Special antioxidant for manufacturing of copper wire

An anti-oxidant and copper wire technology, applied in the coating process of metal materials, etc., can solve the problems of reduced anti-oxidation effect and easy damage of anti-oxidation film, and achieve the effect of not being easily damaged

Active Publication Date: 2017-04-26
南通德晋昌光电科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the copper wire production process, the anti-oxidation film formed on the surface of the copper wire is easily damaged during the stranding or extrusion process, resulting in a decrease in the anti-oxidation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A special antioxidant for copper wire production, comprising the following components in mass percentage:

[0015] Benzotriazole 6%, ethylene glycol 35%, polyether modified polysiloxane sulfate sodium salt 5%, sodium lauryl sulfate 4.5%, deionized water to 100%.

Embodiment 2

[0017] A special antioxidant for copper wire production, comprising the following components in mass percentage:

[0018] Benzotriazole 6%, ethylene glycol 38%, polyether modified polysiloxane sulfate sodium salt 5%, sodium lauryl sulfate 5%, β-mercaptobenzothiazole 4%, hexame Add 5% sodium phosphate, 5% phosphite, and deionized water to 100%.

Embodiment 3

[0020] A special antioxidant for copper wire production, comprising the following components in mass percentage:

[0021] Benzotriazole 7%, ethylene glycol 40%, polyoxyethylene alkylphenol ether 6%, sodium lauryl sulfate 5%, β-mercaptobenzothiazole 3%, sodium hexametaphosphate 2%, Phosphite 3%, deionized water added to 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An antioxidant for cooling a copper wire comprises the following components in percentages by mass: 6-7% of benzotriazole, 35-40% of glycol, 5-6% of a wetting agent, 4-5% of a surfactant, and deionized water to 100%, and preferably comprises the following components in percentages by mass: 3-4% of beta-mercaptobenzothiazole, 2-5% of sodium hexametaphosphate and 3-5% of phosphite. By the antioxidant, a compact antioxidative protecting film can be formed on the copper wire, and the oxidation resistance of the copper wire is improved effectively, so that the copper wire has long quality guarantee period and low oxygen content. The antioxidant is simple and reasonable in proportioning, low in cost and suitable for industrial application.

Description

technical field [0001] The invention relates to the production field of copper wires, in particular to a special antioxidant for making copper wires. Background technique [0002] In the process of manufacturing copper wire, affected by high temperature, copper wire is easy to react with oxygen, which generally shortens the service life. Especially when it is used as a wire, a layer of oxide film will be formed at the joint and will not conduct electricity. In severe cases, the resistance of the wire will increase and it will easily cause a fire. [0003] Benzotriazole is mostly used as a vapor phase corrosion inhibitor in the production of copper and copper alloys. It has excellent performance, almost no odor, and is non-toxic. However, in the copper wire production process, the anti-oxidation film formed on the surface of the copper wire is easily destroyed during the stranding or extrusion process, resulting in a decrease in the anti-oxidation effect. Contents of the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23F11/10C23C22/68
CPCC23C22/68C23F11/10
Inventor 王俞民
Owner 南通德晋昌光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products