High-performance compound color paste for pultrusion process and preparation method thereof

A pultrusion molding, high-performance technology, applied in the direction of pigment paste, etc., can solve the problems of complex color paste toner agglomeration, floating color, precipitation, etc., and achieves small color difference between batches, bright color, and compatibility. Good results

Active Publication Date: 2020-12-11
CHANGZHOU ZHONGJIE COMPOSITES
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to the difference between two or more toners, there are phenomena such as toner agglomeration, precipitation and skinning in the complex color paste, and the phenomenon of floating color and blooming often occurs when it is used in pultrusion molding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1）

[0021] The pultrusion process of the present embodiment is made of the following components by weight for the high-performance complex color paste:

[0022] Dioctyl phthalate (DOP) 100 parts.

[0023] 100 parts of toner: 90 parts of Y35 chrome yellow from Changzhou Yale Color Trading Co., Ltd. and 10 parts of R706 titanium dioxide from DuPont.

[0024] 2 parts of wetting and dispersing agent: 1 part of BYK-9076 produced by German BYK Chemical Co., Ltd. and 1 part of Liou 7967 produced by Wuxi Liou Chemical Materials Co., Ltd.

[0025] 2 copies of Liou 7904 produced by Wuxi Liou Chemical Materials Co., Ltd.

[0026] 0.5 parts of methyl ethyl ketone oxime.

[0027] The preparation method of the high-performance complex color color paste for the pultrusion process of the present embodiment is as follows:

[0028] ① Stir 90 parts of dioctyl phthalate and 1.8 parts of wetting and dispersing agent evenly, then add 90 parts of Y35 chrome yellow, stir at 600rpm for 12 minutes, and ...

Embodiment 2～ Embodiment 5）

[0032] Each embodiment is basically the same as Embodiment 1, and the differences are shown in Table 1.

[0033] Table 1

[0034] Example 1 Example 2 Example 3 Example 4 Example 5 carrier resin 100 DOPs 50 DOPs 500 DOPs 100 DBPs 100 DIDPs Toner 90 parts of Y35 chrome yellow + 10 parts of R706 titanium dioxide 1 part of Cabot M100 carbon black + 99 parts of R706 titanium dioxide 50 parts of phthalocyanine green GFP+50 parts of R706 titanium dioxide 25 parts of Cabot M100 carbon black + 75 parts of R706 titanium dioxide 40 parts of phthalocyanine blue BGS+60 parts of R706 titanium dioxide Wetting and dispersing agent 1 copy of BYK-9076 and 1 copy of Leo 7967 1 copy of BYK-9076 and 1 copy of Leo 7967 5 copies of BYK-9076 and 10 copies of Leo 7967 5 copies of BYK-9076 and 15 copies of Leo 7967 5 copies of BYK-9076 and 5 copies of Leo 7967 Leo 7904 2 copies 1 copy 4 parts 9 servings 4 parts Methyl eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-performance compound-color color paste for a pultrusion technology and a preparation method thereof. The compound-color color paste is prepared from the following components in parts by weight: 100 parts of toner, 10 to 1000 parts of carrier resin, 1 to 50 parts of wetting dispersant, 0.5 to 20 parts of functional agent A and 0.1 to 10 parts of functional agent B. The preparation method comprises the steps of respectively mixing two kinds or more than two kinds of toner with the carrier resin and the wetting dispersant and evenly stirring; then respectively pouring into a three-roller grinding machine to be ground until required fineness is achieved and obtaining single-color color paste; mixing all the single-color color paste, then adding the functional agent A and the functional agent B, evenly stirring and matching color until chromatic aberration meets a requirement. The compound-color color paste disclosed by the invention has good evenness and good resin compatibility, has no skinning, solidification, sedimentation or toner agglomeration in a storage process, has no surface dyeing dim phenomenon in a pultrusion process and can meet related requirements of the pultrusion technology.

Description

technical field [0001] The invention relates to a high-performance multiple-color color paste for pultrusion molding technology and a preparation method thereof. Background technique [0002] The pultrusion molding process is to form and solidify continuous glass fiber bundles, belts or cloth impregnated with resin glue containing color paste, under the action of traction, through extrusion dies, and continuously produce FRP profiles of unlimited length. This process is most suitable for the production of FRP profiles of various cross-sectional shapes, such as rods, tubes, solid profiles (I-shaped, trough-shaped, square profiles) and hollow profiles (door and window profiles, blades, etc.). [0003] Requirements for the color paste used in the pultrusion process: 1. High temperature resistance: the temperature resistance of the color paste is ≥180°C; 2. High toner content and strong tinting power; 3. Small color difference between batches △E≤0.5, for dark color paste There ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D17/00
CPCC09D17/003C09D17/004C09D17/005C09D17/008
Inventor 孙全收史建军
Owner CHANGZHOU ZHONGJIE COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap