A kind of preparation method of pt-cu linear nano catalyst

A nano-catalyst, pt-cu technology, applied in catalyst activation/preparation, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problems of unguaranteed yield, small length and diameter, and thick nanowire diameter. , to achieve the effect that the method is simple and easy to implement and has broad application prospects.

Active Publication Date: 2018-12-07
HEBEI UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the process of preparing nanowires by the template method is complicated, the preparation cycle is long, the diameter of the prepared nanowires is thick, the long diameter is small, and the yield cannot be guaranteed.
Therefore, there are still some difficult problems and challenges in the preparation of high-quality nanowires.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of pt-cu linear nano catalyst
  • A kind of preparation method of pt-cu linear nano catalyst
  • A kind of preparation method of pt-cu linear nano catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 1. At room temperature, add 5ml of oleylamine to the reaction kettle.

[0034] 2. At room temperature, 0.01g of platinum acetylacetonate (Pt(acac) 2 , 2.54×10 -5 mol) and 0.05g potassium iodide (3.01×10 -4 mol) into 5ml oleylamine, magnetically stirred for 30min, then added 0.02g copper acetylacetonate (Cu(acac) 2 , 7.64×10 -5 mol), and magnetically stirred for 10 min.

[0035] 3. Tighten the reactor and put it in the oven, set the oven temperature to 170°C, and the reaction time to 12 hours.

[0036] 4. After the reaction is finished, wash with absolute ethanol for 4 times to obtain the Pt-Cu linear nanocatalyst.

experiment example 2

[0038] Other experimental steps are the same as in Experimental Example 1, except that the amount of KI in step 2 is changed from 0.05 g to 0 g.

experiment example 3

[0040] Other experimental steps are the same as in Experimental Example 1, except that the amount of KI in step 2 is changed from 0.05g to 0.025g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is a preparation method of Pt-Cu linear nanocatalyst. The method includes the following steps: adding platinum acetylacetonate and potassium iodide to oleylamine, then adding copper acetylacetonate, and the reaction time is 3-24 hours at 160-180°C; finally cleaning with absolute ethanol to obtain Pt- Cu linear nanocatalyst. The method for preparing Pt-Cu linear nanocatalysts provided by the present invention is a simple method, does not use templates, is simple to operate, and is easy to produce.

Description

technical field [0001] The invention belongs to the technical field of functional materials, and more specifically relates to a preparation method of a Pt-Cu linear nano-catalyst. Background technique [0002] One-dimensional nanomaterials refer to nanomaterials that have two dimensions in the nanoscale range in space, such as nanowires, nanorods, nanobelts, and nanotubes. Compared with nano-bulk materials, one-dimensional nanomaterials have excellent size effects and can form more complex nanoscale structures, especially one-dimensional noble metal materials well integrate the unique properties of one-dimensional nanomaterials and metals themselves, and have Different from the special physical and chemical properties of the corresponding bulk materials, it can be applied in the fields of ultra-large-scale integrated circuits, optical fibers, chemical sensors, chemical catalysis, and biomedicine. Therefore, one-dimensional noble metal nanomaterials have become the frontier ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89B01J35/02B01J35/06B01J35/00
CPCB01J23/8926B01J37/08B01J35/58B01J35/40
Inventor 于晓飞董立丽李兰兰赵建玲
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More