Plastic optical fiber extrusion preparation method

A technology for plastic optical fibers and raw materials, applied in the field of plastic optical fiber processing, can solve problems such as limiting polymer optical materials, and achieve the effects of improving refractive index, high performance and high production efficiency

Inactive Publication Date: 2016-12-14
周仁勇
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These factors greatly limit the practical application of such polymer optical materials in the field of optics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The technical solutions of the present invention will be further described below in conjunction with the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0016] A plastic optical fiber extrusion preparation method, characterized in that it comprises the following steps:

[0017] S1: Doping PbS nanoparticles into the core polymer;

[0018] S2: Heat the core material and the shell raw material to 60±5°C respectively, and mix them according to the ratio of 1:3, and extrude the mixture through the mold nozzle to obtain the mixture filaments;

[0019] S3: sealing and diffusing the mixture filaments at a constant temperature of 80±5°C, and then cooling down;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a plastic optical fiber extrusion preparation method. The plastic optical fiber extrusion preparation method comprises the following steps that PbS nanoparticles are doped in a core polymer; a core material and a shell layer raw material are respectively heated to 60+ / -5 DEG C, and are mixed according to a ratio of 1: 3; the mixture is extruded through a mold nozzle to obtain mixture filaments; the closed dispersion is performed for the mixture filaments in constant-temperature environment of 80+ / -5 DEG C; then, the cooling is performed; and the treated mixture filaments are coated by a polyolefin material, are heated after coating, are stretched to reach a target diameter, and are cooled to obtain plastic optical fibers. The method is high in production efficiency; the produced plastic optical fibers overcome the defect of step optical fiber dispersion; and the PbS nanoparticles are doped in the core polymer, so that the refractive index is increased, and the optical fibers are better in performances.

Description

technical field [0001] The invention relates to the technical field of plastic optical fiber processing, in particular to a plastic optical fiber extrusion preparation method. Background technique [0002] At present, the optical fibers used in communication optical cables are basically made of silica optical fibers, made of high-purity silica SiO 2 With the addition of an appropriate amount of dopant, it shows certain advantages in long-distance information transmission due to its low loss and high resistance to electromagnetic interference, but it encounters problems that are difficult to connect due to thin fiber cores when entering the home. Difficult, while installation and maintenance costs are relatively high, not suitable for the needs of LAN. The plastic optical fiber has the characteristics of thick fiber core, easy installation and maintenance and low cost, and has begun to be applied. However, in the current plastic optical fiber production methods, it is diffi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29D11/00
CPCB29D11/00663
Inventor 周仁勇
Owner 周仁勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products