Blue photosensitive resin composition, color filter and liquid crystal display device having the same

A resin composition and blue light-sensitive technology, which is applied in the field of blue photosensitive resin composition and liquid crystal display devices, can solve the problems of low exposure and high sensitivity, lower quality of liquid crystal display devices, and failure to solve the problems of color filter adhesion

Inactive Publication Date: 2016-09-28
DONGWOO FINE CHEM CO LTD
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The above-mentioned prior art uses an oxime ester derivative compound as a photopolymerization initiator, but it only has low exposure and high sensitivity effects, and since there is no technical market for using it with a specific blue pigment, it has not yet solved the problem of high-temperature and high-humidity environments. The following is a problem that the quality of the liquid crystal display device decreases due to the phenomenon of liquid crystal bubbles due to the reduction of the adhesion force of the color filter.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blue photosensitive resin composition, color filter and liquid crystal display device having the same
  • Blue photosensitive resin composition, color filter and liquid crystal display device having the same
  • Blue photosensitive resin composition, color filter and liquid crystal display device having the same

Examples

Experimental program
Comparison scheme
Effect test

Synthetic example 1

[0342] Synthesis example 1. Synthesis of photopolymerization initiator (C-1): (13-(2-ethylhexyl)-5-(2,4,6-trimethylbenzyl Acyl)-13H-dibenzo[a,i]carbazol-8-yl]-[4-(2,2,3,3-tetrafluoropropoxy)-phenyl]-ketone oxime-O- Acetate synthesis

[0343] As intermediate 13-(2-ethylhexyl)-13H-dibenzo[a,i]carbazole, 1-naphthylhydrazine hydrochloride was used instead of phenylhydrazine, and according to the following steps 1 to 4 disclosed The sequence of synthesis of photopolymerization initiator C-1.

[0344] Step 1: 13-(2-Ethylhexyl)-13H-dibenzo[a,i]carbazole

[0345] 13H-Dibenzo[a,i]carbazole can be produced according to a specific sequence, such as the sequence disclosed in the literature [SYNLETT, 2006, 7, 1021].

[0346] To 13H-dibenzo[a,i]carbazole (0.70 g, 3.22 mol) in DMF (3 ml) was added sodium hydride (0.19 g, 4.67 mmol) at 0°C. After stirring at 0°C for 1 hour, 1-naphthylhydrazine hydrochloride (1.24 g, 6.44 mmol) was added at 0°C, and the mixture was stirred at room te...

Synthetic example 2

[0353] Synthesis example 2. Synthesis of photopolymerization initiator (C-2): 1-(9,9-H-7-nitrofluoren-2-yl)-acetoxime-O-acetate Synthesis

[0354] Step 1: Synthesis of 1-(9,9-H-7-nitrofluoren-2-yl)-ethanone

[0355]

[0356] Dissolve 5.0g (23.7mmol) of 2-nitrofluorene (1) in 100ml of anhydrous nitrobenzene, add 6.31g (47.4mmol) of anhydrous aluminum chloride, raise the temperature of the reactant to 45°C, and slowly A solution obtained by dissolving 2.79 g (35.5 mmol) of acetyl chloride in 30 ml of anhydrous nitrobenzene was added, and the reactant was heated up to 65° C. and stirred for 1 hour. Thereafter, the reactant was cooled to room temperature, 70 ml of distilled water was added and stirred for about 30 minutes, and then the product was filtered. The resulting solid product was dispersed in 50 ml of ether, stirred at room temperature for 30 minutes, filtered and dried to obtain pale yellow 1-(9,9-H-7-nitrofluoren-2-yl)-ethanone (2 ) 5.08 g (84.7%).

[0357] ...

Synthetic example 3

[0363] Synthesis example 3. Synthesis of photopolymerization initiator (C-3): 1-(9,9-diethyl-9H-fluoren-2-yl)-1,2-propanedione-2- Synthesis of Oxime-O-Acetate

[0364] Step 1: Synthesis of 9,9-diethyl-9H-fluorene (2)

[0365]

[0366] Dissolve 200.0 g (1.20 mol) of fluorene (1), 268.8 g (4.80 mol) of potassium hydroxide and 19.9 g (0.12 mol) of potassium iodide in 1 L of anhydrous dimethyl sulfoxide under a nitrogen atmosphere, and keep the reactant at 15°C , and then 283.3 g (2.60 mol) of bromoethane was slowly added over 2 hours, and the reactant was stirred at 15° C. for 1 hour. Afterwards, 2 L of distilled water was added to the reactant, and after stirring for 30 minutes, the product was extracted with 2 L of dichloromethane, and the extracted organic layer was washed twice with 2 L of distilled water, then the recovered organic layer was dried with anhydrous magnesium sulfate, and the solvent was reduced Pressure distillation and fractional distillation of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a blue photosensitive resin composition, a color filter and a liquid crystal display device having the same, the blue photosensitive resin composition adopts an oxime ester derivative compound as a photopolymerization initiator which is used in a blue pigment, so that the close adaptation is good in a hot and humid environment, the stripping does not occur, and the liquid crystal bubble phenomenon can be improved. In addition, the color filter and liquid crystal display device are made by using the blue photosensitive resin composition, the pattern does not fall off, so that the reliability can be improved.

Description

technical field [0001] The present invention relates to a blue photosensitive resin composition, a color filter, and a liquid crystal display device containing the same. Background technique [0002] Color filters are widely used in image pickup devices, liquid crystal display devices, and the like, and their range of applications is rapidly expanding. A color filter used in a color liquid crystal display device or an imaging element is generally produced by uniformly applying a coloring agent containing colorants corresponding to red, green, and blue on a substrate having a pattern of a black matrix by spin coating. The photosensitive resin composition is then heat-dried (hereinafter, sometimes referred to as pre-fired), the formed coating film is exposed, developed, and further heat-cured (hereinafter sometimes referred to as post-fired) as needed and repeated in color. into) operations to form pixels of various colors. [0003] As such a colored photosensitive resin com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G03F7/033G03F7/004G02B1/04G02B5/22G02F1/1335
CPCG02F1/133514G03F7/004G03F7/033G02B1/04G02B5/223
Inventor 裵辰哲权凤壹金佑泰
Owner DONGWOO FINE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com