Double-terminated epoxy silicone oil and preparation method thereof
An epoxy silicone oil and double-ended technology, which is applied in the field of preparation of double-ended epoxy silicone oil, can solve the problems of high production condition requirements, long production consumption time, reduction of double-ended epoxy silicone oil output and production efficiency, etc., and meets the requirements of production conditions. Low, improve production efficiency, the effect of less production time consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] Embodiment 1: drop into 400kg of double-ended hydrogen-containing silicone oil and 12kg of allyl glycidyl ether in an enamel kettle or a stainless steel reaction kettle, be warming up to 85 ℃ after stirring, add the isopropanol solution of chloroplatinic acid, and react the temperature after 15 minutes. Raise the temperature to 100-115°C, when the solution is transparent and clear, continue to react at 100-115°C for 1 hour, and finally at 110-120°C under reduced pressure, remove the residual allyl glycidyl ether for 30-60min. Low boiler to obtain double-ended epoxy silicone oil.
Embodiment 2
[0015] Embodiment 2: drop into 400kg of double-ended hydrogen-containing silicone oil and 20kg of allyl glycidyl ether in enamel kettle or stainless steel reaction kettle, be warming up to 80 DEG C after stirring, add the isopropanol solution of chloroplatinic acid, and the temperature increases after reaction 15min To 100-115 ℃, when the solution is transparent and clear, continue to react at 100-115 ℃ for 1 hour, and finally, under reduced pressure, at 110-120 ℃, after 30-60min, the residual allyl glycidyl ether is removed. Boiling to obtain double-ended epoxy silicone oil.
Embodiment 3
[0016] Embodiment 3: drop into double-ended hydrogen-containing silicone oil 400kg, allyl glycidyl ether 9kg in enamel kettle or stainless steel reaction kettle, be warming up to 85-90 ℃ after stirring, add the isopropanol solution of chloroplatinic acid, react after 15min The temperature was raised to 110-115°C. When the solution was transparent and clear, the reaction was continued at 100-115°C for 1 hour. Finally, under reduced pressure, the residual allyl glycidyl ether was removed at 110-120°C for 60-90min. Wait for the low boiler to obtain double-ended epoxy silicone oil.
[0017] The double-ended hydrogen-containing silicone oil described in the examples is prepared by the following preparation method, and the preparation method includes the following steps: adding 350-450 kg of octamethylcyclotetrasiloxane successively to the enamel reaction kettle, and the hydrogen-containing double seal The first 4-9kg, after stirring, add 8-15kg of concentrated sulfuric acid, keep t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com