Tensile strength 600MPa grade low-cost high-hole-enlargement steel plate and production method thereof

A technology of tensile strength and production method, applied in the field of metallurgy, can solve the problems of high production cost, increase of production cost, decline of steel plate surface quality, etc., and achieve the effect of increasing strength, improving structure and improving material strength

Active Publication Date: 2017-08-29
TANGSHAN IRON & STEEL GROUP +1
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the 600MPa level high-hole reaming steel produced at home and abroad mostly uses low C, adding alloy elements such as Nb, Ti, Cr, Mo, etc., and uses the comprehensive effect of solid solution strengthening and precipitation strengthening of alloy elements to improve the material strength and ensure the plasticity of the material. However, due to the addition of precious metal elements such as Nb and Mo, the production cost of the existing 600MPa grade high reaming steel is relatively high
[0004] After searching the literature of the prior art, it was found that the Chinese invention patent CN 101928881 announced a hot-rolled high-hole expansion steel plate with a tensile strength of 590MPa and its manufacturing process. This invention uses low C components and adds 0.8-1.6% of Si, 0.8-1.6% Mn, a very small amount of Nb and Ti elements can achieve tensile properties above 590MPa and high hole expansion properties, but due to the addition of Si elements, the surface quality of the steel plate will decrease and the production cost will increase.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tensile strength 600MPa grade low-cost high-hole-enlargement steel plate and production method thereof
  • Tensile strength 600MPa grade low-cost high-hole-enlargement steel plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The thickness of the low-cost high-expansion steel plate with a tensile strength of 600MPa in this example is 2.8mm, and its chemical composition and mass percentage are: C: 0.19%, Mn: 0.98%, S: 0.001%, P: 0.017%, Si: 0.13%, Als: 0.034%, Ti: 0.030%, N: 0.0025%, and the rest are iron and unavoidable impurities.

[0035] The production method includes steelmaking, heating, rolling and cooling processes, and the specific process steps are as follows:

[0036] (1) Steelmaking process: control the chemical composition and mass percentage of molten steel as follows: C: 0.19%, Mn: 0.98%, S: 0.001%, P: 0.017%, Si: 0.13%, Als: 0.034% , Ti: 0.030%, N: 0.0025%, and the rest are iron and unavoidable impurities.

[0037] (2) Heating process: the heating temperature of the slab is 1180°C.

[0038](3) Rolling process: control the starting temperature of slab rough rolling at 1090°C, the rough rolling reduction rate is 84%; the finishing rolling starting temperature is 990°C, the fin...

Embodiment 2

[0044] The thickness of the low-cost high-expansion steel plate with a tensile strength of 600MPa in this example is 3.2mm, and its chemical composition and mass percentage are: C: 0.17%, Mn: 0.95%, S: 0.002%, P: 0.015%, Si: 0.15%, Als: 0.027%, Ti: 0.028%, N: 0.0037%, and the rest are iron and unavoidable impurities.

[0045] The production method includes steelmaking, heating, rolling and cooling processes, and the specific process steps are as follows:

[0046] (1) Steelmaking process: control the chemical composition and mass percentage of molten steel as follows: C: 0.17%, Mn: 0.95%, S: 0.002%, P: 0.015%, Si: 0.15%, Als: 0.027% , Ti: 0.028%, N: 0.0037%, and the rest are iron and unavoidable impurities.

[0047] (2) Heating process: the heating temperature of the slab is 1190°C.

[0048] (3) Rolling process: control the starting temperature of slab rough rolling at 1090°C, the rough rolling reduction rate is 83%; the finishing rolling starting temperature is 1000°C, the f...

Embodiment 3

[0053] In this example, the tensile strength of 600MPa grade low-cost high-expansion steel plate is 2.0mm thick, and its chemical composition and mass percentage are: C: 0.16%, Mn: 0.80%, S: 0.002%, P: 0.018%, Si: 0.16%, Als: 0.039%, Ti: 0.015%, N: 0.0031%, and the rest are iron and unavoidable impurities.

[0054] The production method includes steelmaking, heating, rolling and cooling processes, and the specific process steps are as follows:

[0055] (1) Steelmaking process: control the chemical composition and mass percentage of molten steel as follows: C: 0.16%, Mn: 0.80%, S: 0.002%, P: 0.018%, Si: 0.16%, Als: 0.039% , Ti: 0.015%, N: 0.0031%, and the rest are iron and unavoidable impurities.

[0056] (2) Heating process: the heating temperature of the slab is 1200°C.

[0057] (3) Rolling process: control the starting temperature of the slab rough rolling at 1110°C, the rough rolling reduction rate is 84%; the finish rolling start temperature is 1010°C, the finish rolling...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a tensile strength 600MPa grade low-cost high-hole-enlargement steel plate and a production method thereof. The high-hole-enlargement steel plate is prepared from the following chemical components in percentage by mass: 0.15 to 0.20% of C, less than or equal to 0.30% of Si, 0.80 to 1.00% of Mn, less than or equal to 0.020% of P, less than or equal to 0.010% of S, 0.020 to 0.050% of Als, 0.010 to 0.030% of Ti, less than or equal to 0.0060% of N, and the balance of Fe and inevitable impurities. The production method of the steel plate comprises the processes of steelmaking, heating, rolling and cooling. The intermediate low C and conventional Mn are adopted, few amount of Si and Ti elements are added, and a cooling path is controlled, so that a hot rolled steel strip of which the tensile strength is 600 to 650MPa, the lower yield strength is 500 to 550 MPa, the elongation percentage A50 is more than or equal to 25%, and the hole enlargement rate is more than or equal to 95% is obtained, and the steel strip is low in cost, is excellent in performance and has strong market competiveness.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a steel plate with a tensile strength of 600MPa grade and low cost and high hole expansion and a production method thereof. Background technique [0002] Hot-rolled steel sheets are widely used in automobile chassis, wheels, suspensions, and body structural parts. Due to the relatively complicated hole expansion and flanging deformation in the manufacturing process of wheels, suspensions and other components, the materials are required to have high hole expansion performance. Combined with the current situation of energy conservation and emission reduction, and the gradual advancement of automobile lightweight, the 330-500MPa grade steel used in the above parts is gradually replaced by the 600MPa grade steel grade, so the 600MPa grade high reaming steel has a broad market prospect. [0003] At present, the 600MPa level high-hole reaming steel produced at home and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/14C21D8/02
CPCC21D8/0226C21D2211/002C21D2211/005C22C38/001C22C38/02C22C38/04C22C38/06C22C38/14
Inventor 武冠华马德刚田秀刚张玉文李雅琴马光宗李经哲王建兴孙宏亮
Owner TANGSHAN IRON & STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap