Environment-friendly single-component silylated polyether sealant for vehicle and preparation method thereof

A technology of silane polyether and silane-modified polyether, which is applied in the field of environment-friendly single-component silane polyether sealant for vehicles and its preparation, can solve the problems of inability to meet the needs of high-end vehicles, inappropriate formula ratios, and environmental protection. The performance cannot be achieved and other problems, and the production process method is simple, the practicability is strong, and the decoration performance is excellent.

Inactive Publication Date: 2017-06-13
河南瑞朗达新材料有限公司
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the improper formula ratio of traditional MS sealant, its environmental protection performance does not meet the EU TVOC standard limit (TVOC standard, that is, total volatile organic compounds ≤ 50μgC / g), and cannot meet the needs of high-end vehicles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly single-component silylated polyether sealant for vehicle and preparation method thereof
  • Environment-friendly single-component silylated polyether sealant for vehicle and preparation method thereof
  • Environment-friendly single-component silylated polyether sealant for vehicle and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054]Prepare the environment-friendly single-component silane polyether sealant for vehicles with the following formula and process:

[0055] Weigh 500g of nano-active calcium carbonate, 100g of heavy calcium carbonate, 500g of light calcium carbonate, 50g of fumed silica, 50g of titanium dioxide, 10g of 1010 type anti-aging agent, 4g of N-220 white carbon black, and 4g of Tinuvin326 type ultraviolet absorber Put 10g of agent, Tinuvin770 light stabilizer and 10g of heat stabilizer together into a double planetary mixer, heat to 120°C, under the protection of dry inert gas, mix for dehydration pretreatment, stir slowly (25-50rPm) for 120 minutes; add S303H silane Modified polyether resin 1000g, DIDP plasticizer (diisodecyl phthalate) 150g, vacuumize and heat to 110°C, stir at high speed (1000rPm) for 150 minutes, cool down to 40°C, add A-171 silane 30g of dehydrating agent, stir slowly (250rpm) for 25 minutes, add 20g of silane coupling agent phenyltrimethoxysilane, stir slowl...

Embodiment 2

[0059] Prepare the environment-friendly single-component silane polyether sealant for vehicles with the following formula and process:

[0060] Weigh 300g of nano-active calcium carbonate, 100g of heavy calcium carbonate, 300g of light calcium carbonate, 100g of iron red, 10g of 1010 type anti-aging agent, 100g of N-220 white carbon black, 20g of Tinuvin326 type ultraviolet absorber, and 20g of Tinuvin770 type light stabilizer Add 20g of Tinunvin-68 heat stabilizer and 20g of Tinunvin-68 heat stabilizer together in a double planetary mixer, heat to 80°C, stir slowly (25-50rPm) for 120 minutes, add 200g of S203H silane-modified polyether resin, S303H silane-modified polyether Resin 800g, DIDP plasticizer 300g, vacuumize and heat to 120°C, high-speed stirring (1000rPm) for 150 minutes, cool down to 30°C, add A-171 silane water remover 30g, slowly stir (250rPm) for 25 minutes, add Silane coupling agent phenyltrimethoxysilane 20g, stir slowly (250rpm) for 25 minutes, add 60g of γ-...

Embodiment 3

[0064] Prepare the environment-friendly single-component silane polyether sealant for vehicles with the following formula and process:

[0065] Weigh 1200g of nano-active calcium carbonate, 50g of titanium dioxide, 10g of 1010 type anti-aging agent, 4g of N-220 white carbon black, 10g of Tinuvin326 type ultraviolet absorber, 10g of Tinuvin770 type light stabilizer, and 10g of heat stabilizer and put them into a double planetary mixer , heated to 110°C, stirred slowly (25-50rPm) for 120 minutes; added 200g of S203H silane-modified polyether resin, 800g of S303H silane-modified polyether resin, 170g of DIDP plasticizer, vacuumed and heated to 110 ℃, high-speed stirring (1000rPm) for 150 minutes, cooling down to 40 ℃, adding 25g of VTMO type silane dewatering agent, stirring slowly (250rPm) for 25 minutes, adding 25g of silane coupling agent phenyltrimethoxysilane, stirring slowly (250rpm) After 25 minutes, add 50g of N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane adhesion crossl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly single-component silylated polyether sealant for a vehicle and a preparation method thereof and belongs to the technical field of sealants or adhesives. The sealant is prepared from the following components in parts by weight: 100 parts of silane modified polyether resin, 5-40 parts of a plasticizer, 50-150 parts of a filler, 0.1-15 parts of a reinforcing agent, 0.1-15 parts of a colorant, 0.5-10 parts of a water removal agent, 0.1-8 parts of an adhesive force cross-linking agent, 0.1-3 parts of a heat stabilizer, 0.1-3 parts of an anti-ultraviolet absorbent, 0.1-3 parts of a hindered amine light stabilizer, 0.1-3 parts of an antioxidant, 0.2-10 parts of a silane coupling agent and 0.2-8.0 parts of a catalyst. The sealant has extremely low TVOC content and accords with the European Union TVOC standard, that is to say, the total volatile organic compound is less than or equal to 50mugC / g; and the environment-friendly single-component silylated polyether sealant can be widely applied to the fields of automobile vehicles, rail transit, aerospace, ships and warships and architecture decoration.

Description

technical field [0001] The invention belongs to the technical field of sealant, and in particular relates to an environment-friendly single-component silane polyether sealant for vehicles and a preparation method thereof. Background technique [0002] At present, the sealants widely used in the market mainly include polysulfide sealants, silicone sealants and polyurethane sealants. Polysulfide sealants, silicone sealants and polyurethane sealants still have a large market in China. Among them, polysulfide adhesives are declining in the market due to their slow curing speed at low temperature, easy aging and hardening, poor weather resistance, and strong irritating odor; polyurethane sealants are weak in strength, tearing, puncture, and The erosion performance is very good, but because of its isocyanate end group, the storage stability is harsh, and the CO released after curing 2 The gas is easy to make the adhesive layer form bubbles, the slow complete curing speed and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J171/00C09J11/06C09J11/04
CPCC09J171/00C08K3/26C08K3/36C08K5/5419C08K13/02C08K2003/265C08K2201/014C08L2205/025C09J11/04C09J11/06C08L71/00C08K5/544
Inventor 亢建华冯巧亢鹏程王宗胜亢延超
Owner 河南瑞朗达新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com