Sterilization and smoke suppression halogen-free wood fire retardant

A fire retardant and wood technology, applied in wood treatment, impregnated wood, wood impregnation, etc., can solve the problems of low moisture absorption rate, low bactericidal and antibacterial effect, etc., achieve good anti-loss performance, improve anti-moisture performance and stability Sexuality, the effect of improving smoke suppression performance

Inactive Publication Date: 2017-02-01
GUANGXI UNIV
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the flame retardant in the above patent has the advantages of flame retardancy, smoke suppression, good stability, and low moisture absorption rate, its bactericidal and antibacterial effect is not outstanding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of sterilization and smoke suppression halogen-free wood flame retardant is composed of the following raw materials by mass: 70 parts of amidine urea phosphate, 40 parts of urea, 15 parts of zinc borate, 6 parts of ammonium molybdate, 9 parts of pentaerythritol, dihydrogen phosphate 15 parts of ammonium, 20 parts of silica sol, 10 parts of decabromodiphenyl ether, 8 parts of fatty alcohol polyoxyethylene ether, 13 parts of cetyltrimethoxysilane, 15 parts of nano titanium dioxide modified with Pt; The percentage of nano-titania in the Pt-modified nano-titania is 85%.

[0016] The preparation method includes the following steps: weigh the components according to the weight ratio, and then combine the amidino urea phosphate, urea, diammonium hydrogen phosphate, zinc borate, ammonium molybdate, pentaerythritol, decabromodiphenyl ether and Pt modified Nano-titanium dioxide is mixed uniformly, then silica sol, fatty alcohol polyoxyethylene ether and cetyltrimethoxysilane ...

Embodiment 2

[0018] A kind of sterilization and smoke suppression halogen-free wood flame retardant is composed of the following raw materials by mass: 40 parts of amidine urea phosphate, 50 parts of urea, 10 parts of zinc borate, 10 parts of ammonium molybdate, 3 parts of pentaerythritol, and dihydrogen phosphate 20 parts of ammonium, 12 parts of silica sol, 15 parts of decabromodiphenyl ether, 5 parts of fatty alcohol polyoxyethylene ether, 20 parts of cetyltrimethoxysilane, 3+ 20 parts of modified nano titanium dioxide; said Fe 3+ The percentage of nanometer titanium dioxide in the modified nanometer titanium dioxide is 90%.

[0019] The preparation method includes the following steps: weigh each component according to the weight ratio, and then combine the amidino urea phosphate, urea, diammonium hydrogen phosphate, zinc borate, ammonium molybdate, pentaerythritol, decabromodiphenyl ether and iron 3+ The modified nano-titanium dioxide is mixed uniformly, and then silica sol, fatty alcohol p...

Embodiment 3

[0021] A kind of sterilization and smoke suppression halogen-free wood flame retardant is composed of the following raw materials by mass: 40 parts of amidine urea phosphate, 50 parts of urea, 20 parts of zinc borate, 5 parts of ammonium molybdate, 10 parts of pentaerythritol, and dihydrogen phosphate 1 part of ammonium, 25 parts of silica sol, 3 parts of decabromodiphenyl ether, 10 parts of fatty alcohol polyoxyethylene ether, 1 part of cetyltrimethoxysilane, 1 part of nano titanium dioxide modified by Ag; The percentage of nano-titania in the Ag-modified nano-titania is 80%.

[0022] The preparation method includes the following steps: weigh each component according to the weight ratio, and then combine the amidino urea phosphate, urea, diammonium hydrogen phosphate, zinc borate, ammonium molybdate, pentaerythritol, decabromodiphenyl ether and Ag modified The nano-titanium dioxide is mixed uniformly, then silica sol, fatty alcohol polyoxyethylene ether and cetyltrimethoxysilane...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sterilization and smoke suppression halogen-free wood fire retardant. The sterilization and smoke suppression halogen-free wood fire retardant is composed of, by mass, 40-80 parts of guanyl urea phosphate, 30-50 parts of urea, 10-20 parts of zinc borate, 5-10 parts of ammonium molybdate, 3-10 parts of pentaerythritol, 1-20 parts of ammonium dihydrogen phosphate, 12-25 parts of silica sol, 3-15 parts of decabromodiphenyl ether, 5-10 parts of fatty alcohol-polyoxyethylene ether, 1-20 parts of hexadecyltrimethoxysilane, and 1-20 parts of nanometer titania modified by one of Pt, Ag and Fe<3+>. The sterilization and smoke suppression halogen-free wood fire retardant is good in flame retardant property, high in anti-moisture absorption property and leaching resistance, good in stability, completely non-poisonous and low in cost and has the smoke suppression and sterilization effects.

Description

Technical field [0001] The invention relates to the technical field of flame-retardant materials, in particular to a sterilization and smoke-suppressing halogen-free wood flame retardant. Background technique [0002] Wood is an ideal material for construction, furniture and interior decoration, but its flammability limits its use. Wood flame retardant is a kind of mechanism that promotes the formation of charcoal, forms an isolation layer, releases incombustible gases, terminates free radical reactions, and absorbs combustion heat. It makes wood flammable and becomes non-combustible, which greatly increases the safety of wood. Sex. [0003] At present, wood flame retardants are mainly composed of halogen and its compound flame retardants, metal hydroxide flame retardants, phosphorus-based halogen-free flame retardants, boron-based flame retardants, phenolic flame retardants, FRW flame retardants, etc. Halogen and its compound flame retardants are rarely used because they produce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/52
CPCB27K3/52B27K2240/30
Inventor 郭琴
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com