Spraying type ceramic surface-sintered silver paste and preparation method thereof

A technology of ceramic surface and silver paste, applied in the field of ceramic surface processing, can solve problems such as harmful effects on the environment and people's health, and achieve the effects of not easily falling off, avoiding falling off, and simple preparation process

Active Publication Date: 2017-03-22
河北银瓷天成文化传播有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the commonly used process is to disperse silver powder in organic solvent, apply it on the ceramic surface, and then sinter to make silver adhere. In this process, the organic solvent will produce a large amount of VOC during the sintering process, which will cause harmful effects on the environment and people's health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A spray-coated ceramic surface sintered silver paste, which comprises the following components in parts by weight: 50 parts of nano-silver powder, 1 part of glass powder, 8 parts of Tween, 10 parts of polyvinylpyrrolidone, 8 parts of simethicone, sweet almond 5 parts of oil, 15 parts of water.

[0018] Wherein the particle size of the nano-silver powder is 50-250 nanometers.

[0019] The preparation method of the glass powder is as follows: Weigh the raw materials according to the following mass percentage: SiO 2 35%, Al 2 o 3 35%, CaO12%, NaO5%, BaO10%, B 2 o 3 2.8%, Er 2 o 3 0.2%, mix evenly, melt at 1200-1400°C for 2 hours to obtain molten glass, quench the molten glass with water, dry and mill in a ball mill for 12 hours, and obtain glass powder after drying.

[0020] The preparation method of the spray-coated ceramic surface sintered silver paste is as follows: add water into a container, add polyvinylpyrrolidone and stir until dissolved, then add Tween, sim...

Embodiment 2

[0022] A spray-coated ceramic surface sintered silver paste, which includes the following components in parts by weight: 55 parts of nano-silver powder, 2 parts of glass powder, 5 parts of Tween, 8 parts of polyvinylpyrrolidone, 10 parts of simethicone, sweet almond 3 parts of oil, 18 parts of water.

[0023] Wherein the particle size of the nano-silver powder is 50-250 nanometers.

[0024] The preparation method of the glass powder is as follows: Weigh the raw materials according to the following mass percentage: SiO 2 45%, Al 2 o 3 25%, CaO12%, NaO5.99%, BaO10%, B 2 o 3 2%, Er 2 o 3 0.01%, mix evenly, melt at 1200-1400°C for 3 hours to obtain molten glass, quench the molten glass with water, dry and mill in a ball mill for 12 hours, and obtain glass powder after drying.

[0025] The preparation method of the spray-coated ceramic surface sintered silver paste is as follows: add water into a container, add polyvinylpyrrolidone and stir until dissolved, then add Tween, s...

Embodiment 3

[0027] A spray-coated ceramic surface sintered silver paste, which comprises the following components in parts by weight: 60 parts of nano-silver powder, 3 parts of glass powder, 10 parts of Tween, 5 parts of polyvinylpyrrolidone, 5 parts of simethicone, sweet almond 4 parts of oil, 20 parts of water.

[0028] Wherein the particle size of the nano-silver powder is 50-250 nanometers.

[0029] The preparation method of the glass powder is: take the raw material according to the following mass percentage: SiO 2 35%, Al 2 o 3 25%, CaO15%, NaO10%, BaO10%, B 2 o 3 4.9%, Er 2 o 3 0.1%, mix evenly, melt at 1200-1400°C for 4 hours to obtain molten glass, quench the molten glass with water, dry and mill in a ball mill for 12 hours, and obtain glass powder after drying.

[0030] The preparation method of the spray-coated ceramic surface sintered silver paste is as follows: add water into a container, add polyvinylpyrrolidone and stir until dissolved, then add Tween, simethicone an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spraying type ceramic surface-sintered silver paste which contains the following components: 50-60 parts of nanometer silver powder, 1-3 parts of glass powder, 5-10 parts of twain, 5-10 parts of polyvinylpyrrolidone, 5-10 parts of dimeticone, 3-5 parts of sweet almond oil and 15-20 parts of water. A preparation method comprises the following steps: adding water into a container; adding polyvinylpyrrolidone and stirring till dissolving; adding twain, dimeticone and sweet almond oil and stirring for 0.5-1 hour at 500-600rpm; lastly, adding the nanometer silver powder and the glass powder and stirring for 20-30min at 500-600rpm. According to the invention, the preparation process of the silver paste is simple, the silver layer is firm after the sintering and is difficult to fall off; the silver paste is nontoxic and harmless and contains no other heavy metal; when the silver paste is applied to the food container, the silver paste has disinfecting and bactericidal effects; the silver paste is wide in application prospect.

Description

technical field [0001] The invention relates to the technical field of ceramic surface processing, in particular to a spray-coated ceramic surface sintered silver paste and a preparation method thereof. Background technique [0002] Porcelain is one of the most widely used utensils in people's daily life. With the improvement of people's material and cultural level, the requirements for the ornamental and functional requirements of ceramic products are getting higher and higher. Traditional ceramic products can no longer meet people's needs. need. [0003] Silver is a kind of precious metal that people love. It has good decorative properties and is one of the most commonly worn decorations. In addition, silver also has bactericidal properties, so silver has begun to be applied to dining utensils to play It has the functions of disinfection, sterilization and preservation. [0004] At present, the commonly used process is to disperse silver powder in organic solvent, apply ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/88C03C12/00C03C6/04
CPCC03C1/00C03C12/00C04B41/5111C04B41/88C04B41/5022C04B41/50C04B41/4539C04B41/4543C04B41/0072
Inventor 王博任云杨儒林顾晓甜
Owner 河北银瓷天成文化传播有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com