Preparation method of enteromorpha carbon nano material and regenerated cellulose blended fiber

A technology of carbon nanomaterials and regenerated cellulose, applied in the direction of artificial filaments in cellulose solution, fiber chemical characteristics, rayon manufacturing, etc., to achieve the effects of wide sources, good adsorption and deodorization effects, and environmental protection

Active Publication Date:
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no method in the prior art to combine Enteromorpha and regenerated cellulose to produce a blended fiber with better performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The invention provides a preparation method of Enteromorpha carbon nanomaterial regenerated cellulose blended fiber, comprising the following preparation steps:

[0028] (1) Use Enteromorpha as raw material to prepare high-performance Enteromorpha carbon nanomaterials: collect Enteromorpha, pick and remove impurities, wash, freeze-dry, crush and sieve to obtain 100 mesh Enteromorpha powder; take the Enteromorpha powder in Calcined to black in a nitrogen atmosphere at 200°C for 60 minutes to obtain a pre-carbonized product; add potassium permanganate to the pre-carbonized product according to a weight ratio of 1:1, at a temperature of 50°C and a stirring speed of Stirring under the condition of 50r / min for 4h to obtain a precursor; drying the precursor at 50°C for 6h to obtain an intermediate product; subjecting the intermediate product to heat treatment to obtain product I, the conditions of the heat treatment are, at 10 The temperature was raised to 600°C at a heating ...

Embodiment 2

[0032] Different from Example 1, a preparation method of Enteromorpha carbon nanomaterial regenerated cellulose blended fiber comprises the following preparation steps:

[0033] (1) Use Enteromorpha as raw material to prepare high-performance Enteromorpha carbon nanomaterials: collect Enteromorpha, pick and remove impurities, wash, freeze-dry, crush and sieve to obtain 50 mesh Enteromorpha powder; take the Enteromorpha powder in Calcined to black under argon atmosphere at 800°C for 60 minutes to obtain a pre-carbonized product; add phosphorus pentoxide to the pre-carbonized product according to the weight ratio of 1:5, at a temperature of 50°C and a stirring speed of Stirring at 300r / min for 10h to obtain a precursor; drying the precursor at 100°C for 12h to obtain an intermediate product; subjecting the intermediate product to heat treatment to obtain product I, the heat treatment conditions being, Raise the temperature to 1400°C at a heating rate of 20°C / min, and then heat f...

Embodiment 3

[0037] Different from Example 1, a preparation method of Enteromorpha carbon nanomaterial regenerated cellulose blended fiber comprises the following preparation steps:

[0038] (1) Use Enteromorpha as raw material to prepare high-performance Enteromorpha carbon nanomaterials: collect Enteromorpha, pick and remove impurities, wash, freeze-dry, crush and sieve to obtain 70 mesh Enteromorpha powder; take the Enteromorpha powder in Calcined to black under argon atmosphere at 650°C for 30 minutes to obtain a pre-carbonized product; add phosphorus pentoxide to the pre-carbonized product according to the weight ratio of 1:3, at a temperature of 30°C and a stirring speed of Stirring at 250r / min for 8h to obtain a precursor; drying the precursor at 85°C for 10h to obtain an intermediate product; subjecting the intermediate product to heat treatment to obtain product I, the conditions of the heat treatment are as follows: The temperature was raised to 1000°C at a heating rate of 15°C / m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
antibacterial rateaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an enteromorpha carbon nano material and regenerated cellulose blended fiber. The preparation method is characterized by comprising the following preparation steps of (1), preparing a high-performance enteromorpha carbon nano material by using enteromorpha as a raw material; (2), blending the enteromorpha carbon nano material with a regenerated cellulose spinning solution; (3), spinning the blended spinning solution through a wet-method spinning device, and shaping a fiber through a coagulating bath, so as to prepare the enteromorpha carbon nano material and regenerated cellulose blended fiber. According to the preparation method of the enteromorpha carbon nano material and regenerated cellulose blended fiber, the raw materials are rich in source and low in cost, the method is simple in preparation process, is free from pollution and can be used for quantitative production; the prepared enteromorpha carbon nano material and regenerated cellulose blended fiber is good in antibacterial, adsorptive and deodorant effects, and is higher in added value compared with ordinary regenerated cellulose.

Description

technical field [0001] The invention belongs to the technical field of preparation of blended regenerated cellulose, and in particular relates to a preparation method of Enteromorpha carbon nanomaterial regenerated cellulose blended fiber. Background technique [0002] Regenerated fibers are chemical fibers made from natural polymers by chemical methods, and have basically the same chemical composition as the original polymers. Due to the characteristics of softness, comfort, breathability and environmental protection of regenerated cellulose fiber, the clothes woven by it are favored by consumers all over the world. Due to the reduction of cultivated land and the depletion of oil resources, the output of natural fibers and synthetic fibers will be more and more restricted; while people pay attention to the environmental protection performance in the process of textile consumption, the value of regenerated cellulose fibers has been reconsidered. Know and discover. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/02D01F1/10
CPCD01F1/10D01F1/103D01F2/02
Inventor 曲丽君田明伟迟淑丽杜敏芝赵壬海于荣荣赵洪涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com