A kind of preparation method of nanoscale ultrafine analcime

Anallite and nano-scale technology, applied in the field of molecular sieve synthesis, can solve the problems of large alkali consumption, serious pollution, large particle size and the like, and achieve the effect of low cost

Active Publication Date: 2018-10-12
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The analcite crystal grains obtained by this method can reach nanoscale, but the particle size is still relatively large, and when fly ash is used as raw material, the pretreatment process needs to consume a large amount of alkali, the corrosion and pollution are serious, and the entire preparation process is also relatively cumbersome.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of nanoscale ultrafine analcime
  • A kind of preparation method of nanoscale ultrafine analcime

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] At room temperature, mix water, sodium hydroxide, silica sol, and N-methylpyrrolidine according to a certain ratio, then heat in sealed water at 90°C for 24 hours, cool to room temperature, and then add the spare sodium metaaluminate powder to the above solution in, and stir well. The final material ratio satisfies: Al 2 o 3 / SiO 2 =30, N-Methylpyrrolidine / SiO 2 =0.15,OH - / SiO 2 =0.75,H 2 O / SiO 2 =40. Afterwards, the above mixture was ultrasonically (1.0 KW / L) and magnetically stirred at 40°C for 3 hours, and then placed in a reaction kettle for crystallization at 175°C for 120 hours. The obtained product was washed with distilled water, dried at 120°C, and then calcined at 550°C for 5 hours. It is confirmed to be analcime by XRD detection, observed by scanning electron microscope, it is spherical shape, the grain size is about 30nm, belongs to the nanoscale range, and the specific surface area is 270m 2 / g.

Embodiment 2

[0037] At room temperature, mix water, sodium hydroxide, silica sol, and N-methylpyrrolidine according to a certain ratio, then heat in airtight water at 100°C for 24 hours, cool to room temperature, and then add the spare sodium metaaluminate powder to the above solution in, and stir well. The final material ratio satisfies: Al 2 o 3 / SiO 2 =40, N-Methylpyrrolidine / SiO 2 =0.20,OH - / SiO 2 =0.8,H 2 O / SiO 2 =60. Afterwards, the above mixture was ultrasonically stirred (0.5 KW / L) at 60°C for 3 hours, and then placed in a reaction kettle for crystallization at 180°C for 140 hours. The obtained product was washed with distilled water, dried at 120°C, and then calcined at 550°C for 5 hours. The product was confirmed to be analcime by XRD detection, observed by scanning electron microscope, it was spherical shape, the grain size was about 35nm, belonging to the nanoscale range, and the specific surface area was 212m 2 / g.

Embodiment 3

[0039]At room temperature, mix water, sodium hydroxide, silica sol, and N-methylpyrrolidine according to a certain ratio, then heat in sealed water at 120°C for 6 hours, cool to room temperature, and then add aluminum isopropoxide powder to the above solution, and stir well. The final material ratio satisfies: Al 2 o 3 / SiO 2 =60, N-Methylpyrrolidine / SiO 2 =0.25,OH - / SiO 2 =0.9,H 2 O / SiO 2 =80. Afterwards, the above mixture was ultrasonically (2.0 KW / L) and magnetically stirred at 50°C for 3 hours, and then placed in a reactor for crystallization at 180°C for 140 hours. The obtained product was washed with distilled water, dried at 120°C, and then calcined at 550°C for 5 hours. The product was confirmed to be analcime by XRD detection, observed by scanning electron microscope, it was in spherical shape, the grain size was about 18nm, it belonged to ultra-fine nanometer range, and the specific surface area was 380m 2 / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a nano-scale ultra-fine analcime preparation method, wherein an alkali source, a silicon source, an aluminum source, water and N-methylpyrrolidine are adopted as reaction raw materials and crystallization is performed for 5-200 h under autogenous pressure and 140-200 DEG C hydrothermal condition to obtain the small grain nanometer analcime. According to the present invention, the obtained nano-scale ultra-fine analcime has characteristics of simple process, pure crystal phase, high crystallinity, large specific surface, low cost and the like, and has wide application prospects in ion adsorption and purification.

Description

technical field [0001] The invention relates to a preparation method of nano-scale ultrafine analcime, which belongs to the technical field of molecular sieve synthesis. Background technique [0002] Analcime has a unique internal structure and crystal chemical properties, and has special properties in catalysis, adsorption, ion exchange, etc. As one of the zeolite minerals, analcime has a very broad field of development and utilization, and has a large potential market value. However, the natural analcite mineral has the disadvantages of high impurity content, difficult purification, and large crystal grains. The artificially synthesized analcite perfect crystal is more universal and controllable. [0003] (Journal of the American Chemical Society 2007, 129, 13305-13312) reported the preparation of cubic tetragonal trioctahedral analcite crystals by hydrothermal method. In the preparation process of this method, a surfactant needs to be added, the raw materials are expens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/02B82Y30/00
Inventor 杨卫亚凌凤香王少军沈智奇季洪海王丽华郭长友
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com