Method for preparing yttrium oxide nano material

A technology of nanomaterials and yttrium oxide, which is applied in the field of preparation of yttrium oxide nanomaterials, can solve problems such as unfavorable large-scale industrial production, expensive alkoxides, and component deviations, and achieve high production efficiency, low preparation costs, and good dispersion Effect

Inactive Publication Date: 2016-12-21
BOHAI UNIV
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the solid-phase sintering reaction method is one of the most commonly used methods for preparing powders, but the composition of the product is prone to deviation, and the single-phase calcination temperature is above 2000 °C
Although the sol-gel method is an ideal and simple method for preparing yttrium oxide nanomaterials, it generally uses expensive alkoxides, which is not conducive to large-scale industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing yttrium oxide nano material
  • Method for preparing yttrium oxide nano material
  • Method for preparing yttrium oxide nano material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Accurately weigh yttrium acetylacetonate and dissolve it in methanol (12C, 99.95%) with stirring to prepare a methanol solution of yttrium acetylacetonate with a molar concentration of 0.01mol / L. The methanol solution obtained is carried out solvothermal reaction, and the solvothermal reaction temperature is 220 ℃, and the solvothermal reaction time is 24 hours. After the solvothermal reaction was completed, it was naturally cooled to room temperature, and the product obtained by the reaction was filtered and washed and placed in an oven at a programmed temperature increase rate of 5°C / min, and dried at 100°C for 3 hours. Then place it in a muffle furnace for calcination, the calcination time is 8 hours, the calcination temperature is 600 °C, and the heating rate is 10 °C / min. After natural cooling, the yttrium oxide nanomaterial with a size of 30 nm was obtained, and the yield of the product was 99.9%. The purity of the product is 99.98%, and the impurity carbon conte...

Embodiment 2

[0032] Accurately weigh yttrium acetylacetonate and dissolve it in methanol (12C, 99.95%) with stirring to prepare a methanol solution of yttrium acetylacetonate with a molar concentration of 0.02mol / L. The methanol solution obtained is carried out solvothermal reaction, and the solvothermal reaction temperature is 110 ℃, and the solvothermal reaction time is 48 hours. After the solvothermal reaction was completed, it was naturally cooled to room temperature, and the product obtained by the reaction was filtered and washed and placed in an oven at a programmed temperature increase rate of 5°C / min, and dried at 60°C for 5 hours. Then place it in a muffle furnace for calcination, the calcination time is 5 hours, the calcination temperature is 700 °C, and the heating rate is 20 °C / min. After natural cooling, the yttrium oxide nanomaterial with a size of 50 nm was obtained, and the yield of the product was 99.5%. The purity of the product is 99.92%, and the impurity carbon conten...

Embodiment 3

[0034] Accurately weigh yttrium acetylacetonate and dissolve it in methanol (12C, 99.95%) with stirring to prepare a methanol solution of yttrium acetylacetonate with a molar concentration of 0.05mol / L. The methanol solution obtained is carried out solvothermal reaction, and the solvothermal reaction temperature is 200 ℃, and the solvothermal reaction time is 12 hours. After the solvothermal reaction was completed, it was naturally cooled to room temperature, and the product obtained by the reaction was filtered and washed and placed in an oven at a programmed temperature increase rate of 5°C / min, and dried at 120°C for 1 hour. Then place it in a muffle furnace for calcination, the calcination time is 4 hours, the calcination temperature is 700 °C, and the heating rate is 10 °C / min. After natural cooling, the yttrium oxide nanomaterial with a size of 40 nm was obtained, and the yield of the product was 99.6%. The purity of the product is 99.95%, and the impurity carbon conten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of inorganic non-metal material preparation, and in particular relates to a method for preparing a yttrium oxide nano material. The method comprises the following steps: sufficiently dissolving yttrium acetylacetonate in a methanol solution, performing a solvothermal reaction, performing filtration and washing, and performing drying, calcining and cooling, thereby obtaining the yttrium oxide nano material. The method is simple and feasible in process, high in product purity and low in preparation cost; the size of a prepared product is 30-50nm, and the product is good in both uniformity and dispersibility, and moreover is simple in production process, low in sintering temperature and easy in application to practical large-scale production. The yttrium oxide nano material prepared by using the method has wide application prospects in fields such as fluorescence medium materials.

Description

technical field [0001] The invention belongs to the technical field of preparation of inorganic non-metallic materials, and in particular relates to a preparation method of yttrium oxide nanometer material. Background technique [0002] Yttrium oxide (Y 2 o 3 ) material has become an important research object in the field of laser dielectric material research due to its unique crystal structure. Yttrium oxide in the cubic phase has excellent physical and chemical properties, and high transparency in a wide frequency range from 280 nm to 8 mm. And the melting point of yttrium oxide is as high as 2430 °C. Yttrium oxide can also be used to manufacture magnetic materials for microwaves and important materials for military industry, as well as optical glass, ceramic material additives, high-brightness phosphors for large-screen TVs and other picture tube coatings. It is also used in the manufacture of film capacitors and special refractory materials, as well as magnetic bubbl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F17/00B82Y30/00
CPCC01F17/206C01P2004/03C01P2004/64C01P2006/80
Inventor 张杰许家胜于禄王莉丽崔岩孙啸虎
Owner BOHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com