Production method of smooth-surface domestic glass ceramic

A glass ceramics, production method technology, applied in glass production, glass pressing, glass forming and other directions, can solve problems such as product scrapping

Active Publication Date: 2016-08-03
广东健诚高科玻璃制品股份有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are certain risks in this technological innovation. When the technology is immature, all products will be scrapped.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of smooth-surface domestic glass ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] The daily-use glass-ceramic production method with smooth surface is characterized in that it comprises the following production steps:

[0024] (1) Production of semi-finished products

[0025] Using conventional production methods, the raw material of glass ceramics is smelted at 1400°C to form glass slurry, and the glass slurry is metered and put into a steel mold installed on a press, and pressurized to form a semi-finished product of daily-use glass ceramics;

[0026] (2) Flame polishing treatment of products

[0027] The semi-finished products are processed in the flame polishing room; the flame polishing room is equipped with a rotating disk, a graphite male mold and 2 combustion nozzles, and a supporting mold is set on the rotating disk, of which the flame nozzle of the No. The flame hole of the combustion nozzle is set in the middle, and the appearance of the graphite male mold is the same as the appearance of the inner cavity of the product;

[0028] Place t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of smooth-surface domestic glass ceramic. The production method is characterized by comprising the first step of semi-finished product production, the second step of product flame polishing treatment, the third step of product shaping and the fourth step of annealing treatment. According to the method, the produced domestic glass ceramic product has a smooth surface, tiny cracks in the surface of the product are basically eliminated, burrs and coarse surfaces at edges are eliminated, the edges are flat and smooth, the product is neat and free of deformation in appearance, and the quality of the product meets the GB / T30771 'domestic glass ceramic' standard requirement.

Description

technical field [0001] The invention relates to the field of glass ceramics, in particular to a method for producing daily-use glass ceramics with a smooth surface. Background technique [0002] In the GB / T30771 "Glass Ceramics for Daily Use" standard, glass ceramics are defined as "a type of ceramic composite material composed of a crystal phase and a glass phase. Generally, the glass is properly heated to produce a sufficient amount of crystal phase in the glass. Obtained." The definition of glass ceramics for daily use is "glass ceramic products for daily use". [0003] The appearance, shape and use of daily-use glass ceramics are similar to those of daily-use ceramics, but the materials are different from those of daily-use ceramics, and the production process is also different. The production process of daily-use glass ceramics is similar to that of daily-use glass, but there are differences. It is through high-temperature melting of composite materials, hot-press form...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B11/12C03B29/00C03B25/00
CPCY02P40/57C03B11/122C03B25/00C03B29/00
Inventor 詹建怀
Owner 广东健诚高科玻璃制品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com