Coating for non-shrinkage-cavity fusion cast brick heating insulated feeder head

A technology of thermal insulation riser and heating insulation layer, which is applied in the field of coatings, can solve the problems of low utilization rate of riser, achieve the effect of preventing the surface phenomenon of bonding bricks, good social and economic benefits, and saving recycling

Active Publication Date: 2016-08-24
郑州远东耐火材料有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above situation, in order to overcome the defects of the prior art, the object of the present invention is to provide a coating for heating and heat preservation risers of non-shrinkage electric fused bricks, which can effectively solve the problem of fusion bonding of risers and brick bodies, and utilization of risers. low rate problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating for non-shrinkage-cavity fusion cast brick heating insulated feeder head
  • Coating for non-shrinkage-cavity fusion cast brick heating insulated feeder head
  • Coating for non-shrinkage-cavity fusion cast brick heating insulated feeder head

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The specific implementation manners of the present invention will be described in further detail below in conjunction with the accompanying drawings.

[0030] Such as Figure 2-7 Shown, a kind of coating that is used for heating insulation riser of non-shrinkage electric fused brick of the present invention is to be coated on the priming coating on the internal surface of heating insulation riser and be coated on the surface coat coating on the priming coating surface;

[0031] Described primer comprises components by weight percentage: first mixed paint 50%, water 50%; Wherein, described first mixed paint comprises components by weight percentage: graphite powder 93%, cryolite 4% , bentonite 3%; the specific preparation method is: mixing graphite powder, graphite powder and bentonite together to obtain the first mixed coating, then adding the first mixed coating to water and mixing evenly to obtain final product;

[0032]The surface coating includes components by weig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a coating for a non-shrinkage-cavity fusion cast brick heating insulated feeder head. The problems of fusion and bonding of a feeder head and a brick body and low utilization rate of the feeder head can be effectively solved. According to the technical scheme, the coating comprises a ground coating with which the inner surface of the heating insulated feeder head is coated and a surface coating with which the surface of the ground coating is coated. The ground coating is prepared from, by weight, 49-51% of a first composition and 49-51% of water, wherein the first composition is prepared from, by weight, 92-94% of graphite powder, 3.9-4.1% of cryolite, and 2.9-3.1% of bentonite; the surface coating is prepared from, by weight, 65-67% of a second coating, 4.4-4.6% of cryolite, 1.4-1.6% of iron oxide powder, 0.9-1.1% of bentonite and 2.9-3.1% of xanthan gum. The coating is reasonable in formula, effectively solves the problem of the post-casting fusion and bonding phenomenon, greatly recycles feeder head materials, and has the good social and economic benefits.

Description

technical field [0001] The invention relates to a coating, in particular to a coating used for heating and heat preservation risers of non-shrinkage electric fused bricks. Background technique [0002] Zirconium corundum fused bricks have been developed in my country for decades. The raw materials for casting sand molds are mainly silica sand, and water glass or resin is added as binder for the production of sand molds. The high temperature resistance and heat resistance effect of silica sand It is more suitable for the production of fused brick sand molds, coupled with its advantages of abundant resources and low cost, it is still the first choice material for fused brick sand molds. [0003] The service life of the float glass furnace is currently about 8 years on average, and the average service life of the horseshoe flame daily-use glass furnace is about 5 years. The pool wall brick of the glass furnace is a key part of the service life of the glass furnace. From the indu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66C03B5/43
CPCC03B5/43C04B35/66
Inventor 龙沾卫
Owner 郑州远东耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products