Rubber antiskid and abrasion-resistant shoe sole and preparation method thereof

A slippery wear-resistant, shoe sole technology, applied in the field of rubber, can solve the problems of non-wearable and poor anti-skid effects, and achieve the effects of increased life, high anti-skid wear resistance, and guaranteed wearing comfort

Inactive Publication Date: 2017-01-11
张顺其
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: the purpose of this invention is to provide a rubber anti-skid wear-resistant shoe, which solves a series of shortcomings such as poor anti-skid effect and non-wear resistance of the sole, and improves the service life of the shoe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber antiskid and abrasion-resistant shoe sole and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A rubber anti-slip and wear-resistant shoe sole, prepared from the following components by weight: 20 parts of butadiene rubber, 55 parts of natural rubber, 2 parts of sulfur, 4.5 parts of nano-zinc oxide, 1 part of stearic acid, and 0.5 parts of vulcanization accelerator DM 0.5 parts of nano-silicon nitride, 40 parts of carbon black, 3 parts of anti-aging agent DNP, 10 parts of diethyl phthalate, 7 parts of modified benzoxazine resin, 15 parts of dicyclopentadiene dioxide epoxy resin , 10 parts of B205 ceramic sand, 3 parts of high-performance hollow glass microspheres, and 7.5 parts of aramid fiber.

[0019] The preparation method of the above-mentioned rubber anti-slip wear-resistant shoe sole is: (1) pre-mixing: adding carbon black, butadiene rubber, natural rubber, nano-zinc oxide, stearic acid and diethyl phthalate into the internal mixer After masterbatching for 5 minutes, store at room temperature for 36 hours; (2) Mixing: Put the mixed rubber in step (1) into t...

Embodiment 2

[0021] A rubber anti-slip and wear-resistant shoe sole, which is prepared from the following components in parts by weight: 30 parts of butadiene rubber, 40 parts of natural rubber, 1 part of sulfur, 6.5 parts of nano-zinc oxide, 3 parts of stearic acid, and vulcanization accelerator DM 3 1.5 parts of nano-silicon nitride, 50 parts of carbon black, 1 part of anti-aging agent DNP, 6 parts of diethyl phthalate, 15 parts of modified benzoxazine resin, 5 parts of dicyclopentadiene dioxide epoxy resin , 5 parts of B205 ceramic sand, 8 parts of high-performance hollow glass microspheres, and 12.5 parts of aramid fiber.

[0022] The preparation method of the above-mentioned rubber anti-slip wear-resistant shoe sole is: (1) pre-mixing: adding carbon black, butadiene rubber, natural rubber, nano-zinc oxide, stearic acid and diethyl phthalate into the internal mixer After masterbatching for 12 minutes, store at room temperature for 24 hours; (2) Mixing: Put the mixed rubber in step (1) ...

Embodiment 3

[0024] A rubber anti-slip and wear-resistant shoe sole, which is prepared from the following components by weight: 22 parts of butadiene rubber, 50 parts of natural rubber, 1.8 parts of sulfur, 6 parts of nano-zinc oxide, 1.5 parts of stearic acid, and 2.5 parts of vulcanization accelerator DM 1.2 parts of nano-silicon nitride, 43 parts of carbon black, 1.8 parts of anti-aging agent DNP, 7 parts of diethyl phthalate, 13 parts of modified benzoxazine resin, dicyclopentadiene dioxide epoxy resin 8 parts, 10 parts of B205 ceramic sand, 7 parts of high-performance hollow glass microspheres, 11 parts of aramid fiber.

[0025] The preparation method of the above-mentioned rubber anti-slip wear-resistant shoe sole is: (1) pre-mixing: adding carbon black, butadiene rubber, natural rubber, nano-zinc oxide, stearic acid and diethyl phthalate into the internal mixer After masterbatching for 8 minutes, store it at room temperature for 30 hours; (2) Mixing: Put the mixed rubber in step (1)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a rubber antiskid and abrasion-resistant shoe sole and a preparation method thereof. The rubber antiskid and abrasion-resistant shoe sole is prepared from, by weight, 20-30 parts of butadiene rubber, 40-55 parts of natural rubber, 1-2 parts of sulfur, 4.5-6.5 parts of nano-zinc oxide, 1-3 parts of stearic acid, 0.5-3 parts of vulcanization accelerator DM, 0.5-1.5 parts of nanometer silicon nitride, 40-50 parts of carbon black, 1-3 parts of antiager DNP, 6-10 parts of diethyl phthalate, 7-15 parts of modified benzoxazine resin, 5-15 parts of bicyclopentadiene dioxide epoxy resin, 5-10 parts of B205 ceramic sand, 3-8 parts of high-performance hollow glass beads and 7.5-12.5 parts of aramid fibers. The rubber antiskid and abrasion-resistant shoe sole is prepared through the steps of pre-mixing, mixing, cooling and vulcanizing. The formula and preparation method of shoe sole rubber are improved, the shoe sole rubber with the high anti-skid coefficient and abrasion resistance is obtained, the service life is prolonged, and the use comfort is improved.

Description

technical field [0001] The invention relates to the field of rubber, in particular to a rubber anti-slip wear-resistant shoe sole and a preparation method thereof. Background technique [0002] Shoes are requisite supplies for people to go out, and there are many types of shoes for various people to choose from. As an elastic polymer, rubber has abundant raw materials, low price, good elasticity and high strength, and is very suitable as a material for making shoe soles. People have different requirements for shoes, but wear resistance and anti-skid performance are common requirements of people. With the development of the times, people have higher and higher requirements for shoes. There are running shoes, sneakers, football shoes and other shoes specially used for various sports. These shoes will generate a lot of friction with the ground when worn, so it will cause a lot Large wear, which puts forward higher requirements for the wear resistance of the sole material. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L77/10C08K13/04C08K3/06C08K3/22C08K5/09C08K3/34C08K3/04C08K7/28A43B13/04
CPCA43B13/04C08K2201/011C08L7/00C08L2205/035C08L2205/16C08L9/00C08L77/10C08K13/04C08K3/06C08K2003/2296C08K5/09C08K3/34C08K3/04C08K7/28
Inventor 樊之雄
Owner 张顺其
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com