An anti-green and primer technology, applied in the field of coatings, can solve the problems of insignificant effect, discoloration of paint film, poor anti-greening and so on

Active Publication Date: 2018-09-28
江苏赛鑫树脂有限公司 +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing PE primers all need to use organic cobalt as a reaction accelerator. After a period of time, the divalent cobalt ions existing in the molecules are oxidized to trivalent cobalt ions, resulting in discoloration of the paint film.
Existing technology only replaces the accelerator but the effect is not obvious
[0004] In response to this situation, we have developed a PE primer resin with excellent anti-greening properties to be used in PE wood furniture paints, which can change the shortcomings of traditional PE resins to make PE primers with poor anti-greening properties, and can better meet the needs of furniture companies.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1: 29 parts of maleic anhydride, 25 parts of dicyclopentadiene, 18 parts of diethylene glycol, and 22 parts of styrene. Heat up to 90-120°C with nitrogen gas and start stirring, keep warm for 1-2 hours, then raise the temperature to 190-200°C at a rate of 20°C / h, stop heating and cool down to room temperature to make resin;

[0019] Prepared by mixing 70 parts of resin, 3 parts of styrene, 0.4 parts of dispersant, 1 part of anti-settling agent, 20 parts of talcum powder, 5 parts of zinc stearate, 0.3 parts of defoamer, and 0.3 parts of leveling agent, stirring and dispersing at room temperature for 2 hours Primer;

[0020] Mix the primer: cobalt isooctanoate: methyl ethyl ketone peroxide: thinner=100:1.1:1.2:35. Spray on the template.

Embodiment 2

[0021] Example two: 29 parts of maleic anhydride, 25 parts of dicyclopentadiene, 18 parts of diethylene glycol, and 22 parts of styrene. Heat up to 90-120°C with nitrogen gas and start stirring, keep warm for 1-2 hours, then raise the temperature to 190-200°C at a rate of 20°C / h, stop heating and cool down to room temperature to make resin;

[0022] 70 parts of resin, 3 parts of styrene, 0.5 parts of dibutyltin dilaurate, 0.4 parts of dispersant, 1 part of anti-settling agent, 20 parts of talcum powder, 5 parts of zinc stearate, 0.3 parts of defoamer, leveling agent 0.3 parts are stirred and dispersed at room temperature for 2 hours to make a primer;

[0023] Mix the primer: cobalt isooctanoate: methyl ethyl ketone peroxide: thinner=100:1.1:1.2:35. Spray on the template.

Embodiment 3

[0024] Example three: 29 parts of maleic anhydride, 25 parts of dicyclopentadiene, 18 parts of diethylene glycol, and 22 parts of styrene. Heat up to 90-120°C with nitrogen gas and start stirring, keep warm for 1-2 hours, then raise the temperature to 190-200°C at a rate of 20°C / h, stop heating and cool down to room temperature to make resin;

[0025] 70 parts of resin, 3 parts of styrene, 0.5 parts of dibutyltin dilaurate, 0.4 parts of dispersant, 1 part of anti-settling agent, 20 parts of talcum powder, 5 parts of zinc stearate, 0.3 parts of defoamer, leveling agent 0.3 parts are stirred and dispersed at room temperature for 2 hours to make a primer;

[0026] Mix the primer: cobalt isooctanoate: methyl ethyl ketone peroxide: thinner=100:1.4:1.6:35. Spray on the template.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of paint, and provides an anti-greening PE (polyethylene) primer and a preparation method thereof. The PE anti-greening primer provided by the invention comprises the following components in parts by weight: 70 parts of resin, 3 parts of styrene, 0.5 part of anti-greening modifier, 0.4 part of dispersing agent, 1 part of anti-settling agent, 20 parts of talcum powder, 5 parts of zinc stearate, 0.3 part of defoaming agent and 0.3 part of leveling agent. Compared with the prior art, the PE primer provided by the invention has a favorable film coating effect and excellent anti-greening performance and can be widely used for furniture painting.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an anti-greening PE primer. Background technique [0002] The curing reaction of unsaturated polyester is a free radical copolymerization reaction. During the curing reaction, an initiator (white water) and an accelerator (blue water) need to be added. Through the redox reaction, the cobalt salt in the accelerator decomposes the initiator to produce high Active free radicals, free radicals attack the unsaturated double bonds in the polyester molecular chain and the cross-linking monomer styrene to activate them, so that a cross-linking reaction occurs, and the polyester forms an excellent paint film with a three-dimensional network structure. In order to improve the sandability, it is generally necessary to increase the amount of blue water and white water to shorten the construction time and improve production efficiency, which will turn the paint film color green and affect the appearan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/06C09D7/61C09D7/63C09D7/62C08G63/676
CPCC08G63/676C08K3/24C08K3/34C08K5/098C08K5/14C08K5/57C08K9/10C08K13/02C08K13/06C08K2201/014C09D7/61C09D7/62C09D7/63C09D167/06
Inventor 路旭东张小平
Owner 江苏赛鑫树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap