Preparation method of neodymium-iron-boron magnet applicable to new energy automobile

A new energy vehicle, NdFeB technology, applied in the direction of magnetic objects, inductor/transformer/magnet manufacturing, magnetic materials, etc., can solve the problems of high production cost and unsatisfactory performance, and achieve the effect of improving performance

Inactive Publication Date: 2017-05-31
ZHEJIANG ZHONGKE MAGNETIC IND
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the motor field of new energy vehicles, the performance requirements of NdFeB magnet products are relatively high, and the performance of existing magnetic powder and NdFeB magnet products cannot be met, and the production cost is very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The invention relates to the field of magnetic steel production, in particular to a method for preparing an NdFeB magnet suitable for new energy vehicles.

[0023] In order to solve the above technical problems, the present invention provides a method for preparing an NdFeB magnet suitable for new energy vehicles, which is characterized in that it comprises the following steps:

[0024] (1) Weigh 28.25% of praseodymium and neodymium metal, 2.75% of dysprosium, 0.98% of boron, 0.3% of niobium, 0.6% of aluminum, 2% of cobalt, 0.2% of copper, 0.25% of terbium, 0.2% of gallium, and 64.47% of pure iron Mix evenly; Mix evenly; After experimental testing, the ratio of materials is mixed according to the above, and the obtained product has better performance. The ratio of the various materials will directly affect the magnetic performance parameters of the final product.

[0025] (2) Add the material obtained in step (1) into a vacuum induction belt furnace, and in a vacuum st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of magnetic steel production, and particularly relates to a preparation method of neodymium-iron-boron magnet applicable to new energy automobiles. The method comprises the steps that raw materials of 28.25% of praseodymium neodymium metals, 2.75% of dysprosium, 0.98% of boron, 0.3% of niobium, 0.6% of aluminum, 2% of cobalt, 0.2% of copper, 0.25% of terbium, 0.2% of gallium, and 64.47% of pure iron are weighed according to the weight proportions and are mixed evenly, and after the processes of fusion in a vacuum induction swing furnace, copper wheel cooling, reaction in a hydrogen quenching reactor, oxidizing agent adding, stirring, and grinding, the magnetic powder is obtained; then models are made for the magnetic powder according to the sizes of the products, and in an environment of complete seal and low oxygen, after the pressing with a high magnetic field pressing machine, and under a high intensity pressure of 20 Mpa, crude products with densities of 4.4-4.8 g / cm<3> are made; the crude products are put into a vacuum sintering furnace, under a vacuum condition, the crude products are heat preserved under a high temperature of 1020-1045 DEG C for 5 hours and under an intermediate temperature of 850-950 DEG C for 3 hours and under a low temperature of 500-560 DEG C for 5 hours, and the neodymium-iron-boron magnet products are obtained.

Description

technical field [0001] The invention relates to the field of magnetic steel production, in particular to a method for preparing an NdFeB magnet suitable for new energy vehicles. Background technique [0002] In the motor field of new energy vehicles, the performance requirements of NdFeB magnet products are relatively high, and the performance of existing magnetic powder and NdFeB magnet products cannot be met, and the production cost is very high. Contents of the invention [0003] The main technical problem to be solved by the present invention is to provide a method for preparing NdFeB magnets suitable for new energy vehicles, using self-made magnetic powder to manufacture NdFeB magnet products, thereby improving the performance of NdFeB magnet products and reducing production cost. [0004] A method for preparing an NdFeB magnet suitable for new energy vehicles, characterized in that it comprises the following steps: [0005] (1) Weigh 28.25% of praseodymium and neod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/057H01F41/02B22F9/04B22F3/02B22F3/10
CPCH01F1/0576B22F3/02B22F3/10B22F9/04H01F1/0577H01F41/0266
Inventor 吴中平吴爱军梁海斌
Owner ZHEJIANG ZHONGKE MAGNETIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com