11-17
绍兴市天龙锡材有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with aluminum-plated metallized films, there are two problems in metallized zinc film evaporation: (1) the zinc layer can be oxidized into ZnO in a very short time when exposed to the air, which is a semiconductor material, and The density is not high. Under the temperature and humidity conditions, the oxidation of the coating is accelerated, and the entire coating is often completely dest...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat sink zinc-based microalloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: A heat sinking zinc-based microalloy, with zinc as the matrix, adding a trace amount of calcium, the components are composed of 0.005% calcium by weight percentage, and the total amount of impurities is not more than 0.02%. The amount is zinc, and the weight percentage sum of each component is 100%.

[0016] Embodiment: 2: a kind of heat-sinking zinc-based microalloy, with zinc as matrix, add trace calcium, described each component composition is respectively calcium 0.01% by weight percentage, and the impurity that total amount is not more than 0.02%, The balance is zinc, and the weight percentage sum of each component is 100%

Embodiment 3

[0017] Embodiment 3: A heat sinking zinc-based microalloy, with zinc as the matrix, adding a trace amount of calcium, the components are composed of 0.05% calcium by weight percentage, and the total amount of impurities is not more than 0.02%. The amount is zinc, and the weight percentage sum of each component is 100%

Embodiment 4

[0018] Embodiment 4: A heat-sinking zinc-based microalloy, with zinc as the matrix, adding a small amount of calcium, the components are composed of 0.1% calcium by weight percentage, and the total amount of impurities is not more than 0.02%. The amount is zinc, and the weight percentage sum of each component is 100%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat sink zinc-based microalloy which takes zinc as a matrix and is added with trace calcium and/or tellurium. The heat sink zinc-based microalloy is prepared from the following components in percentage by weight: 0.005 to 0.2 percent of calcium, 0.001 to 0.03 percent of tellurium, less than or equal to 0.02 percent of impurities, and the balance of zinc, wherein the total weight percentage of all the components is 100 percent. When the zinc alloy disclosed by the invention is used for vacuum evaporation coating of a metal thin film, the occurrence rate of the "splashing" defect is low, and the yield is high; and furthermore, the storage time of the evaporation-coated thin film subjected to is longer than that of a conventional pure zinc evaporation-coated thin film.

Description

Technical field: [0001] The invention relates to the field of manufacturing metallized films for capacitors, and more specifically relates to a zinc-based microalloy used for forming a zinc film evaporation layer by vacuum heat sinking on a plastic film. Background technique: [0002] Metallized film capacitors are capacitors made of organic plastic film as a medium and metallized film as an electrode by winding. The organic films used in metallized film capacitors include polyester (PET), polypropylene (PP), Polycarbonate, etc., among which polyester film medium and polypropylene film medium are the most widely used. [0003] Metallized film is one of the key raw materials for manufacturing metallized film capacitors. The metal deposited on the surface of the film has been mainly aluminum for a long time. The adhesion of the aluminum-coated metallized film is relatively good, and the production process is easy to handle. Due to the chemical reaction between the surface of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C18/00H01G4/008H01G4/33
CPCC22C18/00H01G4/008H01G4/33
Inventor 戴国水宋振亚彭孜李振华沈月明
Owner 绍兴市天龙锡材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap