Graphene modified glass fiber reinforced resin composite material and preparation method thereof

A graphene modification and glass fiber technology, which is applied in the field of graphene modified glass fiber reinforced resin composite materials and its preparation, can solve problems such as unsatisfactory improvement effects, and achieves increased interaction area and interface bonding force, The effect of low cost and simple process

Active Publication Date: 2016-12-07
江苏泰斯鸿科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, although graphene is coated on the surface of glass fiber to enhance the physical properties of glass fiber and expand its application in resin materials and other fields, the improvement effect is not very satisfactory and needs to be further enhanced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene modified glass fiber reinforced resin composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of preparation method of graphene modified glass fiber reinforced resin composite material, comprises the following steps:

[0019] (1) Preparation of glass fiber: After crushing and mixing 51% SiO2, 15% B2O3, 6% Na2O, 10% Al2O3 and 18% CaO, put them in a 400mL corundum crucible, melt them in a silicon-molybdenum rod resistance furnace, and add materials The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers with a diameter of about 10 μm;

[0020] (2) Glass fiber pretreatment: After taking 45 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 2mol / L. The acid leaching treatment is carried out at a constant temperature of 95°C to separate the Dissolve t...

Embodiment 2

[0026] A kind of preparation method of graphene modified glass fiber reinforced resin composite material, comprises the following steps:

[0027] (1) Preparation of glass fiber: After crushing and mixing 51% SiO2, 15% B2O3, 6% Na2O, 10% Al2O3 and 18% CaO, put them in a 400mL corundum crucible, melt them in a silicon-molybdenum rod resistance furnace, and add materials The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers with a diameter of about 10 μm;

[0028] (2) Glass fiber pretreatment: After taking 20 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 2mol / L. The acid leaching treatment is carried out at a constant temperature of 95°C to separate the Dissolve t...

Embodiment 3

[0034] A kind of preparation method of graphene modified glass fiber reinforced resin composite material, comprises the following steps:

[0035] (1) Preparation of glass fiber: After crushing and mixing 51% SiO2, 15% B2O3, 6% Na2O, 10% Al2O3 and 18% CaO, put them in a 400mL corundum crucible, melt them in a silicon-molybdenum rod resistance furnace, and add materials The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers with a diameter of about 10 μm;

[0036] (2) Glass fiber pretreatment: After taking 50 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 2mol / L. The acid leaching treatment is carried out at a constant temperature of 95°C to separate the Dissolve t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene modified glass fiber reinforced resin composite material and a preparation method thereof. The preparation method comprises the following steps that 1, glass fibers are prepared; 2, the glass fibers are pretreated; 3, graphene quantum dots are weighed and prepared into a dispersion solution of which the concentration ranges from 0.1 mg / ml to 1 mg / ml, the solvent is water or acetone or dimethyl sulfoxide, ultrasonic stirring is conducted on 80 ml-100 ml of graphene quantum dot dispersion solution, the pretreated glass fibers are added into the graphene quantum dot dispersion solution, the speed of ultrasonic stirring is decreased by half, soaking is conducted for 30 min to 60 min, and the glass fibers are cleaned and dried for use; 4, a graphene modified glass fiber reinforcement is prepared and modified with a silane coupling agent; 5, resin base materials are composited, and the graphene modified glass fiber reinforced resin composite material is obtained. The prepared graphene modified glass fiber reinforced resin composite material has a more excellent mechanical property.

Description

technical field [0001] The invention relates to a graphene modified glass fiber reinforced resin composite material and a preparation method thereof. Background technique [0002] Glass fiber (original name in English: glass fiber or fiberglass) is an inorganic non-metallic material with excellent performance. Brittle, poor wear resistance. It is generally made of glass balls or waste glass through high-temperature melting, wire drawing, winding, weaving and other processes. The diameter of its single filament is several microns to more than 20 microns, which is equivalent to a hair 1 / 20~1 / 5 of silk, and each bundle of fiber precursors is composed of hundreds or even thousands of single filaments. [0003] Graphene, as an allotrope of carbon, is a single-layer two-dimensional crystal material with a honeycomb structure formed by the hybridization of carbon atoms according to sp2 orbitals. Graphene has good mechanical properties and chemical stability, which will also be us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08K9/02C08K9/06C08K7/14C08J5/08
CPCC08J5/08C08J2377/06C08K7/14C08K9/02C08K9/06C08K2201/003C08L77/06
Inventor 黎淑娟
Owner 江苏泰斯鸿科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.