Waterborne polyurethane coating and preparation process

A water-based polyurethane and coating technology, applied in antifouling/underwater coatings, fire-retardant coatings, coatings, etc., can solve problems such as fire, save energy, improve flame retardant performance, and achieve good flame retardant effect.

Inactive Publication Date: 2017-05-10
ENG EQUIP CO LTD SUZHOU SAI SIDE
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a new type of environmentally friendly material, water-based polyurethane has been widely used in textiles, printing and dyeing, leather processing, wood processing and architectural coatings. However, the materials involved in these fields are basically flammable materials, and there are potential fire hazards. risk, so it is necessary to carry out flame retardant treatment before using these materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Present embodiment provides a kind of waterborne polyurethane coating, and this coating comprises the following components by mass parts:

[0042] Modified waterborne polyurethane: 40 parts, intumescent flame retardant system: 25 parts, flame retardant synergist: 10 parts, water: 20 parts, filler: 20 parts, dispersant: 1 part, defoamer: 0.5 parts, thickening Agent: 0.5 parts, curing agent: 2 parts, anti-mildew fungicide: 0.5 parts, film-forming aid: 3 parts, penetrating agent: 0.5 parts;

[0043] The dispersant is sodium hexametaphosphate; the defoamer is tributyl phosphate; the thickener is hydroxymethyl cellulose; the curing agent is diethylenetriamine; 3-ketone; film-forming aid ethylene glycol butyl ether; penetrating agent is penetrating agent JFC; filler is calcium carbonate;

[0044] The intumescent flame retardant system includes the following components in parts by mass: ammonium polyphosphate: 20 parts, melamine: 10 parts, pentaerythritol: 5 parts;

[0045] ...

Embodiment 2

[0063] Present embodiment provides a kind of waterborne polyurethane coating, and this coating comprises the following components by mass parts:

[0064] Modified waterborne polyurethane: 45 parts, intumescent flame retardant system: 30 parts, flame retardant synergist: 15 parts, water: 25 parts, filler: 30 parts, dispersant: 1-2 parts, defoamer: 1.5 parts, Thickener: 1 part, curing agent: 3 parts, anti-mildew fungicide: 1 part, film-forming aid: 5 parts, penetrating agent: 1.5 parts;

[0065] The dispersant is sodium hexametaphosphate; the defoamer is tributyl phosphate; the thickener is polyacrylamide; the curing agent is phenolic modified amine; Ketone; film-forming aid ethylene glycol butyl ether; penetrant is penetrant JFC; filler is bentonite;

[0066] The intumescent flame retardant system includes the following components in parts by mass: ammonium polyphosphate: 30 parts, melamine: 15 parts, pentaerythritol: 10 parts;

[0067] The flame retardant synergist is a mixt...

Embodiment 3

[0085] Present embodiment provides a kind of waterborne polyurethane coating, and this coating comprises the following components by mass parts:

[0086] Modified waterborne polyurethane: 43 parts, intumescent flame retardant system: 28 parts, flame retardant synergist: 12 parts, water: 23 parts, filler: 23 parts, dispersant: 1 part, defoamer: 0.8 parts, thickening Agent: 0.8 parts, curing agent: 2 parts, anti-mold fungicide: 0.9 parts, film-forming aid: 4 parts, penetrating agent: 0.8 parts;

[0087] The dispersant is sodium hexametaphosphate; the defoamer is tributyl phosphate; the thickener is polyacrylamide; the curing agent is diaminodiphenylmethyl sulfone DDS; Lin-3-ketone; film-forming aid ethylene glycol butyl ether; penetrating agent is penetrating agent JFC; filler is talcum powder;

[0088] The intumescent flame retardant system includes the following components in parts by mass: ammonium polyphosphate: 25 parts, melamine: 13 parts, pentaerythritol: 8 parts;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses waterborne polyurethane coating and a preparation process thereof. The waterborne polyurethane coating is prepared from modified waterborne polyurethane, an expansive fire-retardant system, a flame retardant synergist, water, filler, a dispersing agent, an antifoaming agent, a thickening agent, a curing agent, a mildew-proof bactericide, a coalescing agent and a penetrating agent. The preparation process is simple, feasible and low in preparation cost, and the coating prepared according to the method is great in flame retardation effect, nontoxic and free of environment pollution.

Description

technical field [0001] The invention belongs to the field of paint preparation, in particular to a water-based polyurethane paint and a preparation method thereof. Background technique [0002] As a new type of environmentally friendly material, water-based polyurethane has been widely used in textiles, printing and dyeing, leather processing, wood processing and architectural coatings. However, the materials involved in these fields are basically flammable materials, and there are potential fire hazards. Therefore, it is necessary to carry out flame retardant treatment before using these materials. For the purpose of protecting people's lives and properties and reducing fire risks, it is necessary to develop new environmentally friendly flame-retardant materials and apply them in actual production and life. [0003] As a common green and environmentally friendly textile finishing agent, water-based polyurethane coating agent is a high-molecular organic material and also a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D5/18C09D5/14C09D7/12C08G18/75C08G18/66C08G18/48C08G18/34C08G18/32C08G18/12
CPCC09D175/08C08G18/12C08G18/6692C08G18/755C08L2201/02C09D5/14C09D5/185C09D7/61C09D7/63
Inventor 顾建强钱燕华
Owner ENG EQUIP CO LTD SUZHOU SAI SIDE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products