Integrated wallboard with heat retaining and decorative structure made of wasted red bricks and preparation method thereof

A technology of structural insulation and red bricks, which is applied in building components, building structures, buildings, etc., can solve the problem that red brick waste cannot be reused, achieve good feasibility and industrialization prospects, light weight, sound insulation and heat preservation effect Good results

Inactive Publication Date: 2017-05-31
HEBEI INSTITUTE OF ARCHITECTURE AND CIVIL ENGINEERING
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an integrated wall panel for thermal insulation and decoration using waste red brick structure and its manufacturing method, so as to solve the technical problem that the red brick waste left over from the demolition of the existing red brick masonry structure cannot be effectively reused

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Integrated wallboard with heat retaining and decorative structure made of wasted red bricks and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The integrated wall panel for thermal insulation and decoration using the waste red brick structure includes:

[0052] A recycled aggregate structure layer 1 with a thickness of 80mm, a polystyrene board with a thickness of 40mm as an insulation layer 2, a mortar protection layer 3 with a thickness of 50mm, and a decorative layer 4 of discarded red bricks with a thickness of 10mm.

[0053] The parts by weight of each component of the above-mentioned recycled aggregate structure layer are as follows:

[0054] 1.65 parts of waste red brick coarse aggregate;

[0055] Waste red brick fine aggregate 0.95 parts;

[0056] 1 part of cement;

[0057] 0.38 parts of water.

[0058] The waste red brick fine aggregate is composed of waste red brick powder and tailings sand, and the mixing weight ratio of the two is 1:2.

[0059] Embodiment 1 The production method of this kind of integrated wall panel using waste red brick structure heat preservation and decoration, the productio...

Embodiment 2

[0072] The integrated wall panel for thermal insulation and decoration using the waste red brick structure includes:

[0073] A recycled aggregate structure layer 1 with a thickness of 120mm, a polystyrene board with a thickness of 60mm as an insulation layer 2, a mortar protection layer 3 with a thickness of 50mm, and a decorative layer 4 of discarded red bricks with a thickness of 20mm.

[0074] The parts by weight of each component of the above-mentioned recycled aggregate structure layer are as follows:

[0075] 2.05 parts of waste red brick coarse aggregate;

[0076] 1.05 parts of waste red brick fine aggregate;

[0077] 1 part of cement;

[0078] 0.4 parts of water.

[0079] The waste red brick fine aggregate is composed of waste red brick powder and tailings sand, and the mixing weight ratio of the two is 1:3.

[0080] Embodiment 2 The method of making the integrated wallboard for thermal insulation and decoration using the waste red brick structure is the same as t...

Embodiment 3

[0082] The integrated wall panel for thermal insulation and decoration using the waste red brick structure includes:

[0083] Recycled aggregate structure layer 1 with a thickness of 100mm, polystyrene board with a thickness of 50mm as insulation layer 2, mortar protection layer 3 with a thickness of 50mm, and decorative layer 4 of discarded red bricks with a thickness of 10mm.

[0084] The parts by weight of each component of the above-mentioned recycled aggregate structure layer are as follows:

[0085] 2.55 parts of waste red brick coarse aggregate;

[0086] 1.55 parts of waste red brick fine aggregate;

[0087] 1 part of cement;

[0088] 0.45 parts of water.

[0089] The waste red brick fine aggregate is composed of waste red brick powder and tailings sand, and the mixing weight ratio of the two is 1:2.5.

[0090] Embodiment 3 The method of making the integrated wallboard for thermal insulation and decoration using the waste red brick structure is the same as that of E...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an integrated wallboard with a heat retaining and decorative structure made of wasted red bricks and a preparation method thereof. The integrated wallboard comprises a recycled aggregate structure layer, a heat retaining layer, a mortar protection layer and a wasted red brick decorative layer, wherein the mixture of the recycled aggregate structure layer comprises wasted red brick coarse aggregate, wasted red brick fine aggregate, cement and water, and the wasted red brick decorative layer is formed by splicing wasted red brick slices. The mixture comprises the following components in parts by weight: 1.65-2.55 parts of wasted red brick coarse aggregate, 0.95-1.15 parts of wasted red brick fine aggregate, 1 part of cement and 0.38-0.45 part of water. Through the combination of the wasted red bricks and a fabricated low-rise building in a village, the invention provides the integrated wallboard with the heat retaining and decorative structure made of the wasted red bricks and the preparation method thereof. The integrated wallboard is mainly used for a fabricated residential structure in the village, and achieves the purposes of simple production process, low production cost, energy conservation and waste utilization.

Description

technical field [0001] The invention relates to a building component, in particular to a structural heat preservation and decoration integrated exterior wall board made of discarded red bricks and a manufacturing method thereof. Background technique [0002] With the demolition and reconstruction of cities and towns at this stage, a large number of old red brick masonry houses are facing demolition, resulting in a large amount of red brick waste. Although there is a method for making concrete by using waste red bricks, the amount of red bricks is relatively small, which cannot solve the problem of reusing a large amount of red bricks. Therefore, there is an urgent need for a method to solve a large amount of red brick waste, to realize the rational utilization of materials, to achieve the purpose of turning waste into treasure, energy conservation and environmental protection, in line with today's construction industry policies. Contents of the invention [0003] The purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/288E04F13/075C04B28/00
CPCE04C2/288C04B28/00E04F13/0862E04F13/0875E04F2290/04C04B18/16
Inventor 蔡焕琴李雪娜麻建锁周苗苗王丽楠刘永伟
Owner HEBEI INSTITUTE OF ARCHITECTURE AND CIVIL ENGINEERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More