Soft hard alternate composite coating used for surface of bearing bush material and preparation method of soft hard alternate composite coating

A composite coating and bearing bush technology is applied in the field of metal surface engineering to achieve the effects of improving wear resistance and friction reduction performance, improving working life and anti-lock performance, and improving bearing capacity of bearing bushes

Inactive Publication Date: 2016-12-14
SHANGHAI JIAO TONG UNIV
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wear-resistant and anti-friction coating is prepared by using conventional low-cost materials on the surface of the copper alloy of the bearing bush to improve the frictional mechanical properties of the bearing bush

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soft hard alternate composite coating used for surface of bearing bush material and preparation method of soft hard alternate composite coating
  • Soft hard alternate composite coating used for surface of bearing bush material and preparation method of soft hard alternate composite coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment provides a soft and hard composite coating for the surface of the bearing material, such as figure 1 As shown, it includes Cu coating, WC coating and MoS which are sequentially arranged outward from the surface of the bearing material. 2 coating. The thickness of the Cu coating is 15-50 μm, the thickness of the WC coating is 15-50 μm, and the MoS 2 The coating thickness is 15-50 μm. The total thickness of the composite coating is not more than 100 μm.

[0033] This embodiment also provides a method for preparing a soft and hard composite coating on the surface of the bearing material, which includes the following steps:

[0034] 1. Sand blast the inner surface of the bearing pad to make the roughness reach RZ 25-100μm. Put the sprayed bearing pad material into acetone solution for ultrasonic cleaning for 10 minutes. After cleaning, put the bearing pad material in an oven at 80°C for 30 min.

[0035] 2. Preparation of Cu soft coating by flame spraying...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a soft hard alternate composite coating used for the surface of a bearing bush material and a preparation method of the soft hard alternate composite coating. The composite coating comprises a Cu coating, a WC coating and a MoS2 coating which are sequentially arranged from the surface to the outside of the bearing bush material. The preparation method comprises the steps that flames are sprayed on the surface of the bearing bush material, and the Cu coating and the WC coating are sequentially prepared; and then the MoS2 coating is prepared by spraying suspension liquid to the WC coating, so that the composite coating is obtained. The soft hard alternate composite coating used for the surface of the bearing bush material and the preparation method of the soft hard alternate composite coating have the following beneficial effects that the soft hard alternate coating is prepared on the bearing bush material, so that the abrasion resistance, the antifriction performance, the bearing capacity and the embedding performance of the bearing bush are improved, the working life of the bearing bush is prolonged, and the anti-lock performance of the bearing bush is improved.

Description

technical field [0001] The invention belongs to the technical field of metal surface engineering, and in particular relates to a soft-hard alternate composite coating for the surface of bearing pad materials and a preparation method thereof. Background technique [0002] Ordinary copper alloy bearing bushes have high friction coefficient, poor wear resistance, poor embedding, and are easy to lock after working for a long time. Excellent friction mechanical properties are a necessary condition for long-life bearing pads, so prolonging the working life of copper alloy bearing pads is mainly carried out from friction reduction and wear resistance. At present, research at home and abroad shows that wear-resistant and anti-friction coatings mostly use new synthetic materials, which are rare and expensive, but there is no research on three-layer soft-hard alternating coatings composed of ordinary single anti-friction and wear-resistant materials. [0003] At present, materials wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C28/00
CPCC23C28/322C23C28/341
Inventor 曹均尹忠慰李虎林高庚员崔宇清王新波
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com