A kind of ultra-high energy density lithium-ion battery cathode material and preparation method thereof

A lithium-ion battery, cathode material technology, applied in battery electrodes, circuits, electrical components, etc., can solve problems such as low capacity and poor electrochemical performance, improve discharge specific capacity, inhibit structural collapse, and improve comprehensive electrochemical performance. Effect

Active Publication Date: 2019-05-14
UNIV OF ELECTRONICS SCI & TECH OF CHINA
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to aim at lithium-ion battery cathode material layered nickel cobalt lithium manganese oxide (LiNi 0.6 mn 0.2 co 0.2 o 2 ) has the shortcomings of poor electrochemical performance and low capacity, and provides a bulk phase doped modified lithium ion battery positive electrode material Li(Ni 0.6 co 0.2 mn 0.2 ) 1-x Al x o 2-y f y and its preparation method, wherein 0

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high energy density lithium-ion battery cathode material and preparation method thereof
  • A kind of ultra-high energy density lithium-ion battery cathode material and preparation method thereof
  • A kind of ultra-high energy density lithium-ion battery cathode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] When Al and F doping amounts are respectively 0.01 and 0.02 (i.e. x=0.01, y=0.02), the nickel source raw material, cobalt source raw material and manganese source raw material are Ni:Co:Mn=6:2 with the total molar ratio: 2 Weigh the sample and divide it into two parts, respectively dissolve it in an appropriate amount of deionized water according to the molar ratio Ni:Co:Mn=5:2:3 and 7:2:1 to prepare a 1mol / L sulfate mixed solution a and b; sodium hydroxide solution and ammonia are mixed to form a mixed solution with a concentration of sodium hydroxide of 2 mol / L and a concentration of ammonia of 0.5 mol / L, which is recorded as solution c; the prepared two solutions a and b are successively mixed with solution c Slowly add it dropwise into the reaction tank with continuous stirring, adjust the pH with ammonia water to control the pH value at about 11, the reaction temperature is 50°C, coprecipitate reaction for 5h, and then age at 70°C for 12h, and then the obtained prod...

Embodiment 2

[0037] When Al and F doping amounts were 0.02 and 0.04 (i.e. x=0.02, y=0.04) respectively, the nickel source raw material, cobalt source raw material and manganese source raw material were Ni:Co:Mn=6:2 with the total molar ratio: 2 Weigh the sample and divide it into two parts, respectively dissolve it in an appropriate amount of deionized water according to the molar ratio Ni:Co:Mn=5:2:3 and 7:2:1 to prepare a 1mol / L sulfate mixed solution a and b; sodium hydroxide solution and ammonia are mixed to form a mixed solution with a concentration of sodium hydroxide of 2 mol / L and a concentration of ammonia of 0.5 mol / L, which is recorded as solution c; the prepared two solutions a and b are successively mixed with solution c Slowly add it dropwise into the reaction tank with continuous stirring, adjust the pH with ammonia water to control the pH value at about 11, the reaction temperature is 50°C, coprecipitate reaction for 5h, and then age at 70°C for 12h, and then the obtained pr...

Embodiment 3

[0040] When Al and F doping amounts were 0.02 and 0.02 (i.e. x=0.02, y=0.02) respectively, the nickel source raw material, cobalt source raw material and manganese source raw material were Ni:Co:Mn=6:2 with the total molar ratio: 2 Weigh the sample and divide it into two parts, respectively dissolve it in appropriate amount of deionized water according to the molar ratio Ni:Co:Mn=5:2:3 and 7:2:1 to prepare a 1mol / L sulfate mixed solution a and b; sodium hydroxide solution and ammonia are mixed to form a mixed solution with a concentration of sodium hydroxide of 2 mol / L and a concentration of ammonia of 0.5 mol / L, which is referred to as solution c; the prepared two solutions a and b are successively mixed with solution c Slowly add it dropwise into the reaction tank with continuous stirring, adjust the pH with ammonia water to control the pH value at about 11, the reaction temperature is 60°C, coprecipitate reaction for 5h, and then age at 70°C for 12h, and then the obtained pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
retention rateaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of lithium-ion batteries, and provides a lithium-ion battery positive electrode material with ultra-high energy density, which is used to overcome the shortcomings of poor electrochemical performance, low specific capacity and low energy density of nickel-cobalt lithium manganese oxide; the lithium-ion battery positive electrode material of the present invention The molecular expression of Li(Ni 0.6 co 0.2 mn 0.2 ) 1‑x Al x o 2‑y f y , where 0

Description

technical field [0001] The invention belongs to the field of lithium ion batteries, and relates to a lithium ion battery positive electrode material and a preparation method thereof, in particular to a lithium ion battery positive electrode material Li(Ni 0.6 co 0.2 mn 0.2 ) 1-x al x o 2-y f y and a preparation method thereof, wherein 0<x, y≤0.05. Background technique [0002] Lithium-ion batteries have the advantages of high voltage, high energy density, and no memory effect, and are widely used in portable electronic devices. The earliest positive electrode material used in commercial lithium-ion batteries is LiCoO 2 , but Co is scarce in natural resources, expensive, and pollutes the environment, and LiCoO 2 The actual specific capacity is low, and overcharging will lead to irreversible capacity loss and increase in polarization voltage. Therefore, with the deepening of the research on cathode materials with low price and excellent performance, it has been fou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/48H01M4/505H01M4/525
CPCH01M4/48H01M4/505H01M4/525Y02E60/10
Inventor 刘兴泉王震伟赵红远蔡宇谭铭刘珊珊熊伟强陈炳
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap