A kind of energy-saving and environment-friendly building foam cement

A foaming cement and foaming agent technology, applied in the field of energy saving, can solve the problems of poor toughness and high water absorption, achieve high toughness, good waterproof performance, and reduce pollutant emissions

Active Publication Date: 2019-04-09
承德喜上喜水泥有限责任公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current foamed cement generally has problems such as high water absorption and poor toughness, which limit its wide application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An energy-saving and environment-friendly building foam cement, which is composed of the following raw materials in mass percentage: 30% of cement, 5% of nickel-iron slag powder, 2% of expanded vermiculite, 2% of mica powder, 0.5% of waterproofing agent, foaming agent 1.5%, multifunctional bio-viscosity regulator 0.01, modified brown silk 1%, polycarboxylate superplasticizer 1%, and the balance is water.

[0031] The cement is P·O4 2.5 grade cement.

[0032] The ferronickel slag powder is the waste discharged from the refining of nickel metal or the smelting process of ferronickel alloy, and it is ground to a specific surface area of ​​400m 2 / kg-500m 2 / kg obtained.

[0033] The expanded vermiculite is crushed from non-metallic mineral vermiculite after high-temperature calcination, and the fineness is 80-100 mesh.

[0034] The mica powder has a fineness of 60 mesh to 120 mesh.

[0035] The waterproofing agent is composed of magnesium stearate and methyltriethoxysi...

Embodiment 2

[0040] An energy-saving and environment-friendly building foam cement, which is composed of the following raw materials in mass percentage: 35% of cement, 8% of nickel-iron slag powder, 8% of expanded vermiculite, 5% of mica powder, 1.2% of waterproofing agent, foaming agent 2.5%, multifunctional bio-viscosity regulator 0.05%, modified brown silk 2%, polycarboxylate superplasticizer 2%, and the balance is water.

[0041] The cement is P·O4 2.5 grade cement.

[0042] The ferronickel slag powder is the waste discharged from the refining of nickel metal or the smelting process of ferronickel alloy, and it is ground to a specific surface area of ​​400m 2 / kg-500m 2 / kg obtained.

[0043] The expanded vermiculite is crushed from non-metallic mineral vermiculite after high-temperature calcination, and the fineness is 80-100 mesh.

[0044] The mica powder has a fineness of 60 mesh to 120 mesh.

[0045] The waterproofing agent is composed of magnesium stearate and methyltriethoxys...

Embodiment 3

[0050] An energy-saving and environment-friendly building foam cement, which is composed of the following raw materials in mass percentage: 32% of cement, 6% of nickel-iron slag powder, 5% of expanded vermiculite, 4% of mica powder, 1% of waterproofing agent, foaming agent 2%, multifunctional biological viscosity regulator 0.03%, modified brown silk 1.6%, polycarboxylate superplasticizer 1.4%, and the balance is water.

[0051] The cement is P·O4 2.5 grade cement.

[0052] The ferronickel slag powder is ground to a specific surface area of ​​400m2 by refining metallic nickel or the waste discharged during the smelting process of ferronickel alloy 2 / kg-500m 2 / kg obtained.

[0053] The expanded vermiculite is crushed from non-metallic mineral vermiculite after high-temperature calcination, and the fineness is 80-100 mesh.

[0054] The mica powder has a fineness of 60 mesh to 120 mesh.

[0055] The waterproofing agent is composed of magnesium stearate and methyltriethoxysil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of energy saving, and discloses an energy-saving environment-friendly building foam cement which is composed of the following substances in percentage by mass: 30-35% of cement, 5-8% of ferronickel slag powder, 2-8% of expanded vermiculite, 2-5% of mica powder, 0.5-1.2% of waterproofing agent, 1.5-2.5% of foaming agent, 0.01-0.05% of multifunctional biological viscosity modifier, 1-2% of modified coir fiber, 1-2% of polycarboxylic acid water reducing agent and the balance of water. The foam cement has the characteristics of favorable waterproofness, high toughness, heat insulation, energy saving and the like, and is green and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of energy saving. Background technique [0002] The energy-saving technology of building wall structure is one of the important directions of building energy-saving research in all countries in the world. The development of high-performance building wall structure insulation materials, products and systems is the key to realizing building energy conservation. Guobanfa [2013] No. 1 Document "Green Building Action Plan" requires: "Accelerate the development of building insulation systems and materials with good fire and heat insulation performance. Foamed cement is a new generation of green and environmentally friendly new non-toxic insulation materials. It has the advantages of light weight, good thermal insulation performance, excellent fire resistance, and good environmental protection. It is widely used in wall insulation, floor heating insulation, roof insulation and other related projects. However, prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B38/02C04B111/27
CPCC04B28/04C04B2111/27C04B2201/32C04B14/20C04B14/202C04B18/144C04B2103/302C04B16/02C04B24/085C04B24/42C04B24/38C04B22/068C04B24/123C04B38/02
Inventor 管祥玲
Owner 承德喜上喜水泥有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap