Preparation for modified MIL-53(Fe) metal organic framework and method for treating organic wastewater with activated persulfate thereof

A metal-organic framework and organic wastewater technology, applied in chemical instruments and methods, oxidized water/sewage treatment, water/sewage treatment, etc., can solve the problem of easy deactivation of catalysts, insufficient active center sites, and reaction cycle Long and other problems, to achieve the effect of strong catalyst recyclability, easy operation, and improved degradation efficiency

Active Publication Date: 2017-07-18
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the technical problems of insufficient active center sites, poor dispersion, long reaction cycle, easy deactivation of the catalyst and poor recyclability when the traditional iron catalyst catalyzes the activation of PS, and provides a modified MIL-53 (Fe ) Preparation of Metal Organic Framework and Method for Activating Persulfate to Treat Organic Wastewater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation for modified MIL-53(Fe) metal organic framework and method for treating organic wastewater with activated persulfate thereof
  • Preparation for modified MIL-53(Fe) metal organic framework and method for treating organic wastewater with activated persulfate thereof
  • Preparation for modified MIL-53(Fe) metal organic framework and method for treating organic wastewater with activated persulfate thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The preparation of modified MIL-53(Fe) metal-organic framework and its catalytic activation of persulfate to treat golden orange G simulated wastewater, the specific operation steps are as follows:

[0037] (1) Preparation Method 1 of Modified MIL-53(Fe) Metal Organic Framework: Weigh 0.995g (5mmol) FeCl 2 4H 2 O and 0.831g (5mmol) 1,4-BDC were poured into 25mL DMF and stirred for 20min to mix well. Pour the mixed solution into a 100mL polytetrafluoroethylene-lined reaction kettle, and place it in an electric thermostat blast drying oven preheated to 150°C. After 5 hours, the reactor was taken out and cooled to room temperature naturally. Separate the solid from the liquid by filtration or centrifugation, and wash the solid with methanol and then deionized water. Finally, the above solid was dried in an oven at 65° C. to obtain the modified MIL-53(Fe) metal-organic framework.

[0038] (2) Preparation method 2 of modified MIL-53(Fe) metal-organic framework: the diffe...

Embodiment 2

[0049] The material prepared under the conditions of the preparation method 1 of the modified MIL-53(Fe) metal organic framework in Example 1 is used as a catalyst, and sodium persulfate is used as an oxidant to simulate the initial COD of Jincheng G wastewater Cr 120mg / L, set four treatment groups, respectively: (1) add 1.0g / L modified MIL-53 (Fe) metal organic framework - 7.6g / L sodium persulfate - Jincheng G wastewater; (2) Add 1.0g / L modified MIL-53(Fe) metal organic framework—Golden Orange G wastewater; (3) Add 7.6g / L sodium persulfate—Golden Orange G wastewater; (4) Add 1.0g / L unmodified MIL-53(Fe)—7.6g / L Sodium Persulfate—Golden Orange G Wastewater. Take four 250mL Erlenmeyer flasks as reaction flasks, add the solutions set by the above three treatment groups to the reaction flasks respectively, and fully stir the reaction at 25°C, and take samples at 20min, 40min, 60min, 90min and 120min respectively Determination of wastewater COD Cr , the results are shown in Table...

Embodiment 3

[0054] Use a 250mL Erlenmeyer flask as a reaction flask to prepare COD Cr The golden orange G (OG) dye waste water that is 120mg / L, with the preparation method 1 of modified MIL-53 (Fe) metal-organic framework among the embodiment 1 as the material that the condition prepares is catalyst, and sodium persulfate is oxidizing agent, does not adjust Wastewater pH, set up five treatment groups: after adding 7.6g / L sodium persulfate, add catalyst 0.1g / L (treatment group 1), 0.3g / L (treatment group 2), 0.5g catalyst respectively to five groups of reaction flasks / L (Treatment Group 3), 1.0g / L (Treatment Group 4), 1.5g / L (Treatment Group 5), fully stirred at 25°C for reaction, and samples were taken at 20min, 40min, 60min, 90min and 150min respectively And measure the wastewater COD Cr , the results are shown in Table 3.

[0055] table 3

[0056]

[0057]

[0058] The results in Table 3 show that the amount of modified MIL-53 (Fe) metal-organic framework has a certain effect ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation for a modified MIL-53(Fe) metal organic framework and a method for treating organic wastewater with activated persulfate thereof. Compared with unmodified MIL-53(Fe), the modified MIL-53(Fe) metal organic framework compounded according to the invention contains more ferrous reactive metal centers. The modified MIL-53(Fe) metal organic framework used as a catalytic active site can enhance the effective contact between the metal organic framework material and the persulfate so as to generate free radicals of sulfate with strong oxidizing property, so that the refractory pollutants in wastewater can be effectively removed. The modified MIL-53(Fe) metal organic framework has higher material stability, can maintain the stability of the crystal structure after the catalytic activation reaction of persulfate and can still maintain higher catalytic activity after repeated cyclic utilization. The method for treating organic wastewater according to the invention has the advantages of environmental protection, simple and convenient operation, low cost, high catalyst activity, high reusability, and the like. Besides, the method is also suitable for the treatment of various organic wastewaters.

Description

technical field [0001] The invention belongs to the technical field of water pollution control, and in particular relates to the preparation of a modified MIL-53 (Fe) metal organic framework and a method for treating organic wastewater by activating persulfate. Background technique [0002] In recent years, the use of activated persulfate (PS, persulfate) to generate sulfate radicals (SO 4 - ·) Advanced Oxidation Technologies (AOTs) to treat refractory organic wastewater is a research hotspot in the field of wastewater treatment technology. Compared with the traditional Fenton method, PS oxidation technology does not need to produce SO under acidic conditions of 3-5 4 - ·To realize the effective degradation of pollutants. And SO 4 - The standard oxidation-reduction potential (E 0 =+2.5~+3.1v) Compared with the hydroxyl radical (OH·)(E 0 =+1.9~+2.7v) high, longer stability and half-life (about 4s), lower reactivity with background organic matter naturally present in w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G83/00C02F1/72C02F101/30
CPCC02F1/725C02F2101/30C08G83/008Y02P20/582
Inventor 马邕文万金泉王艳濮梦婕王九妹
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com