A kind of method for preparing al0.5cocrfeni high entropy alloy

A high-entropy alloy and intermediate alloy technology, applied in the field of preparation of high-entropy alloy materials, can solve the problems of inability to prepare large-volume high-entropy alloys, and achieve the effects of similar grain size, guaranteed composition uniformity, and accurate composition

Active Publication Date: 2018-07-17
NORTHWESTERN POLYTECHNICAL UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiency in the prior art that cannot prepare large-volume high-entropy alloys, the present invention proposes a method for preparing large-volume Al 0.5 CoCrFeNi High Entropy Alloy Method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing al0.5cocrfeni high entropy alloy
  • A kind of method for preparing al0.5cocrfeni high entropy alloy
  • A kind of method for preparing al0.5cocrfeni high entropy alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This embodiment is a kind of FeCoCr and Ni that adopt master alloy 2 Al as raw material to prepare Al 0.5 CoCrFeNi high-entropy alloy method, the Al 0.5 The atomic molar ratio of CoCrFeNi high-entropy alloy is Al 0.5 CoCrFeNi.

[0031] The specific implementation steps are as follows:

[0032] Step 1, surface treatment: for FeCoCr and Ni 2 Al surface grinding treatment. Specifically, bulk FeCoCr with a purity of 99.9wt.% and bulk Ni with a purity of 99.9wt.% 2 Al surface is polished clean. The polished FeCoCr and Ni 2 Al is placed in the acetone solution and ultrasonically cleaned for 10 minutes and then placed in a drying oven to dry, so that the FeCoCr and Ni 2 The surface of Al exhibits metallic luster. According to the prepared Al 0.5 The atomic molar ratio of CoCrFeNi high-entropy alloy is determined by the FeCoCr and Ni 2 The mass ratio of Al is 2.3105:1. Weigh FeCoCr and Ni 2 Al. In the present embodiment, the FeCoCr that weighs is 12kg, Ni 2 Al is...

Embodiment 2

[0042] This embodiment is a method for preparing bulk Al 0.5 The method of CoCrFeNi high-entropy alloy, concrete implementation steps are as follows:

[0043] Step 1, surface treatment: for FeCoCr and Ni 2 Al surface grinding treatment. Specifically, bulk FeCoCr with a purity of 99.9wt.% and bulk Ni with a purity of 99.9wt.% 2 Al surface is polished clean. The polished FeCoCr and Ni 2 Al is placed in the acetone solution and ultrasonically cleaned for 20min and then placed in a drying oven to dry, so that the FeCoCr and Ni 2 The surface of Al exhibits metallic luster. According to the prepared Al 0.5 The atomic molar ratio of CoCrFeNi high-entropy alloy is determined by the FeCoCr and Ni 2 The mass ratio of Al is 2.3105:1. Weigh FeCoCr and Ni 2 Al. In the present embodiment, the FeCoCr that weighs is 15kg, Ni 2 Al is 6.492kg.

[0044] Step 2, furnace body preheating: add any FeCoCr or Ni into the crucible of the vacuum induction melting furnace 2 Al as a preheater...

Embodiment 3

[0053] This embodiment is a method for preparing bulk Al 0.5 The method of CoCrFeNi high-entropy alloy, concrete implementation steps are as follows:

[0054] Step 1, surface treatment: for FeCoCr and Ni 2 Al surface grinding treatment. Specifically, bulk FeCoCr with a purity of 99.9wt.% and bulk Ni with a purity of 99.9wt.% 2 Al surface is polished clean. The polished FeCoCr and Ni 2 Al is placed in the acetone solution and ultrasonically cleaned for 15 minutes and then placed in a drying oven to dry, so that the FeCoCr and Ni 2 The surface of Al exhibits metallic luster. According to the prepared Al 0.5 The atomic molar ratio of CoCrFeNi high-entropy alloy is determined by the FeCoCr and Ni 2 The mass ratio of Al is 2.3105:1. Weigh FeCoCr and Ni 2 Al. In the present embodiment, the FeCoCr that weighs is 12kg, Ni 2 Al is 5.194kg.

[0055] Step 2, furnace body preheating: add any FeCoCr or Ni into the crucible of the vacuum induction melting furnace 2 Al as a preh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an Al0.5CoCrFeNi high-entropy alloy. An intermediate alloy serves as a raw material, and volatilization of a low-melting-point element Al in the smelting process is greatly reduced. Meanwhile, a vacuum induction heating device is adopted, the electromagnetic stirring effect of the induction heating device is utilized, and therefore the component uniformity of a cast ingot is guaranteed. According to the method, the melting point difference between the lowest-melting-point metal Al and the highest-melting-point metal Cr is indirectly reduced, the problem of excessive volatilization of the low-melting-point Al simple substance in the smelting process is solved, and the component uniformity of the multi-element high-entropy alloy is guaranteed through the electromagnetic stirring effect existing in induction heating. Through reasonable designing of the atmosphere, the air pressure, the die preheating temperature, the smelting temperature, the heat preservation time, the casting speed and other parameters in the smelting process, a large Al0.5CoCrFeNi high-entropy alloy cast ingot is successfully prepared.

Description

technical field [0001] The invention belongs to the field of preparation of high-entropy alloy materials, in particular to a method for preparing large-volume Al alloys using induction heating equipment and intermediate alloy raw materials. 0.5 CoCrFeNi high-entropy alloy method. Background technique [0002] High-entropy alloys have attracted the attention of many researchers for their unique alloy design concept and excellent performance. The high mixing entropy makes the high-entropy alloys solidify into simple solid solution structures such as face-centered cubic (FCC) and body-centered cubic (BCC). The unique structure makes high-entropy alloys have excellent properties in many aspects and have broad application prospects. For example, the high-entropy alloy solid solution structure has good thermal stability and strength at high temperatures, which makes it expected to be applied in the fields of aero-engines, ship engines, and key metal parts of ultra-supercritical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/00C22C1/03
CPCC22C1/03C22C30/00
Inventor 李金山郭桐寇宏超王毅唐斌其他发明人请求不公开姓名
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com