A kind of continuous oxygen bleaching refining agent and preparation method thereof

A technology of surfactant and rare earth catalyst, which is applied in the fields of plant fiber, fiber treatment, textiles and papermaking, etc., can solve the problems of large amount of refining agent and NaOH, unsatisfactory removal effect of cottonseed hulls, high COD value of discharged wastewater, etc., to achieve reduction The amount of NaOH, the strong damage is small, and the effect of reducing the COD value

Active Publication Date: 2018-12-18
SHANGHAI ARGUS NEW MATERIAL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the development of refining agents mainly focuses on biological enzyme refining agents and non-biological alkali-resistant refining agents. The key technology of the former lies in the selection and application of scouring enzymes, and the key technology of the latter lies in the selection and application of surfactants. Base (benzene) sodium sulfonate, fatty alcohol polyoxyethylene ether and other series of surfactants, the former is ecological and environmentally friendly, and the refining effect is not good, while the latter is excellent in refining effect, but not environmentally friendly
Such as the Chinese patent CN 102154230 A, the invention relates to the application of a scouring enzyme in the pretreatment of textiles, which is energy-saving and environmentally friendly, but the removal effect on cottonseed hulls is not ideal, and a good refining effect cannot be achieved; another example is the Chinese patent CN 104532556 A, introduced a high alkali-resistant textile refining agent and its preparation method, using sodium alkylsulfonate, fatty alcohol polyoxyethylene ether series surfactants, excellent removal effect on natural impurities and cottonseed hulls, but refining The amount of solvent and NaOH is large, reaching 10 g / L and 30 g / L respectively, resulting in a high COD value of discharged wastewater, which is not conducive to environmental protection
[0004] To sum up, there is currently no scouring agent that is suitable for short-process new processes, satisfies the scouring and bleaching effect and is more environmentally friendly. Therefore, it is of great practical significance to develop a continuous oxygen bleaching scouring agent that meets the above requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of continuous oxygen bleaching refining agent and preparation method thereof
  • A kind of continuous oxygen bleaching refining agent and preparation method thereof
  • A kind of continuous oxygen bleaching refining agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] In a more preferred embodiment, the preparation method of continuous oxygen bleaching refining agent of the present invention comprises the following steps:

[0025] 1) 5-10wt% hydrogen peroxide stabilizer, 2-5wt% biodegradable surfactant, 18-25wt% Jimmy surfactant, 2-4wt% hyperbranched surfactant and 50-70wt% deionized water Add to the reaction kettle, stir at 40-60°C for 10-20 minutes;

[0026] 2) Add 2-8wt% rare earth catalyst to the mixture formed in step 1), raise the temperature to 50-70°C, and continue stirring for 1-2 hours;

[0027] 3) cooling to room temperature to obtain the continuous oxygen bleaching refining agent.

[0028] The continuous oxygen bleaching refining agent prepared by the invention is highly efficient and environmentally friendly, and the process has wide applicability. The amount of NaOH is reduced by about 40% compared with conventional refining agents, and the COD value of discharged wastewater is reduced by more than 40%. The whiteness, ...

Embodiment 1

[0046]Add lignosulfonate (Wuhan Fengzhulin Chemical Technology Co., Ltd., weight-average molecular weight 2900) 2.1 grams, polycarboxylic acid (Hubei Xinkang Pharmaceutical Chemical Co., Ltd., weight-average molecular weight 3150) 2.0 grams, polyhydroxyacrylic acid in the four-necked flask Sodium (Jinjinle (Hunan) Chemical Co., Ltd., weight average molecular weight 3100) 2.3 grams, Sapindus saponin (Hunan Langlin Biological Products Co., Ltd.) 2.8 grams, N,N'-dilauroyl ethylenediamine diethylsulfonic acid Sodium 21g, AAS-HBP 2g and deionized water 65g, stir at 45°C for 15 minutes, add Tb 0.5 Eu 0.5 (TTA) 3 4.3 grams of Phen, heated up to 55°C, continued to stir for 1.5 hours, and cooled to room temperature to obtain the continuous oxygen bleaching refining agent 1, with a solid content of 36.2%.

Embodiment 2

[0048] Add lignosulfonate (Wuhan Fengzhulin Chemical Technology Co., Ltd., weight-average molecular weight 4200) 2.0 grams, polycarboxylic acid (Hubei Xinkang Pharmaceutical Chemical Co., Ltd., weight-average molecular weight 3950) 1.9 grams, polyhydroxyacrylic acid in the four-necked flask Sodium (Jinjinle (Hunan) Chemical Co., Ltd., weight average molecular weight 4100) 2.2 grams, the average degree of polymerization is 1.2 C 12 Starch glucoside (purchased from Lanzhou University of Technology) 3 grams, N,N'-difatty acyl ethylenediamine dipropionate 22 grams, (formula I), SHBP 2.3 grams and deionized water 63 grams, stirred at 40 ° C for 15 min, add Pr 2 (BA) 6 (Phen) 2 4.8 grams, heated up to 55°C, continued to stir for 1.5 hours, and cooled to room temperature to obtain the continuous oxygen bleaching refining agent 2, with a solid content of 35.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
gross effectaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a continuous oxygen bleaching refining agent and a preparation method thereof. The continuous oxygen bleaching refining agent comprises a rare-earth catalyst, a hydrogen peroxide stabilizer, biodegradable surfactant, Gemini surfactant, hyperbranched surfactant and water. Compared with a conventional refining agent, the continuous oxygen bleaching refining agent has the advantages that the continuous oxygen bleaching refining agent is efficient and environmental friendly and wide in process applicability, the NaOH use amount is lowered by about 40%, the COD value of discharged wastewater is lowered by more than 40%, and the whiteness, capillary effect and breaking strength of fabric treated by the continuous oxygen bleaching refining agent are evidently better.

Description

technical field [0001] The invention relates to a pretreatment auxiliary agent for printing and dyeing and a preparation method thereof, in particular to a continuous oxygen bleaching refining agent and a preparation method thereof. Background technique [0002] Cotton fabrics are favored by consumers for their moisture absorption and air permeability, but cotton fibers contain many natural impurities, which make cotton fabrics yellow in color and poor in water absorption. Therefore, cotton fabrics must be refined for the main purpose of removing natural impurities and bleached for the main purpose of removing natural pigments. The appearance, feel and dyeing performance of the refined and bleached cotton fabrics can be significantly improved, and the wearing performance can be improved. The segmented continuous steaming, scouring and bleaching process used in the conventional scouring and bleaching of cotton fabrics has a long route, high energy consumption, and large sewag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/50D06M11/38D06M15/01D06M15/263D06M13/188D06M13/342D06M15/11D06M13/467D06M13/50D06M13/402D06M15/53D06M13/256D06L4/13D06L4/12D06M101/06
CPCD06M11/38D06M11/50D06M13/188D06M13/256D06M13/342D06M13/402D06M13/467D06M13/50D06M15/01D06M15/11D06M15/263D06M15/53D06M2101/06
Inventor 党婉蓉李正雄
Owner SHANGHAI ARGUS NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com