Non-ionic polyacrylamide as well as preparation method and application thereof
A polyacrylamide, non-ionic technology, used in the chemical industry, can solve the problems of unfavorable particle subsidence, poor flocculation effect, low molecular weight, etc., and achieve the effect of low initiator dosage, mild reaction conditions and large molecular weight
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] The present embodiment provides a kind of preparation method of nonionic polyacrylamide, it comprises the following steps:
[0028] The semi-finished product is prepared according to the mass ratio of 100:0.01, taking acrylamide monomer and photoinitiator, mixing the acrylamide monomer and deionized water to prepare an aqueous solution of acrylamide with a mass fraction of 16%; Next, the acrylamide aqueous solution and the photoinitiator were mixed evenly, and reacted for 2 hours to obtain a non-ionic polyacrylamide semi-finished product; wherein, the photoinitiator was benzaldehyde benzoin dimethyl ether;
[0029] Finished product preparation At 80-90°C, according to the mass ratio of 1000:7, add urea to the polyacrylamide semi-finished product, mix evenly, and react for 2 hours to prepare non-ionic polyacrylamide.
Embodiment 2
[0031] This example provides a method for preparing nonionic polyacrylamide. The difference between this example and Example 1 is that the photoinitiator is azodietherpropane hydrochloride.
Embodiment 3
[0033] The present embodiment provides a kind of preparation method of nonionic polyacrylamide, it comprises the following steps:
[0034] The preparation of semi-finished products takes acrylamide monomer and redox initiator according to the mass ratio of 100:0.03, mixes the acrylamide monomer and deionized water to prepare an acrylamide aqueous solution with a mass fraction of 19%; Under the conditions, the acrylamide aqueous solution and the redox initiator were mixed uniformly, and reacted for 3 hours to obtain a non-ionic polyacrylamide semi-finished product; wherein, the redox initiator included ammonium persulfate and sodium bisulfite, and the over The molar ratio of ammonium sulfate and sodium bisulfite is 1:1;
[0035] Finished product preparation At 80-90°C, according to the mass ratio of 1000:10, add urea to the polyacrylamide semi-finished product and mix evenly, and react for 2.5 hours to prepare non-ionic polyacrylamide. Polyacrylamide is successively crushed, g...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com