Novel thermal-insulation metal material and preparation method thereof

A technology for insulating metal materials and metal material layers, which is applied in chemical instruments and methods, layered products, natural mineral layered products, etc., can solve problems such as inability to meet use requirements, rust, etc., and achieves low cost and simple preparation process. , good thermal insulation performance

Inactive Publication Date: 2017-01-04
苏州极地实业有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Metal materials are usually made of 100% metal components. Products made of such metal materials have been widely used and promoted in the market, but they are easily affected by external factors and rusted, and in some specific The environment often cannot meet the needs of people, such as the heat insulation performance of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing a novel heat-insulating metal material, comprising the steps of:

[0024] a: 30 parts of Al, 6 parts of Cu, and 2 parts of Fe are placed in an inert gas and heated for 1 hour, and it is guaranteed not to melt;

[0025] b: Cool the three materials of 30 parts of Al, 6 parts of Cu and 2 parts of Fe that have been heat-treated in step a to room temperature, and the cooling time is 2 hours;

[0026] c: 30 parts of Al, 6 parts of Cu, 2 parts of Fe, 2 parts of Ti, 1 part of Cr, 1 part of Ni, 1 part of C, 1 part of Mo and unavoidable impurities that have been cooled in step b Mixing, pouring and other treatments in the furnace to make prefabricated parts;

[0027] d: cooling and tempering the prefabricated part in step b to obtain a finished metal material.

[0028] It is particularly emphasized that the inert gas in step a is any one or a mixture of helium, argon, and neon.

Embodiment 2

[0030] A method for preparing a novel heat-insulating metal material, comprising the steps of:

[0031] a: 35 parts of Al, 8 parts of Cu, and 3 parts of Fe were placed in an inert gas and heated for 1.5 hours, and it was guaranteed not to melt;

[0032] b: 35 parts of Al, 8 parts of Cu, and 3 parts of Fe three materials that have been heated and heated in step a are cooled to room temperature, and the cooling time is 3 hours;

[0033] c: 35 parts of Al, 8 parts of Cu, 3 parts of Fe, 4 parts of Ti, 2 parts of Cr, 3 parts of Ni, 2 parts of C, 1.5 parts of Mo and unavoidable impurities that have been cooled in step b Mixing, pouring and other treatments in the furnace to make prefabricated parts;

[0034] d: cooling and tempering the prefabricated part in step b to obtain a finished metal material.

[0035] It is particularly emphasized that the inert gas in step a is any one or a mixture of helium, argon, and neon.

Embodiment 3

[0037] A method for preparing a novel heat-insulating metal material, comprising the steps of:

[0038] a: 40 parts of Al, 10 parts of Cu, and 4 parts of Fe are placed in an inert gas for heating treatment for 2 hours, and it is guaranteed not to melt;

[0039] b: Cool the three materials of 40 parts of Al, 10 parts of Cu and 4 parts of Fe that have been heat-treated in step a to room temperature, and the cooling time is 4 hours;

[0040] c: Place 40 parts of Al, 10 parts of Cu, 4 parts of Fe, 6 parts of Ti, 3 parts of Cr, 5 parts of Ni, 3 parts of C, 2 parts of Mo and unavoidable impurities in the cooling process of step b. Mixing, pouring and other treatments in the furnace to make prefabricated parts;

[0041] d: cooling and tempering the prefabricated part in step b to obtain a finished metal material.

[0042] It is particularly emphasized that the inert gas in step a is any one or a mixture of helium, argon, and neon.

[0043] The beneficial effects of the present inv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel thermal-insulation metal material and a preparation method thereof. The novel thermal-insulation metal material comprises a first thermal-insulation layer, a second thermal-insulation layer and a metal material layer bonded between the first thermal-insulation layer and the second thermal-insulation layer, wherein the first thermal-insulation layer is an aluminum plated polyester film, and the second thermal-insulation layer is asbestos fiber. All elements added into the metal material layer are as follows in parts by weight: 30 to 40 parts of Al, 6 to 10 parts of Cu, 2 to 4 parts of Fe, 2 to 6 parts of Ti, 1 to 3 parts of Cr, 1 to 5 parts of Ni, 1 to 3 parts of C, 1 to 2 parts of Mo and unavoidable impurities. According to the novel thermal-insulation metal material, the metal material layer is wrapped by the first thermal-insulation layer and the second thermal-insulation layer; thus, a high temperature can be insulated completely, and the novel thermal-insulation metal material is good in thermal-insulation performance. Furthermore, the novel thermal-insulation material is simple in preparation technology and low in cost, and the thermal-insulation performance of the metal material is further improved by warming and heating the main metal raw materials before fusion and pouring.

Description

technical field [0001] The invention relates to a novel heat-insulating metal material and a preparation method thereof. Background technique [0002] Metal materials are usually made of 100% metal components. Products made of such metal materials have been widely used and promoted in the market, but they are easily affected by external factors and rusted, and in some specific The environment often cannot meet people's use needs, such as the heat insulation performance of metal materials. [0003] There are many kinds of thermal insulation materials, which can be divided into organic thermal insulation materials, inorganic thermal insulation materials and metal thermal insulation materials according to their materials. The thermal insulation materials used for thermal equipment and pipelines are mostly inorganic thermal insulation materials. This type of material has the characteristics of non-rot, non-combustible, and high-temperature resistance; organic heat-insulating ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/09B32B15/14B32B27/36B32B27/06B32B27/16B32B19/08B32B19/04C22C21/12C22C30/02C22C1/02
CPCB32B15/09B32B5/02B32B15/14B32B27/06B32B27/16B32B27/36B32B2262/108B32B2307/304C22C1/026C22C21/12C22C30/02
Inventor 朱宗文
Owner 苏州极地实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com