Steel fiber self-compacting concrete and preparation method thereof and prefabricated component

A self-compacting concrete and steel fiber technology, which is applied in the field of building materials, can solve the problems of small increase in compressive strength and no improvement, and achieve good compaction, reduce wear and increase degrees of freedom.

Active Publication Date: 2017-08-11
苏州港松建材有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Although the steel fiber self-compacting concrete in the prior art can solve the crack resistance and tensile properties, from another perspective, the compressive strength of the steel fiber self-compacting concrete has little or no improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel fiber self-compacting concrete and preparation method thereof and prefabricated component
  • Steel fiber self-compacting concrete and preparation method thereof and prefabricated component

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~16

[0101] (1) Prepare raw materials:

[0102] Magnetic beads: iron oxide body after strong magnetic treatment, the particle size is 2~5mm.

[0103] Cement: P O42.5 ordinary Portland cement, apparent density is 3.10g / cm 3 .

[0104] Fly ash: Class I fly ash, apparent density 2.04g / cm 3 .

[0105] Sand: medium sand with a fineness modulus of 2.36 and an apparent density of 2.65g / cm 3 , bulk density is 1.45g / cm 3 , with a moisture content of 0.4%.

[0106] Natural Coarse Aggregate: Crushed stone with continuous particle size of 5~20mm, the apparent density is 2.75g / cm 3 , bulk density is 1.35g / cm 3 , The water absorption rate is 0.45%.

[0107] Short steel fiber: diameter is 0.06cm, length is 0.6~1.8cm, the shape can be straight steel fiber (a), prismatic steel fiber (b), corrugated steel fiber (c), hook steel fiber ( d / e), large head-shaped steel fibers (f), double-pointed steel fibers (g), bundled steel fibers (h), etc., were purchased from the market.

[0108] Non-metal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Apparent densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a steel fiber self-compacting concrete, wherein the water-binder ratio of the concrete is controlled to be 0.3-0.7. The concrete is prepared from, by weight, 1-5 parts of 3-20 mm short steel fiber, 0.5-3 parts of magnetic beads, 1-4 parts of non-metallic fiber, 23-27 parts of natural coarse aggregate, 20-22.5 parts of sand, 10-14 parts of cement, 1.5-3.5 parts of fly ash, 4-8 parts of water, and 0.001-0.160 part of water reducing agent. The obtained high performance self-compacting concrete not only has simple production processes, but also can meet requirements on compressive strength and tensile performance.

Description

technical field [0001] The present application relates to the technical field of building materials, especially the technical field of novel self-compacting concrete, and specifically relates to a steel fiber self-compacting concrete and a preparation method and application of the steel fiber self-compacting concrete. Background technique [0002] Self-compacting concrete (Self-Consolidating Concrete referred to as SCC) refers to the concrete that can flow and compact under its own gravity, and can completely fill the formwork even if there are dense steel bars, and at the same time obtain good homogeneity and do not require additional vibration. The preparation of self-compacting concrete is generally through the selection and matching of admixtures, cementing materials, coarse and fine aggregates, and a reasonable mix ratio design, so that the yield stress of the concrete is reduced enough to be overcome by the shear stress due to its own weight, and the fluidity of the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B28/08C04B14/30C04B14/48C04B14/42C04B14/46C04B20/00
CPCC04B14/308C04B20/0052C04B28/04C04B28/08C04B18/08C04B14/06C04B14/02C04B24/24C04B22/002C04B20/0016C04B14/48C04B14/42C04B14/46C04B14/4625
Inventor 马剑潘荣楠蔡梦帆石辉陈天明王欢
Owner 苏州港松建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products