Paint, and preparation method and application thereof

A coating and pigment technology, applied in the field of water-based one-component coatings, to achieve the effects of reducing VOC emissions, good mechanical properties, and lightening loads

Inactive Publication Date: 2016-12-07
DAYANG RIYUE LIQUOR IND CO LTD
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness and gloss of the existing water-based plastic coating films need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation method of the coating of the present embodiment comprises the following specific steps:

[0034] Step 1: Add A81 aldehyde resin into a three-neck flask equipped with a condenser and stirring.

[0035] Step 2: Add TDI trimer, raise the temperature to 80° C., and react for 2 hours. Adding an appropriate amount of catalyst dibutyltin dilaurate while adding the TDI trimer can effectively shorten the reaction time.

[0036] Step 3, adding isopropyl titanate to continue the reaction for 2 h.

[0037]In step 4, the temperature is lowered to below 60°C and the material is discharged to obtain an interface adhesion promoter. The mass ratio of isopropyl titanate, TDI trimer and A81 aldehyde resin added in the above steps is 4:2:1. The interfacial adhesion promoter prepared by adding metal organic matter, polyisocyanate and hydroxyl-containing oligomer at this mass ratio is the most stable.

[0038] Step 5, 20 parts by weight of carbon black slurry, 100 parts b...

Embodiment 2

[0041] The preparation method of the coating of the present embodiment comprises the following specific steps:

[0042] Step 1, adding solid hydroxy acrylic resin into a three-neck flask equipped with a condenser and stirring.

[0043] Step 2: Add TDI-TMP adduct, raise the temperature to 80° C., and react for 2 hours.

[0044] Step 3, adding aluminum isopropoxide to continue the reaction for 2 h.

[0045] In step 4, the temperature is lowered to below 60°C and the material is discharged to obtain an interface adhesion promoter. The mass ratio of aluminum isopropoxide, TDI-TMP adduct and solid hydroxyl acrylic resin added in the above steps is 4:2:1.

[0046] Step five, with 35 parts by weight of titanium white paste, 5 parts by weight of barium sulfate, 100 parts by weight of carboxyl-containing anionic water-based acrylic modified polyurethane resin, 8 parts by weight of auxiliary agents, 3 parts by weight of interfacial adhesion promoter and 20 parts by weight of deionize...

Embodiment 3

[0049] The preparation method of the coating of the present embodiment comprises the following specific steps:

[0050] Step 1, epoxy resin is added in the there-necked flask with condenser and stirring.

[0051] Step 2: Add biuret N75, heat up to 80°C, and react for 2 hours.

[0052] Step 3, adding zirconate to continue the reaction for 2h.

[0053] In step 4, the temperature is lowered to below 60°C and the material is discharged to obtain an interface adhesion promoter. The mass ratio of zirconate, biuret N75 and epoxy resin added in the above steps is 4:2:1.

[0054] Step five, with 33 parts by weight of phthalocyanine blue syrup, 100 parts by weight of carboxyl-containing anionic water-based fluorine-modified polyurethane resin, 10 parts by weight of auxiliary agents, 3 parts by weight of interfacial adhesion promoter and 20 parts by weight of Deionized water was put into a stainless steel cylinder for stirring and dispersing, the rotation speed was set at 700rad / min, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to paint, and a preparation method and application of the paint. The paint is prepared from the following ingredients including 90 to 110 weight parts of carboxyl-containing anionic waterborne resin, 15 to 40 weight parts of water-resistant pigment, 5 to 15 weight parts of body pigment, 7 to 12 weight parts of auxiliary agents, 2 to 4 weight parts of interface attaching force enhancing agents and 15 to 25 weight parts of deionized water. The interface attaching force enhancing agents is prepared from metal organic matters, polyisocyanates and hydroxyl-containing low polymers through reaction through reaction. The paint has excellent interface attaching force with amorphous plastic cement substrates.

Description

technical field [0001] The invention relates to a water-based one-component coating, a preparation method of the coating, and an application of the coating, which belong to the technical field of coatings. Background technique [0002] With people's increasing emphasis on environmental protection and energy, countries all over the world have enacted or are enacting increasingly strict laws and regulations to strictly limit the emission of VOC in coatings. In order to adapt to the transformation of the economic structure and the increasingly serious environmental problems, our country clearly proposes to accelerate the development of high-performance, energy-saving, functional coatings and supporting raw materials, especially the development of water-based automotive paints and water-based plastic coatings. Since various plastics and more and more derived compound products are widely used in people's daily life and industrial consumer goods industries, including major applica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D175/14C09D7/12
Inventor 胡州平袁立新
Owner DAYANG RIYUE LIQUOR IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka