Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Steel powder and molds using it

A powder and mold technology, applied in the field of steel powder, can solve the problems of low corrosion resistance, no involvement, difficulty in improving cooling efficiency, etc., achieve high performance and realize the effect of cooling efficiency

Active Publication Date: 2019-11-05
DAIDO STEEL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, cooling efficiency has reached its limit, and further improvement of cooling efficiency is difficult
Due to reasons that inhibit the improvement of cooling efficiency, there are the following problems: (1) low thermal conductivity, (2) crack promotion of water cooling holes and (3) low corrosion resistance
In addition, these patent documents do not relate to an embodiment in which steel is used in powder form as a material for the laminate forming method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel powder and molds using it
  • Steel powder and molds using it
  • Steel powder and molds using it

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0153] Dies and test pieces were produced by the lamination molding method by using 34 kinds of steel powders shown in Table 1, and various tests were performed. Specifically, tests for evaluating hardness, thermal conductivity, mold surface temperature, thermal cracking, and cracking of water cooling holes were performed.

[0154] Some of the steel powders shown in Table 1 contain elements not shown in the table within the range specified as the amount of impurities.

[0155] In Table 1, Comparative Steel 1 is JIS SKD61-type steel, Comparative Steel 2 is 18Ni maraging steel, Comparative Steel 3 is martensitic stainless steel SUS 420J2, and Comparative Steel 4 is steel SCM435 for machine structure. In each comparative steel, the amounts of at least two elements were outside the range specified by the present invention.

[0156] Table 1: Chemical composition (mass %) (balance: Fe)

[0157]

[0158] Table 1 (continued) chemical composition (mass%) (balance: Fe)

[0159] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elastic limitaaaaaaaaaa
Orientation degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to steel powder and a die using the same. The steel powder comprises has a composition containing, by mass percentage, 0.10<=C<0.25, 0.005<=Si<=0.600, 2.00<=Cr<=6.00, -0.0125x[Cr]+0.125<=Mn<= -0.100x [Cr]+1.800, wherein [Cr] represents the value of Cr content by mass percentage, 0.01<=Mo<=1.80, -0.00447 * [Mo]+0.010<=V<=-0.1117 * [Mo]+0.901 , wherein the [Mo] represents the value of Mo content by mass percentage, 0.0002<=N<=0.3000, and the balance being Fe and unavoidable impurities.

Description

technical field [0001] The present invention relates to a steel powder having excellent thermal conductivity and corrosion resistance, and a mold produced by using the steel powder. Background technique [0002] Generally, steel ingots are produced by melting steel, which are then forged and / or rolled to produce block or flat square material, which are cut by machining to form mold-shaped products, and then the mold-shaped products Applying heat treatment such as quenching or tempering to manufacture such as injection molding dies, die casting dies, hot press (also called hot stamp or die quench) dies for molding resins and rubber, etc. First class molds or dies. [0003] With these molds, cooling of the mold is generally performed by providing a cooling circuit (water cooling line) inside it and passing cooling water through the cooling circuit. [0004] In such molds, increasing the efficiency of cooling with cooling water leads to shortening of cycle time, that is, rapi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/18C22C38/12C22C38/04C22C38/02B22F1/00B22F3/10B22D17/22B29C45/26B21D37/01C21D1/673
CPCB21D37/01B22D17/22B22F1/00B22F3/10B29C45/26C21D1/673C22C38/001C22C38/02C22C38/04C22C38/12C22C38/18
Inventor 河野正道
Owner DAIDO STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More