Rubber sealing ring used for GIS composite apparatus and production method thereof

A technology of rubber sealing rings and combined electrical appliances, applied in the field of rubber materials, can solve problems such as low compression permanent deformation, and achieve the effects of long service life, long vulcanization time and uniform vulcanization

Inactive Publication Date: 2017-05-10
SHANDONG ELECTRIC POWER ENG CONSULTING INST CORP +1
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to meet the sealing performance requirements of GIS combined electrical appliances for long-term operation, aiming at the problem of compression set index that affects long-term sealing performance, to provide a rubber sealing ring for GIS combined electrical appliances and its preparation method, low compression set It can withstand the corrosion of HF that may be produced by the arc decomposition product of GIS insulating gas——SF6 gas

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber sealing ring used for GIS composite apparatus and production method thereof
  • Rubber sealing ring used for GIS composite apparatus and production method thereof
  • Rubber sealing ring used for GIS composite apparatus and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The rubber sealing ring for GIS combined electrical appliances is made of the following raw materials by weight: 100 parts of EPDM rubber; 5 parts of zinc oxide; 1 part of stearic acid; 25 parts of high wear-resistant carbon black; 30 parts of spray carbon black 6 parts of dioctyl sebacate; 1 part of antioxidant MB; 2.5 parts of vulcanizing agent BIPB.

[0023] The preparation method comprises the following steps:

[0024] (1) Weighing and batching according to the above ratio, and then put the weighed EPDM raw rubber into the internal mixer for 5 minutes to make the raw rubber obtain sufficient fluidity;

[0025] (2) Add zinc oxide, stearic acid, carbon black and other raw materials except vulcanizing agent to the above plasticized raw rubber, and continue banburying for 10 minutes to ensure that various raw materials are mixed evenly;

[0026] (3) Take out the mixed rubber material from the internal mixer, put it into the open mixer and pass it 5 times, so that the r...

Embodiment 2

[0029] The rubber sealing ring for GIS combined electrical appliances is made of the following raw materials by weight: 100 parts of EPDM rubber; 5 parts of zinc oxide; 1 part of stearic acid; 20 parts of high wear-resistant carbon black; 30 parts of spray carbon black ; 8 parts of dioctyl sebacate; 0.5 parts of antioxidant MB; 2.5 parts of vulcanizing agent BIPB.

[0030] The preparation method comprises the following steps:

[0031] (1) Weighing and batching according to the above ratio, and then put the weighed EPDM raw rubber into the mixer for 3 minutes to make the raw rubber obtain sufficient fluidity;

[0032] (2) Add zinc oxide, stearic acid, carbon black and other raw materials except vulcanizing agent to the above-mentioned plasticized raw rubber, and continue banburying for 5 minutes to ensure that various raw materials are mixed evenly;

[0033] (3) Take out the mixed rubber material from the internal mixer, put it into the open mixer and pass it through for 3 tim...

Embodiment 3

[0036] A rubber sealing ring for GIS combined electrical appliances, made of the following raw materials in parts by weight: 100 parts of EPDM rubber; 3 parts of zinc oxide; 2 parts of stearic acid; 20 parts of high wear-resistant carbon black; spray carbon black 30 parts; 8 parts of dioctyl sebacate; 1 part of antioxidant MB; 2 parts of vulcanizing agent BIPB.

[0037] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a rubber sealing ring used for a GIS composite apparatus and a preparation method thereof. The rubber sealing ring is produced by steps of plasticating, banburying and mixing on the following raw materials in parts by weight: 100 parts of ethylene-propylene-diene monomer, 3-5 parts of zinc oxide, 1-2 parts of stearic acid, 20-25 parts of high-wear resistant carbon black, 30-35 parts of spray carbon black, 6-8 parts of dioctyl sebacate, 0.5-1 part of an antioxidant MB, and 2-3 parts of a vulcanizing agent BIPB. The product has extremely low permanent compression set value, the actual measurement value is 10%, which is lower than the requirement of less than or equal to 25% in JB / T7052-1993, longer life is guaranteed; the brittleness is abnormal at the temperature of -60 DEG C, so that the usage performance and life of the product at low temperature are guaranteed; the product is tolerable 40% of hydrofluoric acid for 48 hours and the performance has no change; and the aged life assessment of the sealing ring can reach as high as 55.6 years.

Description

technical field [0001] The invention relates to the distribution of an O-shaped rubber sealing ring for a GIS combined electrical appliance, belonging to the technical field of rubber materials. Background technique [0002] The live parts of GIS combined electrical appliances are all sealed in SF6 gas. The existing combined electrical appliances are basically sealed with O-shaped rubber sealing rings, so the sealing performance of the sealing rings is very important for the operation of the high-voltage switch of combined electrical appliances. In order to ensure the stability of the power system, the power system requires less maintenance or even maintenance-free for various switches. Today, the design life of combined electrical appliances is required to be maintenance-free for more than 30 years, which puts forward the long-term life of the O-shaped rubber seal ring that plays the main sealing role higher requirements. Contents of the invention [0003] The purpose of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08K13/02C08K3/22C08K5/09C08K3/04C08K5/12C08K5/37C08K5/14
CPCC08K3/04C08K3/22C08K5/09C08K5/12C08K5/14C08K5/37C08K13/02C08K2003/2296C08K2201/014C08L23/16C08L2203/20
Inventor 邹振宇黄萍杨勇李颖瑾汪江浩张光明李秀芝于玉铭王军飞曲娟娟
Owner SHANDONG ELECTRIC POWER ENG CONSULTING INST CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com