A special admixture for high-performance underwater masonry mortar

A masonry mortar and high-performance technology, which is applied in the field of special admixtures for high-performance underwater masonry mortar, can solve the problems of lack of construction technology, products and construction technology, little practical use effect and meaning, and general effect, etc. Normal hardening strength, good strength retention rate, good construction effect

Active Publication Date: 2018-08-31
北京建工新型建材有限责任公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the existing public technology has listed the technical routes, proportions and related instructions of some special admixtures for underwater masonry mortar, the effect in actual use is general, and there is no clear construction process and product and construction technology description, which has led to practical problems. Use effect and meaning is not big

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The special admixture for high-performance underwater masonry mortar in this embodiment is composed of the following components by weight: 2 parts by weight of thickener; 1 part by weight of superplasticizer; 5 parts by weight of thixotropic agent; 8 parts by weight of special cement ; 12 parts by weight of coagulation agent; 8 parts by weight of early strength agent.

[0026] Wherein: the thickener is cellulose; the superplasticizer is sulfonated resin; the thixotropic agent is modified bentonite;

[0027] The special cement is composed of the following components by weight: 3 parts by weight of sodium acetate; 8.5 parts by weight of fly ash; 0.8 parts by weight of sodium lignosulfonate; 55 parts by weight of Portland cement with a strength of 42.5.

[0028] The coagulation regulator is composed of the following components by weight: 13 parts by weight of anhydrous citric acid, 32 parts by weight of anhydrous sodium pyrophosphate, 2.5 parts by weight of sodium tripolyp...

Embodiment 2

[0032] The special admixture for high-performance underwater masonry mortar in this embodiment is composed of the following components by weight: 5 parts by weight of thickener; 0.5 parts by weight of superplasticizer; 8 parts by weight of thixotropic agent; 5 parts by weight of special cement ; 15 parts by weight of coagulation regulator; 5 parts by weight of early strength agent.

[0033] Wherein: the thickener is synthetic resin; the superplasticizer is sodium sulfonate; the thixotropic agent is montmorillonite;

[0034] The special cement is composed of the following components by weight: 6 parts by weight of sodium acetate; 5.5 parts by weight of fly ash; 0.8 parts by weight of sodium lignosulfonate; 68 parts by weight of Portland cement with a strength of 42.5.

[0035] The coagulation regulator is composed of the following components by weight: 17 parts by weight of anhydrous citric acid, 28 parts by weight of anhydrous sodium pyrophosphate, 3.5 parts by weight of sodiu...

Embodiment 3

[0039] The special admixture for high-performance underwater masonry mortar in this embodiment is composed of the following components by weight: 3 parts by weight of thickener; 0.6 parts by weight of superplasticizer; 6 parts by weight of thixotropic agent; 6 parts by weight of special cement ; 12.5 parts by weight of coagulation regulator; 6 parts by weight of early strength agent.

[0040] Among them: the thickener is hydroxypropyl methylcellulose ether; the superplasticizer is sulfonated resin; the thixotropic agent is modified bentonite;

[0041] The special cement is composed of the following components by weight: 4 parts by weight of sodium acetate; 6 parts by weight of fly ash; 0.8 parts by weight of sodium lignosulfonate; 60 parts by weight of Portland cement with a strength of 42.5.

[0042] The coagulation regulator is composed of the following components by weight: 14 parts by weight of anhydrous citric acid, 29 parts by weight of anhydrous sodium pyrophosphate, 2....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a special high-performance additive for underwater masonry mortar. The special high-performance additive is composed of, by weight, 2-5 parts of a thickening agent, 0.5-1 part of super plasticizer, 5-8 parts of a thixotropic agent, 5-8 parts of special cement, 12-15 parts of a set controlling agent and 5-8 parts of an early strength agent. In the special high-performance additive for the underwater masonry mortar, the thickening agent can improve the adhesiveness of a mixed product, and therefore the underwater non-disperse mortar is endowed with the properties of dispersing and separating resistance. The super plasticizer can improve the fluidity and workability of the mixed product, and therefore the material is endowed with good self-leveling and self-compacting properties. The frequently-used super plasticizer mainly includes sulfonated resin or sulfonate, and therefore the material has the properties of underwater dispersing and separating resistance. Through the combined action of the doped special cement and the set controlling agent, the material is endowed with early strength and rapid hardening.

Description

technical field [0001] The invention relates to a special admixture for high-performance underwater masonry mortar. Background technique [0002] When cement mortar or concrete is in the state of water or under high disturbance, the slurry will easily segregate when it encounters water (cement is easy to lose, sand and gravel are easy to separate), which will affect the hardening and the performance of concrete or mortar. In the past, the repair of construction or damage of underwater concrete buildings was generally completed by building cofferdams, draining water, and then pouring concrete or building walls and plastering mortar. This type of project has the disadvantages of time-consuming, labor-intensive and expensive. The second method is to use chutes, conduits, pumps, open bottom containers, etc. to transport ordinary concrete or mortar to the underwater pouring or repairing position to complete. But the common underwater concrete or mortar that the second kind of w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38C04B111/74
CPCC04B40/0039C04B2103/0068C04B2111/74C04B7/26C04B24/383C04B24/161C04B14/104C04B24/06C04B22/16C04B24/38C04B14/04C04B22/128C04B22/0093C04B22/062C04B14/06C04B24/122C04B24/24C04B24/16C04B14/106
Inventor 史忠金颖张倩倩梁云利侯凯
Owner 北京建工新型建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products