A technology of moxa sticker and graphene powder, which is applied in phototherapy, radiation therapy, heating/cooling reflection point instruments, etc., can solve the problem that moxa sticker cannot be recycled, waste, has no heat, magnetic effect, and is easy to damage the skin. and other problems, to achieve the effect of restoring the smoothness of the meridians, the effect is good, and the price is low.

Inactive Publication Date: 2017-09-15
青岛卓护医疗用品有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the prior art, the really effective moxibustion is mainly operated manually by people with many years of experience. The convenient and fast moxibustion sticks are mostly mechanically combined with mugwort leaves and film, which is not effective, and there is no supporting heat and magnetic action, and it is easy to Harm the skin, take effect for a short time and have poor durability. At the same time, some moxibustion stickers with high production costs cannot be recycled and cause great waste.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for making graphene moxa paste, comprising the following steps:

[0031] 1) Preparation of non-woven bag

[0032] ① Use a single-layer non-woven fabric with a mesh gap of 0.2 mm to weave into a cloth bag containing two layers of spaces, the two layers of spaces are respectively the first space and the second space;

[0033] 2) Preparation of far-infrared ceramic beads

[0034] 1. Prepare 12 parts of magnesium chloride, 28 parts of zirconium hypochlorite, 68 parts of aluminum ammonium sulfate, 58 parts of silicon tetrachloride, 72 parts of titanium tetrachloride, 2.5 parts of yttrium trichloride, 1.5 parts of aluminum trichloride by weight, Mix and stir well as an addition;

[0035] ②Calcinate 28 parts of quartz, 38 parts of feldspar, and 6 parts of talc to make clinker;

[0036] ③ by weight, 12 parts of kaolin, 2.5 parts of black tourmaline, 0.4 parts of rare earth are mixed with binder, granulated, dried, and fired into ceramsite;

[0037] ④Mix the ceramsi...

Embodiment 2

[0053]The whole is consistent with Example 1, the difference is:

[0054] A method for making graphene moxa paste, comprising the following steps:

[0055] 1) Preparation of non-woven bag

[0056] ① Use a single-layer non-woven fabric with a mesh gap of 0.1mm to weave into a cloth bag containing two layers of space, and the two layers of space are the first space and the second space;

[0057] 2) Preparation of far-infrared ceramic beads

[0058] 1. Prepare 11 parts of magnesium chloride, 25 parts of zirconium hypochlorite, 65 parts of ammonium aluminum sulfate, 55 parts of silicon tetrachloride, 70 parts of titanium tetrachloride, 2 parts of yttrium trichloride, 1 part of aluminum trichloride by weight, Mix and stir well as an addition;

[0059] ②Calcinate 25 parts of quartz, 35 parts of feldspar, and 5 parts of talc to make clinker;

[0060] ③ by weight, 10 parts of kaolin, 2 parts of black tourmaline, 0.3 parts of rare earth are mixed with binder, granulated, dried, and...

Embodiment 3

[0070] The whole is consistent with Example 1, the difference is:

[0071] 2) Preparation of far-infrared ceramic beads

[0072] 1. Prepare 13 parts of magnesium chloride, 30 parts of zirconium hypochlorite, 70 parts of ammonium aluminum sulfate, 60 parts of silicon tetrachloride, 75 parts of titanium tetrachloride, 3 parts of yttrium trichloride, 2 parts of aluminum trichloride by weight, Mix and stir well as an addition;

[0073] ②Calcinate 30 parts of quartz, 40 parts of feldspar and 8 parts of talc to make clinker;

[0074] ③ by weight, 15 parts of kaolin, 3 parts of black tourmaline, 0.5 part of rare earth are mixed with binder, granulated, dried, and fired into ceramsite;

[0075] ④ Mix and stir the ceramsite obtained in step ③, the clinker obtained in step ②, and the additive obtained in step ①, and sinter it into ceramics after 600°C for 2 hours, 850°C for 2 hours, and 1400°C for 3 hours Blank;

[0076] ⑤Mechanically crush and grind the ceramic billet into ceramic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a graphene moxibustion paste, in particular to sintering far-infrared ceramics by a special process. Graphites are used as raw materials, a fully-oxidized graphite oxide is obtained through the three stages of pre-oxidation, concentrated sulfuric acid and potassium permanganate oxidation and hydrogen peroxide final oxidation, harmless powders with a health care function are obtained through a strong reductant of vitamins C, the graphene moxibustion paste is finally obtained by being filled with old folium artemisiae argyi powders, placed for 3-5 years, with the best thermal moxibustion effect. The graphene moxibustion paste has the advantages of low cost, convenient use, long duration, remarkable effect and cyclic use.

Description

technical field [0001] The invention relates to the field of medicinal products, in particular to a method for manufacturing graphene moxa paste. Background technique [0002] Moxibustion: Moxibustion in Chinese acupuncture and moxibustion therapy. It is a natural therapy that burns moxa sticks and moxa sticks made of moxa leaves, and smokes and roasts the acupuncture points of the human body to achieve health care and cure diseases. Moxibustion originated in ancient China. Because its mechanism of action is similar to that of acupuncture and has complementary therapeutic effects with acupuncture, acupuncture and moxibustion are usually used together, so it is called acupuncture. It is a treatment method that stimulates acupuncture points or specific parts on the body surface by moxibustion materials made of moxa leaves, and adjusts the disordered physiological and biochemical functions of the human body by stimulating the activity of meridian qi, so as to achieve the purpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61H39/06A61N5/06
CPCA61H39/06A61H2201/0207A61H2201/10A61N5/0613A61N5/0625A61N2005/0645A61N2005/066
Inventor 贺虎宋建青
Owner 青岛卓护医疗用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap